CN104480234A - 一种针对皮质文物羊毛脂加脂剂的制备方法 - Google Patents
一种针对皮质文物羊毛脂加脂剂的制备方法 Download PDFInfo
- Publication number
- CN104480234A CN104480234A CN201410579169.7A CN201410579169A CN104480234A CN 104480234 A CN104480234 A CN 104480234A CN 201410579169 A CN201410579169 A CN 201410579169A CN 104480234 A CN104480234 A CN 104480234A
- Authority
- CN
- China
- Prior art keywords
- lanolin
- parts
- solution
- fatting agent
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种针对皮质文物羊毛脂加脂剂的制备方法,采取以下步骤:A)按质量分数取羊毛脂4份,将其溶于20份去离子水中混合均匀;B)将步骤A)得到溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;C)加入表面活性剂进行均匀混合;D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;E)向步骤D)处理后的溶液中按质量分数加入1-3份2-辛基-4-异噻唑啉-3-酮、1-3份亚硫酸钠、10-30份乙醇、10-20份冰醋酸、80-100份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。通过上述步骤得到针对皮质文物羊毛脂加脂剂,具有良好的加脂抗菌防腐的作用。
Description
技术领域
本发明属于皮质文物保护领域,尤其涉及一种通过超声波技术针对皮质文物制备羊毛脂抗菌加脂剂的方法。
背景技术
皮革加脂是皮革生产过程中的重要工序之一,是用加脂材料处理皮革,使皮革吸收一定量的油脂而赋予革一定的物理、机械性能和使用性能的过程,它能润滑皮革纤维,防止皮革板结、折裂,又使皮革具有相应的弹性、韧性、延伸性和柔软性等良好的物理力学性能。皮革加脂的方法包括乳液加脂和干加脂,其中乳液加脂是轻革加脂的主要方法。所用加脂剂主要是由中性油和乳化成分组成的。加脂剂中的油成分不同,经其加脂处理的皮革也具有不同的风格。加脂剂中的乳化成分实际上就是表面活性剂。可以直接添加相应类别的表面活性剂于油成分中,制成外乳化体系的加脂剂。用这种方法制备的加脂剂其应用性能差,目前很少使用。目前几乎是通过化学改性在不溶于水的油脂分子中引入亲水基团,制成自乳化体系的加脂剂。化学改性方法是赋予皮革加脂剂不同特性的重要手段。按加脂剂中乳化成分所带的电荷可将加脂剂分为:阴离子型、阳离子型、两性型和非离子型。
皮质文物由于各种不良因素的综合作用,发生脱水、脱脂、霉变等变化, 变得非常坚硬,其主要成分胶原蛋白纤维和弹性蛋白纤维也发生了严重的变性,使皮革变得异常的坚硬,不利于文物长期保存。针对这种局面,急需对其进行研究保护工作。目前大多数皮革加脂剂多采用酸类改性的方法,不仅污染环境,同时残留的酸液也可能对皮革文物产生二次破坏。同时由于皮革文物内部大量物质流失,内部的胶原纤维出现既缠结又断裂现象,所以传统的皮革加脂剂并不适用于皮革文物。为了保护文物,研究一种新型适用于皮革文物的加脂剂十分重要。
发明内容
为了解决现有技术问题的缺点,本发明针对皮质文物,提供一种通过超声波技术制备羊毛脂抗菌加脂剂的方法。
为此采用如下技术方案:一种针对皮质文物羊毛脂加脂剂的制备方法,其特征在于采取以下步骤:
A)按质量分数取羊毛脂4份,将其溶于20份去离子水中,在常温下充分搅拌使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;
C)向经过步骤B)处理的溶液中加入表面活性剂进行均匀混合,所述表面活性剂为十二烷基苯磺酸钠阴离子表面活性剂,加入量为步骤A)中选取羊毛脂质量的5%-10%;
D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;处理后的溶液在常温下静置10-15分钟后,过滤留取下层乳清状溶液;
E)向步骤D)处理后的溶液中按质量分数加入1-3份2-辛基-4-异噻唑啉-3-酮、1-3份亚硫酸钠、10-30份乙醇、10-20份冰醋酸、80-100份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。
通过上述步骤得到针对皮质文物羊毛脂加脂剂,具有良好的加脂抗菌防腐的作用。本发明与现有技术相比,具有优点是:1)使用超声波技术乳化加工,可以避免传统的硫酸化、磷酸化、磺化改性所带来的污染;2)使用超声波技术乳化加工的加脂剂,乳液粒径更细微,能更好的渗透进皮革文物内部,起到良好的加脂作用;3)使用超声波技术乳化加工,可以避免传统加脂剂所残留的强酸对皮革文物造成二次破坏;4)羊毛脂加脂剂中添加了抗菌成分,可以使皮革更好的抑制霉菌、细菌。
具体实施方式
实施例1采取以下步骤:
A)按质量分数取羊毛脂4份,将其溶于20份去离子水中,在常温下充分搅拌使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪中,在100W的功率下处理30分钟;
C)向经过步骤B)处理的溶液中加入表面活性剂进行均匀混合,所述表面活性剂为十二烷基苯磺酸钠阴离子表面活性剂,加入量为步骤A)中选取羊毛脂质量的5%;
D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在100W的功率下处理30分钟;处理后的溶液在常温下静置10分钟后,过滤留取下层乳清状溶液;
E)向步骤D)处理后的溶液中按质量分数加入1份2-辛基-4-异噻唑啉-3-酮、1份亚硫酸钠、10份乙醇、10份冰醋酸、80份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。
实施例2采取以下步骤:
A)按质量分数取羊毛脂4份,将其溶于20份去离子水中,在常温下充分搅拌使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪中,在150W的功率下处理20分钟;
C)向经过步骤B)处理的溶液中加入表面活性剂进行均匀混合,所述表面活性剂为十二烷基苯磺酸钠阴离子表面活性剂,加入量为步骤A)中选取羊毛脂质量的15%;
D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在150W的功率下处理20分钟;处理后的溶液在常温下静置12分钟后,过滤留取下层乳清状溶液;
E)向步骤D)处理后的溶液中按质量分数加入2份2-辛基-4-异噻唑啉-3-酮、2份亚硫酸钠、20份乙醇、15份冰醋酸、90份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。
实施例3采取以下步骤:
A)按质量分数取羊毛脂4份,将其溶于20份去离子水中,在常温下充分搅拌使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪中,在200W的功率下处理10分钟;
C)向经过步骤B)处理的溶液中加入表面活性剂进行均匀混合,所述表面活性剂为十二烷基苯磺酸钠阴离子表面活性剂,加入量为步骤A)中选取羊毛脂质量的10%;
D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在200W的功率下处理10分钟;处理后的溶液在常温下静置15分钟后,过滤留取下层乳清状溶液;
E)向步骤D)处理后的溶液中按质量分数加入3份2-辛基-4-异噻唑啉-3-酮、3份亚硫酸钠、30份乙醇、20份冰醋酸、100份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。
Claims (1)
1.一种针对皮质文物羊毛脂加脂剂的制备方法,其特征在于采取以下步骤:
A)按质量分数取羊毛脂4份,将其溶于20份去离子水中,在常温下充分搅拌使其混合均匀;
B)将步骤A)得到溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;
C)向经过步骤B)处理的溶液中加入表面活性剂进行均匀混合,所述表面活性剂为十二烷基苯磺酸钠阴离子表面活性剂,加入量为步骤A)中选取羊毛脂质量的5%-10%;
D)将步骤C)所得的溶液放入超声波细胞破碎仪中,在100-200W的功率下处理10-30分钟;处理后的溶液在常温下静置10-15分钟后,过滤留取下层乳清状溶液;
E)向步骤D)处理后的溶液中按质量分数加入1-3份2-辛基-4-异噻唑啉-3-酮、1-3份亚硫酸钠、10-30份乙醇、10-20份冰醋酸、80-100份去离子水,在常温下充分搅拌使其混合均匀后,得到针对皮质文物羊毛脂加脂剂。