CN104388160A - 一种金属润滑油及其制备方法 - Google Patents

一种金属润滑油及其制备方法 Download PDF

Info

Publication number
CN104388160A
CN104388160A CN201410601075.5A CN201410601075A CN104388160A CN 104388160 A CN104388160 A CN 104388160A CN 201410601075 A CN201410601075 A CN 201410601075A CN 104388160 A CN104388160 A CN 104388160A
Authority
CN
China
Prior art keywords
oil
parts
sodium
lubricating oil
benzotriazole
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410601075.5A
Other languages
English (en)
Inventor
杨龙兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Yanggong Machinery Manufacturing Co Ltd
Original Assignee
Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Yanggong Machinery Manufacturing Co Ltd filed Critical Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority to CN201410601075.5A priority Critical patent/CN104388160A/zh
Publication of CN104388160A publication Critical patent/CN104388160A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种金属润滑油，所述金属润滑油由以下质量份数的各组分组成：土耳其油10-15份、蓖麻油4-6份、硬脂酸锌1-2份、石油磺酸钠0.5-0.8份、苯并三氮唑0.1-0.3份、钼酸钠0.5-0.8份、硝酸钠0.4-0.6份、十二烷基硫酸钠1.2-1.6份、甘氨酸0.2-0.4份、聚氧乙烯醚0.1-0.3份。本发明还提供其制备方法。本发明的金属润滑油具有良好的润滑和冷却性能，能够极大程度上保护加工刀具，防止卷刃等现象。

Description

一种金属润滑油及其制备方法
技术领域
本发明涉及一种金属润滑油及其制备方法。
背景技术
润滑油是以矿物基础油或合成基础油为主，加入极压抗磨剂和油性剂调制而成的一种重要的润滑油，用于各种齿轮传动装置，以防止齿面磨损、擦伤、烧结等，延长其使用寿命，提高传递功率效率，减少功率损失。现代机械加工向高速、强力、精密方向发展，超硬、超强度金属加工的发展也使切削加工的难度日益增加。上述原因导致切削加工过程中的摩擦力、摩擦热大幅度提高，这就要求金属加工液具有更好的润滑、冷却、清洗、防锈性能，以便获得理想的加工表面。
发明内容
为了解决现有技术中存在的问题，本发明提供了一种金属润滑油，具有良好的润滑和冷却性能；为此，本发明还提供其制备方法。
本发明提供一种金属润滑油，所述金属润滑油由以下质量份数的各组分组成：土耳其油10-15份、蓖麻油4-6份、硬脂酸锌1-2份、石油磺酸钠0.5-0.8份、苯并三氮唑0.1-0.3份、钼酸钠0.5-0.8份、硝酸钠0.4-0.6份、十二烷基硫酸钠1.2-1.6份、甘氨酸0.2-0.4份、聚氧乙烯醚0.1-0.3份。
优选地，所述金属润滑油由以下质量份数的各组分组成：土耳其油12份、蓖麻油5份、硬脂酸锌1.5份、石油磺酸钠0.6份、苯并三氮唑0.2份、钼酸钠0.6份、硝酸钠0.5份、十二烷基硫酸钠1.4份、甘氨酸0.3份、聚氧乙烯醚0.2份。
本发明还提供上述金属润滑油的制备方法，步骤如下：
（1）将配方量的土耳其油、蓖麻油、硬脂酸锌、石油磺酸钠、苯并三氮唑、钼酸钠、硝酸钠和聚氧乙烯醚混合，升温至50-55℃，搅拌15-20min；
（2）加入配方量的其余组分，搅拌5-10min，冷却至室温，即得。
本发明的金属润滑油具有良好的润滑和冷却性能，能够极大程度上保护加工刀具，防止卷刃等现象。
具体实施方式
以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的金属润滑油的配方如下：
土耳其油12kg、蓖麻油5kg、硬脂酸锌1.5kg、石油磺酸钠0.6kg、苯并三氮唑0.2kg、钼酸钠0.6kg、硝酸钠0.5kg、十二烷基硫酸钠1.4kg、甘氨酸0.3kg、聚氧乙烯醚0.2kg。
本发明的金属润滑油的制备方法如下：
（1）将土耳其油12kg、蓖麻油5kg、硬脂酸锌1.5kg、石油磺酸钠0.6kg、苯并三氮唑0.2kg、钼酸钠0.6kg、硝酸钠0.5kg和聚氧乙烯醚0.2kg混合，升温至52℃，搅拌18min；
（2）加入十二烷基硫酸钠1.4kg和甘氨酸0.3kg，搅拌8min，冷却至室温，即得。
实施例2
本发明的金属润滑油的配方如下：
土耳其油10kg、蓖麻油4kg、硬脂酸锌1kg、石油磺酸钠0.5kg、苯并三氮唑0.3kg、钼酸钠0.5kg、硝酸钠0.4kg、十二烷基硫酸钠1.2kg、甘氨酸0.4kg、聚氧乙烯醚0.3kg。
本发明的金属润滑油的制备方法如下：
（1）将土耳其油10kg、蓖麻油4kg、硬脂酸锌1kg、石油磺酸钠0.5kg、苯并三氮唑0.3kg、钼酸钠0.5kg、硝酸钠0.4kg和聚氧乙烯醚0.3kg混合，升温至50℃，搅拌20min；
（2）加入十二烷基硫酸钠1.2kg和甘氨酸0.4kg，搅拌10min，冷却至室温，即得。
实施例3
本发明的金属润滑油的配方如下：
土耳其油15kg、蓖麻油6kg、硬脂酸锌2kg、石油磺酸钠0.8kg、苯并三氮唑0.1kg、钼酸钠0.8kg、硝酸钠0.6kg、十二烷基硫酸钠1.6kg、甘氨酸0.2kg、聚氧乙烯醚0.1kg。
本发明的金属润滑油的制备方法如下：
（1）将土耳其油15kg、蓖麻油6kg、硬脂酸锌2kg、石油磺酸钠0.8kg、苯并三氮唑0.1kg、钼酸钠0.8kg、硝酸钠0.6kg和聚氧乙烯醚0.1kg混合，升温至55℃，搅拌15min；
（2）加入十二烷基硫酸钠1.6kg和甘氨酸0.2kg，搅拌5min，冷却至室温，即得。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种金属润滑油，其特征在于：所述金属润滑油由以下质量份数的各组分组成：土耳其油10-15份、蓖麻油4-6份、硬脂酸锌1-2份、石油磺酸钠0.5-0.8份、苯并三氮唑0.1-0.3份、钼酸钠0.5-0.8份、硝酸钠0.4-0.6份、十二烷基硫酸钠1.2-1.6份、甘氨酸0.2-0.4份、聚氧乙烯醚0.1-0.3份。
2.根据权利要求1所述的金属润滑油，其特征在于：所述金属润滑油由以下质量份数的各组分组成：土耳其油12份、蓖麻油5份、硬脂酸锌1.5份、石油磺酸钠0.6份、苯并三氮唑0.2份、钼酸钠0.6份、硝酸钠0.5份、十二烷基硫酸钠1.4份、甘氨酸0.3份、聚氧乙烯醚0.2份。
3.权利要求1或2所述的金属润滑油的制备方法，其特征在于：步骤如下：
（1）将配方量的土耳其油、蓖麻油、硬脂酸锌、石油磺酸钠、苯并三氮唑、钼酸钠、硝酸钠和聚氧乙烯醚混合，升温至50-55℃，搅拌15-20min；
（2）加入配方量的其余组分，搅拌5-10min，冷却至室温，即得。
CN201410601075.5A 2014-10-31 2014-10-31 一种金属润滑油及其制备方法 Pending CN104388160A (zh)