CN106166778A - 竹片的软化处理方法 - Google Patents

竹片的软化处理方法 Download PDF

Info

Publication number
CN106166778A
CN106166778A CN201610580740.6A CN201610580740A CN106166778A CN 106166778 A CN106166778 A CN 106166778A CN 201610580740 A CN201610580740 A CN 201610580740A CN 106166778 A CN106166778 A CN 106166778A
Authority
CN
China
Prior art keywords
bamboo chip
parts
hours
take out
treatment method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610580740.6A
Other languages
English (en)
Inventor
荣佳黎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sanjiang Shanchaxuan Arts And Crafts Co Ltd
Original Assignee
Sanjiang Shanchaxuan Arts And Crafts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanjiang Shanchaxuan Arts And Crafts Co Ltd filed Critical Sanjiang Shanchaxuan Arts And Crafts Co Ltd
Priority to CN201610580740.6A priority Critical patent/CN106166778A/zh
Publication of CN106166778A publication Critical patent/CN106166778A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种竹片的软化处理方法，属于竹制品制造技术领域。本发明包括先将竹片放入冷库中，在‑5℃～0℃下冷冻5小时～8小时；然后取出，并趁冷放入50℃～60℃、按重量份计由50份无水乙醇、2份腰果酚、1份硬脂酸锌以及100份电导率小于5μS/cm的去离子水混合制得的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡1小时～2小时；然后取出，并用‑5℃～0℃的0.9wt%盐水漂洗。经过本发明处理后的竹片具有很好的柔软性，非常适于编制各种工艺品。

Description

竹片的软化处理方法
技术领域
本发明属于竹制品制造技术领域，尤其涉及一种竹片的软化处理方法。
背景技术
竹片是竹筒经开片后形成的窄长片材，其主要用来编制各种工艺品。而在编制工艺品时，通常会由于竹片太硬、没有柔韧性而容易发生折断或是伤手的，不仅造成了竹片废品的产生还对编制人员的人身安全造成了隐患。为此，人们在使用竹片编制之前通常会先对竹片进行相应的处理，从而使其符合编制要求。
发明内容
本发明所要解决的技术问题是提供一种可以使竹片软化、具有一定柔韧性的竹片的软化处理方法。
为了解决上述技术问题，本发明所采用的技术方案是：
先将竹片放入冷库中，在-5℃～0℃下冷冻5小时～8小时；然后取出，并趁冷放入50℃～60℃的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡1小时～2小时；然后取出，并用-5℃～0℃的0.9wt%盐水漂洗；
其中，所述浸泡液按重量份计，由50份无水乙醇、2份腰果酚、1份硬脂酸锌以及100份电导率小于5μS/cm的去离子水混合制得。
由于采用上述技术方案，本发明具有如下有益效果：
经过本发明处理后的竹片具有很好的柔软性，非常适于编制各种工艺品。
具体实施方式
以下结合具体实例对本发明作进一步详述：
其中，实施例1～实施例3中所使用的浸泡液均是按重量份计，由50份无水乙醇、2份腰果酚、1份硬脂酸锌以及100份电导率小于5μS/cm的去离子水混合制得。
实施例1
竹片的软化处理方法如下：
先将竹片放入冷库中，在-5℃下冷冻5小时；然后取出，并趁冷放入50℃的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡2小时；然后取出，并用-5℃的0.9wt%盐水漂洗。
经测试，经过本实施例处理后的竹片的硬度为18HB。
实施例2
竹片的软化处理方法如下：
先将竹片放入冷库中，在0℃下冷冻8小时；然后取出，并趁冷放入60℃的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡1小时；然后取出，并用0℃的0.9wt%盐水漂洗。
经测试，经过本实施例处理后的竹片的硬度为18HB。
实施例3
竹片的软化处理方法如下：
先将竹片放入冷库中，在-3℃下冷冻6小时；然后取出，并趁冷放入55℃的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡1小时；然后取出，并用-3℃的0.9wt%盐水漂洗。
经测试，经过本实施例处理后的竹片的硬度为20HB。

Claims (1)

1.一种竹片的软化处理方法，其特征在于：先将竹片放入冷库中，在-5℃～0℃下冷冻5小时～8小时；然后取出，并趁冷放入50℃～60℃的浸泡液中，在功率为80W、频率为50Khz的超声条件下保温浸泡1小时～2小时；然后取出，并用-5℃～0℃的0.9wt%盐水漂洗；
其中，所述浸泡液按重量份计，由50份无水乙醇、2份腰果酚、1份硬脂酸锌以及100份电导率小于5μS/cm的去离子水混合制得。
CN201610580740.6A 2016-07-21 2016-07-21 竹片的软化处理方法 Pending CN106166778A (zh)