CN104440637A - 曲轴磨砂轮的制造方法 - Google Patents
曲轴磨砂轮的制造方法 Download PDFInfo
- Publication number
- CN104440637A CN104440637A CN201410806518.4A CN201410806518A CN104440637A CN 104440637 A CN104440637 A CN 104440637A CN 201410806518 A CN201410806518 A CN 201410806518A CN 104440637 A CN104440637 A CN 104440637A
- Authority
- CN
- China
- Prior art keywords
- grinding wheel
- mass parts
- manufacturing
- parts
- emery wheel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种曲轴磨砂轮的制造方法,包括如下步骤:1)取2.6质量份硼玻璃、3.4质量份闭孔珍珠岩、1.8质量份活性硅微粉、4.7质量份氧化硼、1.3质量份氧化钡投入混料桶混合均匀,过筛得到制备复合结合剂;2)将复合结合剂与磨料混合,加入球磨机中进行球磨,出料后过筛得到成型料;3)成型料压制砂轮毛坯,放入烘房烘干;4)烘干后的砂轮毛坯烧成砂轮成品。本发明曲轴磨砂轮的制造方法,其能提高砂轮制造时的成品合格率,还能提高砂轮的强度。
Description
技术领域
本发明涉及曲轴磨砂轮的制造方法。
背景技术
现有曲轴磨砂轮的制造方法,其砂轮制造时的成品合格率有待提高,制得的砂轮的强度也有待提高。
发明内容
本发明的目的在于提供一种曲轴磨砂轮的制造方法,其能提高砂轮制造时的成品合格率,还能提高砂轮的强度。
为实现上述目的,本发明的技术方案是设计一种曲轴磨砂轮的制造方法,包括如下步骤:
1)取2.6质量份硼玻璃、3.4质量份闭孔珍珠岩、1.8质量份活性硅微粉、4.7质量份氧化硼、1.3质量份氧化钡投入混料桶混合均匀,过筛得到制备复合结合剂;
2)将复合结合剂与磨料混合,加入球磨机中进行球磨,出料后过筛得到成型料;
3)成型料压制砂轮毛坯,放入烘房烘干;
4)烘干后的砂轮毛坯烧成砂轮成品。
本发明的优点和有益效果在于:提供一种曲轴磨砂轮的制造方法,其能提高砂轮制造时的成品合格率,还能提高砂轮的强度。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种曲轴磨砂轮的制造方法,包括如下步骤:
1)取2.6质量份硼玻璃、3.4质量份闭孔珍珠岩、1.8质量份活性硅微粉、4.7质量份氧化硼、1.3质量份氧化钡投入混料桶混合均匀,过筛得到制备复合结合剂;
2)将复合结合剂与磨料混合,加入球磨机中进行球磨,出料后过筛得到成型料;
3)成型料压制砂轮毛坯,放入烘房烘干;
4)烘干后的砂轮毛坯烧成砂轮成品。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.曲轴磨砂轮的制造方法,其特征在于,包括如下步骤:
1)取2.6质量份硼玻璃、3.4质量份闭孔珍珠岩、1.8质量份活性硅微粉、4.7质量份氧化硼、1.3质量份氧化钡投入混料桶混合均匀,过筛得到制备复合结合剂;
2)将复合结合剂与磨料混合,加入球磨机中进行球磨,出料后过筛得到成型料;
3)成型料压制砂轮毛坯,放入烘房烘干;
4)烘干后的砂轮毛坯烧成砂轮成品。