CN104372112A - 一种针对皮质文物微乳液加脂剂的制备方法 - Google Patents
一种针对皮质文物微乳液加脂剂的制备方法 Download PDFInfo
- Publication number
- CN104372112A CN104372112A CN201410579941.5A CN201410579941A CN104372112A CN 104372112 A CN104372112 A CN 104372112A CN 201410579941 A CN201410579941 A CN 201410579941A CN 104372112 A CN104372112 A CN 104372112A
- Authority
- CN
- China
- Prior art keywords
- parts
- microemulsion
- mass
- solution
- massfraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种针对皮质文物微乳液加脂剂的制备方法,采取以下步骤:A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;B)将步骤A)得到溶液放入超声波细胞破碎仪,在60-150W的功率下进行处理10-45分钟;C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;E)按质量分数取1-3份戊二醛,3-5份脱氢酸纳,1-3份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,混合均匀,得到针对皮质文物的微乳液加脂剂。通过上述步骤最终得到针对皮质文物的微乳液加脂剂,具有良好的加脂抗菌防腐的作用。
Description
技术领域
本发明属于皮质文物保护领域,尤其涉及一种针对皮质文物的微乳液加脂剂的制备方法。
背景技术
皮革加脂剂是皮革工业中的一种重要的材料,鞣制、染色后的皮革经过干燥失水后,容易引起真皮层结构的密封和收缩。通过对皮革的加脂,可以润湿皮纤维,使成革丰满、柔软、富有弹性,同时还可以防水抗皱,改善皮革的物理、机械性能。加脂剂在制革生产中是用量最大的皮化材料,对成革性能有极其重要的影响。加脂剂渗透到皮革的胶原纤维之间,起到润滑和增塑作用,分子链及链段易于运动,使成革柔软、防水、防晒、滋润且富有弹性。
皮质文物由于各种不良因素的综合作用,发生脱水、脱脂、霉变等变化, 变得非常坚硬,其主要成分胶原蛋白纤维和弹性蛋白纤维也发生了严重的变性,使皮革变得异常的坚硬,不利于文物长期保存。针对这种局面,急需对其进行研究保护工作。目前大多数皮革加脂剂多采用酸类改性的方法,不仅污染环境,同时残留的酸液也可能对皮革文物产生二次破坏。同时由于皮革文物内部大量物质流失,内部的胶原纤维出现既缠结又断裂现象,所以传统的皮革加脂剂并不适用于皮革文物。为了保护文物,研究一种新型适用于皮革文物的加脂剂十分重要。
发明内容
为了解决上述现有技术的缺点,本发明提供一种针对皮质文物的微乳液加脂剂的制备方法。
本发明所采用的技术方案是:一种针对皮质文物微乳液加脂剂的制备方法,其特征在于采取以下步骤:
A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪,在60-150W的功率下进行处理10-45分钟;
C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;
D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;
E)按质量分数取1-3份戊二醛,3-5份脱氢酸纳,1-3份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;
F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,使其混合均匀,得到针对皮质文物的微乳液加脂剂。
通过上述步骤最终得到针对皮质文物的微乳液加脂剂,具有良好的加脂抗菌防腐的作用。本发明与现有技术相比,具有优点是:1)使用超声波技术乳化加工,可以避免传统加脂剂所残留的强酸对皮革文物造成二次破坏;2)使用超声波技术乳化加工的加脂剂,乳液粒径更细微,能更好的渗透进皮革文物内部,起到良好的加脂作用;3)使用超声波技术乳化加工,可以避免传统的硫酸化、磷酸化、磺化改性所带来的污染;4)微乳液加脂剂中添加了抗菌成分,可以使皮革更好的抑制霉菌,细菌。
具体实施方式
下面结合实施本发明作进一步说明:
实施例1:采取以下步骤:
A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪,在60W的功率下进行处理45分钟;
C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;
D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;
E)按质量分数取1份戊二醛,3份脱氢酸纳,1份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;
F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,使其混合均匀,得到针对皮质文物的微乳液加脂剂。
实施例2:采取以下步骤:
A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪,在100W的功率下进行处理30分钟;
C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;
D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;
E)按质量分数取2份戊二醛,4份脱氢酸纳,2份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;
F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,使其混合均匀,得到针对皮质文物的微乳液加脂剂。
实施例3:采取以下步骤:
A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪,在150W的功率下进行处理10分钟;
C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;
D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;
E)按质量分数取3份戊二醛, 5份脱氢酸纳, 3份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;
F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,使其混合均匀,得到针对皮质文物的微乳液加脂剂。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。
Claims (1)
1.一种针对皮质文物微乳液加脂剂的制备方法,其特征在于采取以下步骤:
A)按质量分数取蓖麻油20份,将其溶于20份去离子水中,在常温下充分搅拌,使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪,在60-150W的功率下进行处理10-45分钟;
C)按质量分数取20份司班-80和20份吐温-80加入到步骤B)所得溶液中混合均匀;
D)按质量分数计取20份聚乙二醇-400加入到步骤C)所得的溶液中;
E)按质量分数取1-3份戊二醛,3-5份脱氢酸纳,1-3份3-丙二醇,加入到步骤D)所得的溶液中混合均匀;
F)将步骤E)得到的溶液在60℃水浴中进行搅拌乳化,使其混合均匀,得到针对皮质文物的微乳液加脂剂。