CN104450086B - 一种精密仪器用防霉润滑脂及其制备方法 - Google Patents
一种精密仪器用防霉润滑脂及其制备方法 Download PDFInfo
- Publication number
- CN104450086B CN104450086B CN201410674248.6A CN201410674248A CN104450086B CN 104450086 B CN104450086 B CN 104450086B CN 201410674248 A CN201410674248 A CN 201410674248A CN 104450086 B CN104450086 B CN 104450086B
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating grease
- precision instrument
- mixture
- mould proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种精密仪器用防霉润滑脂及其制备方法，润滑脂包括聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚、脂肪醇聚氧乙烯醚、有机硅、环烷酸锌、高岭土、烯丙基磺酸钠、季铵盐、抗氧剂和95%乙醇。制备方法为先将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，得混合物Ⅰ；再将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95%乙醇中，得混合物Ⅱ；然后将混合物Ⅰ和混合物Ⅱ混合，再加入季铵盐和抗氧剂，即得。该防霉润滑脂能有效抑制精密仪器润滑、密封部位的微生物生长，确保精密仪器的使用性能。
Description
技术领域
本发明属于防霉润滑剂技术领域，具体涉及一种精密仪器用防霉润滑脂及其制备方法。
背景技术
润滑脂，俗称中油或黄油，是稠厚的油脂状半固体。用于机械的摩擦部分，起润滑和密封作用，也用于金属表面，起填充空隙和防锈作用。主要由矿物油和稠化剂调制而成。根据稠化剂可分为皂基脂和非皂基脂两类。皂基脂的稠化剂常用锂、钠、钙、铝、锌等金属皂，也用钾、钡、铅、锰等金属皂。非皂基脂的稠化剂用石墨、炭黑、石棉等。根据用途可分为通用润滑脂和专用润滑脂两种，前者用于一般机械零件，后者用于拖拉机、铁道机车、船舶机械、石油钻井机械、阀门等。
润滑脂是将稠化剂分散于液体润滑剂中所组成的一种稳定的固体或半固体产品，其中可以加入旨在改善润滑脂某种特性的添加剂及填料。润滑脂在常温下可附着于垂直表面不流失，并能在敞开或密封不良的摩擦部位工作，具有其他润滑剂所不可替代的特点。因此，在汽车和工程机械上的许多部位都是用润滑脂作为润滑材料。
精密仪器的装配过程中常使用润滑脂对产品的摩擦部位进行润滑及密封，但是制造润滑脂用的某些有机原料或其分解物能够为霉菌的生长提供养分，因此仪器使用润滑脂的部位容易生霉，有时霉菌分泌物的挥发还会使光学玻璃起雾，发生这种情况后，将会降低产品的使用性能甚至使产品无法使用。
发明内容
本发明的目的是克服现有技术的不足而提供一种精密仪器用防霉润滑脂及其制备方法，该防霉润滑脂能有效抑制精密仪器润滑、密封部位的微生物生长，确保精密仪器的使用性能。
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8003～10份，冰醋酸1～7份，脂肪醇醚硫酸铵2～8份，三氯羟基二苯醚1～8份，脂肪醇聚氧乙烯醚2～10份，有机硅3～9份，环烷酸锌1～7份，高岭土3～10份，烯丙基磺酸钠4～9份，季铵盐2～7份，抗氧剂1～8份，95％乙醇2～8份。
作为上述发明的进一步改进，所述精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8005～9份，冰醋酸3～6份，脂肪醇醚硫酸铵4～7份，三氯羟基二苯醚2～6份，脂肪醇聚氧乙烯醚5～9份，有机硅4～8份，环烷酸锌3～6份，高岭土4～9份，烯丙基磺酸钠5～8份，季铵盐3～6份，抗氧剂2～5份，95％乙醇4～7份。
作为上述发明的进一步改进，所述季铵盐为十二烷基三甲基氯化铵、十二烷基二甲基苄基氯化铵、十八烷基二甲基羟乙基硝酸铵或十八烷基二甲基羟乙基过氯酸铵中的一种。
作为上述发明的进一步改进，所述抗氧剂为二苯胺、二异辛基二苯胺、N-苯基-α-萘胺、2，6-二叔丁基对甲酚或2，6-二叔丁基-4-甲基苯酚中的一种。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热升温至110～130℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热升温至110～130℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空条件下加热至50～70℃，保温搅拌，冷却至室温，即得。
作为上述发明的进一步改进，步骤1和步骤2所述加热升温过程为程序升温，每半小时升温10℃。
作为上述发明的进一步改进，步骤3中所述真空条件的真空度为0.1～0.25MPa。
本发明的精密仪器用防霉润滑脂不仅具有优良的润滑、防锈和抗氧化性能，使用温度范围宽，还具有防霉功能，能够有效抑制霉菌的生长，保证润滑脂长期使用的过程中无霉菌产生，从而避免仪器由于霉菌的生长而污染仪器，影响仪器的使用。
具体实施方式
实施例1
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8003份，冰醋酸1份，脂肪醇醚硫酸铵2份，三氯羟基二苯醚1份，脂肪醇聚氧乙烯醚2份，有机硅3份，环烷酸锌1份，高岭土3份，烯丙基磺酸钠4份，季铵盐2份，抗氧剂1份，95％乙醇2份。
所述季铵盐为十二烷基三甲基氯化铵；抗氧剂为二苯胺。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热程序升温(每半小时升温10℃)至110℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热程序升温(每半小时升温10℃)至110℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空度为0.1MPa条件下加热至70℃，保温搅拌，冷却至室温，即得。
实施例2
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8005份，冰醋酸3份，脂肪醇醚硫酸铵4份，三氯羟基二苯醚2份，脂肪醇聚氧乙烯醚5份，有机硅4份，环烷酸锌3份，高岭土4份，烯丙基磺酸钠5份，季铵盐3份，抗氧剂25份，95％乙醇4份。
所述季铵盐为十二烷基二甲基苄基氯化铵；抗氧剂为二异辛基二苯胺。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热程序升温(每半小时升温10℃)至130℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热程序升温(每半小时升温10℃)至130℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空度为0.25MPa条件下加热至50℃，保温搅拌，冷却至室温，即得。
实施例3
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8007份，冰醋酸4份，脂肪醇醚硫酸铵5份，三氯羟基二苯醚3份，脂肪醇聚氧乙烯醚8份，有机硅6份，环烷酸锌4份，高岭土7份，烯丙基磺酸钠6份，季铵盐5份，抗氧剂4份，95％乙醇6份。
所述季铵盐为十八烷基二甲基羟乙基硝酸铵；抗氧剂为N-苯基-α-萘胺。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热程序升温(每半小时升温10℃)至110℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热程序升温(每半小时升温10℃)至130℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空度为0.1MPa条件下加热至50℃，保温搅拌，冷却至室温，即得。
实施例4
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇8009份，冰醋酸6份，脂肪醇醚硫酸铵7份，三氯羟基二苯醚6份，脂肪醇聚氧乙烯醚9份，有机硅8份，环烷酸锌6份，高岭土9份，烯丙基磺酸钠8份，季铵盐6份，抗氧剂5份，95％乙醇7份。
所述季铵盐为十八烷基二甲基羟乙基过氯酸铵；抗氧剂为2，6-二叔丁基-4-甲基苯酚。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热程序升温(每半小时升温10℃)至130℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热程序升温(每半小时升温10℃)至110℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空度为0.25MPa条件下加热至70℃，保温搅拌，冷却至室温，即得。
实施例5
一种精密仪器用防霉润滑脂，以重量份计包括：聚乙二醇80010份，冰醋酸7份，脂肪醇醚硫酸铵8份，三氯羟基二苯醚8份，脂肪醇聚氧乙烯醚10份，有机硅9份，环烷酸锌7份，高岭土10份，烯丙基磺酸钠9份，季铵盐7份，抗氧剂8份，95％乙醇8份。
所述季铵盐为十二烷基二甲基苄基氯化铵；抗氧剂为2，6-二叔丁基对甲酚。
上述精密仪器用防霉润滑脂的制备方法，包括以下步骤：
步骤1，将聚乙二醇800、冰醋酸、脂肪醇醚硫酸铵、三氯羟基二苯醚和脂肪醇聚氧乙烯醚混合，加热程序升温(每半小时升温10℃)至120℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，将有机硅、环烷酸锌、高岭土、烯丙基磺酸钠加至95％乙醇中，加热程序升温(每半小时升温10℃)至120℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入季铵盐和抗氧剂，在真空度为0.2MPa条件下加热至60℃，保温搅拌，冷却至室温，即得。
将实施例1至5所得防霉润滑剂进行性能测试，结果如下：
| 试验方法 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 锥入度25℃，15g，5s，0.1mm | GB/T629 | 65 | 63 | 61 | 67 | 66 |
| 滴点，℃ | GB/T3498 | 83 | 79 | 82 | 81 | 80 |
| 挥发度60℃，24h，％ | SH/T0048 | 0.02 | 0.05 | 0.03 | 0.04 | 0.06 |
| 腐蚀铜片，100℃，3h | SH/T0331 | 合格 | 合格 | 合格 | 合格 | 合格 |
| 防霉试验，30℃，湿度94％，30d | 自测 | 无霉菌 | 无霉菌 | 无霉菌 | 无霉菌 | 无霉菌 |
由上表可知，本发明的防霉润滑脂不仅具有优良的润滑、防锈和抗氧化性能，使用温度范围宽，还具有防霉功能，能够有效抑制霉菌的生长，保证润滑脂长期使用的过程中无霉菌产生，从而避免仪器由于霉菌的生长而污染仪器，影响仪器的使用。
Claims (1)
1.一种精密仪器用防霉润滑脂，其特征在于：由以下步骤制备得到：
步骤1，以重量份计，将聚乙二醇800 9份、冰醋酸6份、脂肪醇醚硫酸铵7份、三氯羟基二苯醚6份和脂肪醇聚氧乙烯醚9份混合，按每半小时升温10℃加热升温至130℃，保温搅拌，冷却至室温，得混合物Ⅰ；
步骤2，以重量份计，将有机硅8份、环烷酸锌6份、高岭土9份和烯丙基磺酸钠8份加至95%乙醇7份中，按每半小时升温10℃加热升温至110℃，保温搅拌，冷却至室温，得混合物Ⅱ；
步骤3，以重量份计，将步骤1所得混合物Ⅰ和步骤2所得混合物Ⅱ混合，再加入十八烷基二甲基羟乙基过氯酸铵6份和2，6-二叔丁基-4-甲基苯酚5份，在真空度为0.25MPa条件下加热至70℃，保温搅拌，冷却至室温，即得。