CN104385637A - 橡胶锤用锤体手柄硫化工艺 - Google Patents

橡胶锤用锤体手柄硫化工艺 Download PDF

Info

Publication number
CN104385637A
CN104385637A CN201410503663.5A CN201410503663A CN104385637A CN 104385637 A CN104385637 A CN 104385637A CN 201410503663 A CN201410503663 A CN 201410503663A CN 104385637 A CN104385637 A CN 104385637A
Authority
CN
China
Prior art keywords
hammer
rubber hammer
rubber
steam pressure
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410503663.5A
Other languages
English (en)
Inventor
马聚龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Original Assignee
Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Dongbeitang Yongfeng Rubber Plastic Factory filed Critical Wuxi Dongbeitang Yongfeng Rubber Plastic Factory
Priority to CN201410503663.5A priority Critical patent/CN104385637A/zh
Publication of CN104385637A publication Critical patent/CN104385637A/zh
Pending legal-status Critical Current

Abstract

本发明公开了橡胶锤用锤体手柄硫化工艺，包括如下步骤：1）将橡胶锤依次油洗和水洗，去除表面的污物后放入蒸汽压力炉；2）以50℃/小时的速率将蒸汽压力炉的温度迅速升温到120-150℃，并持续保温30-35分钟；3）以30℃/小时的速率将蒸汽压力炉的温度降至60℃，并保温1-2小时；4）在一小时内完全释放蒸汽压力，打开冷风冷却；5）对橡胶锤受损部位喷涂修复剂，以在橡胶锤外表面形成表面修复剂层；6）采用预置送粉的方式，对修复剂层进行逐层激光熔覆，从修复剂层表面的最低点开始激光熔覆；7）使用自来水进行漂洗，然后使用引风设备进行吹干。本发明操作简单，经本发明处理的橡胶具有较强的耐磨和抗腐蚀性能，使用寿命长。

Description

橡胶锤用锤体手柄硫化工艺
技术领域
本发明涉及橡胶领域，具体地说，特别涉及到一种橡胶锤用锤体手柄硫化工艺。
 
背景技术
在装修行业安装地板时，为了使地板砖下的水泥分布均匀不出现空洞，往往使用橡胶锤敲击地板砖。现有的橡胶锤，包括锤体和手柄，锤体内设有内芯，锤体和手柄为一体结构。现有的橡胶锤是采用的橡胶在长期使用后会出现橡胶疲劳、受损、被腐蚀等问题，影响橡胶锤的使用寿命。
发明内容
本发明的目的在于针对现有技术中的不足，提供一种橡胶锤用锤体手柄硫化工艺，以解决上述问题。
本发明所解决的技术问题可以采用以下技术方案来实现：
橡胶锤用锤体手柄硫化工艺，包括如下步骤：
1）将橡胶锤依次油洗和水洗，去除表面的污物后放入蒸汽压力炉；
2）以50℃/小时的速率将蒸汽压力炉的温度迅速升温到120-150℃，并持续保温30-35分钟；
3）以30℃/小时的速率将蒸汽压力炉的温度降至60℃，并保温1-2小时；
4）保温结束后，在一小时内完全释放蒸汽压力，打开冷风冷却；
5）对橡胶锤受损部位喷涂修复剂，以在橡胶锤外表面形成表面修复剂层；
6）采用预置送粉的方式，对修复剂层进行逐层激光熔覆，从修复剂层表面的最低点开始激光熔覆；
7）使用自来水进行漂洗，然后使用引风设备进行吹干。
优选的，所述步骤2）的最佳保温温度为140℃，最佳保温时间为30分钟。
优选的，所述步骤3）的最佳保温时间为1小时。
与现有技术相比，本发明的有益效果如下：
操作简单，工艺巧妙，经本发明处理的橡胶具有较强的耐磨和抗腐蚀性能，使用寿命长。
 
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例1
1）将橡胶锤依次油洗和水洗，去除表面的污物后放入蒸汽压力炉；
2）以50℃/小时的速率将蒸汽压力炉的温度迅速升温到120℃，并持续保温30分钟；
3）以30℃/小时的速率将蒸汽压力炉的温度降至60℃，并保温1小时；
4）保温结束后，在一小时内完全释放蒸汽压力，打开冷风冷却；
5）对橡胶锤受损部位喷涂修复剂，以在橡胶锤外表面形成表面修复剂层；
6）采用预置送粉的方式，对修复剂层进行逐层激光熔覆，从修复剂层表面的最低点开始激光熔覆；
7）使用自来水进行漂洗，然后使用引风设备进行吹干。
实施例2
1）将橡胶锤依次油洗和水洗，去除表面的污物后放入蒸汽压力炉；
2）以50℃/小时的速率将蒸汽压力炉的温度迅速升温到120℃，并持续保温30分钟；
3）以30℃/小时的速率将蒸汽压力炉的温度降至60℃，并保温1小时；
4）保温结束后，在一小时内完全释放蒸汽压力，打开冷风冷却；
5）对橡胶锤受损部位喷涂修复剂，以在橡胶锤外表面形成表面修复剂层；
6）采用预置送粉的方式，对修复剂层进行逐层激光熔覆，从修复剂层表面的最低点开始激光熔覆；
7）使用自来水进行漂洗，然后使用引风设备进行吹干。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.橡胶锤用锤体手柄硫化工艺，其特征在于，包括如下步骤：
1）将橡胶锤依次油洗和水洗，去除表面的污物后放入蒸汽压力炉；
2）以50℃/小时的速率将蒸汽压力炉的温度迅速升温到120-150℃，并持续保温30-35分钟；
3）以30℃/小时的速率将蒸汽压力炉的温度降至60℃，并保温1-2小时；
4）保温结束后，在一小时内完全释放蒸汽压力，打开冷风冷却；
5）对橡胶锤受损部位喷涂修复剂，以在橡胶锤外表面形成表面修复剂层；
6）采用预置送粉的方式，对修复剂层进行逐层激光熔覆，从修复剂层表面的最低点开始激光熔覆；
7）使用自来水进行漂洗，然后使用引风设备进行吹干。
2.根据权利要求1所述的橡胶锤用锤体手柄硫化工艺，其特征在于，所述步骤2）的最佳保温温度为140℃，最佳保温时间为30分钟。
3.根据权利要求1所述的橡胶锤用锤体手柄硫化工艺，其特征在于，所述步骤3）的最佳保温时间为1小时。
CN201410503663.5A 2014-09-28 2014-09-28 橡胶锤用锤体手柄硫化工艺 Pending CN104385637A (zh)