CN104423061A - 一种新型眼镜片结构 - Google Patents

一种新型眼镜片结构 Download PDF

Info

Publication number
CN104423061A
CN104423061A CN201310382649.XA CN201310382649A CN104423061A CN 104423061 A CN104423061 A CN 104423061A CN 201310382649 A CN201310382649 A CN 201310382649A CN 104423061 A CN104423061 A CN 104423061A
Authority
CN
China
Prior art keywords
rete
coating
chip architecture
resisting
novel glasses
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310382649.XA
Other languages
English (en)
Inventor
丁鹏飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU YUANDA OPTICAL TECHNOLOGY Co Ltd
Original Assignee
JIANGSU YUANDA OPTICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU YUANDA OPTICAL TECHNOLOGY Co Ltd filed Critical JIANGSU YUANDA OPTICAL TECHNOLOGY Co Ltd
Priority to CN201310382649.XA priority Critical patent/CN104423061A/zh
Publication of CN104423061A publication Critical patent/CN104423061A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种新型眼镜片结构，所述新型眼镜片结构具有丙烯酸系材料基片（1），其特征在于，在所述丙烯酸系材料基片（1）的前表面和后表面上均具有膜系，其中前表面上的膜系自内向外依次包括加硬层（2）、防划耐磨膜层（3）、防蓝光反射膜层（4）、防尘膜层（5）和易洁膜层（6）；后表面上的膜系自前向后依次包括加硬层（7）、防划耐磨膜层（8）、绿色增透膜层（9）、防尘膜层（10）和易洁膜层（11）。所述镜片能够高效地减少蓝光对人的眼睛的伤害，并且镜片更加耐磨、耐用，有极强的防污性能。

Description

一种新型眼镜片结构
技术领域
本发明属于光学领域，具体来说涉及一种新型眼镜片结构。
背景技术
现有眼镜片往往在透光率和减少蓝光伤害方面难以同时达到要求。
发明内容
本发明提供一种新型眼镜片结构，采用该新型结构，生产出同时满足透光率要求和减少蓝光伤害的眼镜片。本发明采用的技术方案如下：
一种新型眼镜片结构，所述新型眼镜片结构具有丙烯酸系材料基片1，其特征在于，在所述丙烯酸系材料基片1的前表面和后表面上均具有膜系，其中前表面上的膜系自内向外依次包括加硬层2、防划耐磨膜层3、防蓝光反射膜层4、防尘膜层5和易洁膜层6；后表面上的膜系自前向后依次包括加硬层7、防划耐磨膜层8、绿色增透膜层9、防尘膜层10和易洁膜层11。采用该新型结构，前后表面的膜系参数不同，前表面膜层功能为高效防止蓝光对人眼的伤害，后表面膜层功能为增加镜片的透过率，达到增透的效果。
优选地，所述易洁膜层6、11是通过浸泡法镀上去的。
所述浸泡法包括在将眼镜片从镀膜机器中取出后用配制的药水浸泡20秒，再在烘箱中在60℃下热处理2小时，其中所述药水按重量份计是由乙基全氟异丁基醚15-25份、乙基全氟丁基醚75-85份和氟素表面处理剂1-2份组成。
优选地，所述药水按重量份计是由乙基全氟异丁基醚20份、乙基全氟丁基醚80份和氟素表面处理剂2份组成。由此获得的易洁膜层使得镜片更加耐磨、耐用，有极强的防污性能。
有益效果：
由此获得的镜片一方面能够高效地减少蓝光对人的眼睛的伤害，并且另一方面使得镜片更加耐磨、耐用，有极强的防水防污性能。
附图说明
图1是本发明的具有新型眼镜片结构的结构示意图。
在图中：1丙烯酸系材料基片；2加硬层；3防划耐磨膜层；4防蓝光反射膜层；5防尘膜层；6易洁膜层；7加硬层；8防划耐磨膜层；9绿色增透膜层；10防尘膜层；11易洁膜层。
具体实施方式
下面结合附图详细说明本发明。
参见图1，本发明的新型眼镜片结构包括丙烯酸系材料基片1，在所述丙烯酸系材料基片1的前表面和后表面上均具有膜系，其中前表面上的膜系自内向外依次包括加硬层2、防划耐磨膜层3、防蓝光反射膜层4、防尘膜层5和易洁膜层6；后表面上的膜系自前向后依次包括加硬层7、防划耐磨膜层8、绿色增透膜层9、防尘膜层10和易洁膜层11。采用这种前后表面膜系参数不同的结构，前表面膜层功能为高效防止蓝光对人眼的伤害，后表面膜层功能为增加镜片的透过率，达到增透的效果。
实施例1：浸泡法药水的配制
使用精度分别为0.001g、0.01g的电子天平各一台，将①乙基全氟异丁基醚、②乙基全氟丁基醚、③氟素表面处理剂（OPTOOL DSX，大金工业株式会社）分别按80：20：2的配方比例，按照①②③顺序进行称量添加，添加各成分后进行搅拌1小时，配制好后，使用0.45 μm折叠滤芯进行过滤，制成氟化液混合物。
实施例2. 镜片的处理
将镀膜镜片在上述氟化液混合物中浸泡20秒，取出后在烘箱中60℃热处理2小时。
上面结合附图和实施例对本发明的实施方式作了详细的说明，但是本发明不限于上述实施方式，在所属技术领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下做出各种变化。

Claims (4)

1. 一种新型眼镜片结构，所述新型眼镜片结构具有丙烯酸系材料基片（1），其特征在于，在所述丙烯酸系材料基片（1）的前表面和后表面上均具有膜系，其中前表面上的膜系自内向外依次包括加硬层（2）、防划耐磨膜层（3）、防蓝光反射膜层（4）、防尘膜层（5）和易洁膜层（6）；后表面上的膜系自前向后依次包括加硬层（7）、防划耐磨膜层（8）、绿色增透膜层（9）、防尘膜层（10）和易洁膜层（11）。
2. 如权利要求1所述的新型眼镜片结构，其特征在于，所述易洁膜层（6、11）是通过浸泡法镀上去的。
3. 如权利要求2所述的新型眼镜片结构，其特征在于，所述浸泡法包括在将眼镜片从镀膜机器中取出后用配制的药水浸泡20秒，再在烘箱中在60℃下热处理2小时，其中所述药水按重量份计是由乙基全氟异丁基醚15-25份、乙基全氟丁基醚75-85份和氟素表面处理剂1-2份组成。
4. 如权利要求3所述的新型眼镜片结构，其特征在于，所述药水按重量份计是由乙基全氟异丁基醚20份、乙基全氟丁基醚80份和氟素表面处理剂2份组成。
CN201310382649.XA 2013-08-29 2013-08-29 一种新型眼镜片结构 Pending CN104423061A (zh)