CN104356927B - 一种uv固化抗静电涂料 - Google Patents
一种uv固化抗静电涂料 Download PDFInfo
- Publication number
- CN104356927B CN104356927B CN201410624512.5A CN201410624512A CN104356927B CN 104356927 B CN104356927 B CN 104356927B CN 201410624512 A CN201410624512 A CN 201410624512A CN 104356927 B CN104356927 B CN 104356927B
- Authority
- CN
- China
- Prior art keywords
- antistatic
- antistatic coating
- acrylate
- solidifies
- polyfunctional group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于涂料领域，具体涉及一种UV固化抗静电涂料。所述的UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸脂25‑35％，多官能团氨基丙烯酸酯10‑20％，光引发剂1‑6％，抗静电树脂35‑50％，流平剂0.2‑0.5％，防沉剂0.2‑0.5％，哑光粉3‑6％。本发明采用丙烯酸酯季铵盐类抗静电树脂，不仅能够满足抗静电的要求，而且与UV固化体系具有良好的相容性，本发明中采用的抗静电树脂不仅具有良好的抗静电作用，而且能够稀释低聚物、调节体系粘度、参与光固化过程，最终影响体系光固化速度；抗静电树脂的加入，能和光固化体系形成一个完整的体系。
Description
技术领域
本发明属于涂料领域，特别涉及一种UV固化抗静电涂料。
背景技术
日常生活中，由于摩擦会产生静电，而静电的存在会给很多场合带来危害，如家具会容易吸尘，计算机等仪器工作稳定性下降甚至出现障碍，输油管道等发生燃烧或爆炸等。为了防止静电带来的危害，在家具、地板等材料表面涂装抗静电的涂料是一种很有效的方法，这样既能拥有抗静电的功能，又具有涂料的美观防护作用。
常见的方法是向涂料中添加导电性金属氧化物、纳米金属粉体、金属溶胶、纳米炭黑等导电填料或导电聚合物分散液、离子液体、表面活性剂等导电物，然后在物品表面涂装固化后形成。这些抗静电涂料虽然能够满足抗静电的要求，但是在使用过程中会出现与树脂不相容的现象，特别是在光固化涂料中，直接影响光固化效果。
发明内容
本发明的目的在于提供一种UV固化抗静电涂料。本发明采用丙烯酸酯季铵盐类抗静电树脂，不仅能够满足抗静电的要求，而且与UV固化体系具有良好的相容性。
本发明解决其技术问题所采用的技术方案是：
一种UV固化抗静电涂料，由以下原料按质量百分比组成：
多官能团聚氨酯丙烯酸酯25-35％
多官能团氨基丙烯酸酯10-20％
光引发剂1-6％
抗静电树脂35-50％
流平剂0.2-0.5％
防沉剂0.2-0.5％
哑光粉3-6％。
作为优选，所述多官能团聚氨酯丙烯酸酯为芳香族聚氨酯丙烯酸酯或脂肪族聚氨酯丙烯酸酯。
作为优选，所述流平剂为有机硅流平剂或丙烯酸酯流平剂。
作为优选，所述光引发剂为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、二苯基-(2,4,6-三甲基苯甲酰)氧膦、二苯甲酮中的一种或几种。
作为优选，所述抗静电树脂由丙烯酸酯和季铵盐在有机溶剂中反应而成。
具体地，所述有机溶剂为甲苯、环己烷、二甲苯中的一种或几种。
具体地，所述丙烯酸酯为1,6-乙二醇二丙烯酸酯、三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、甲基丙烯酸羟乙酯中的一种或几种。
一种UV固化抗静电涂料的用途，所述UV固化抗静电涂料用于PVC抗静电地板、PVC抗静电贴面板、三聚氰胺抗静电贴面板的涂装。
本发明的有益效果是：本发明采用丙烯酸酯季铵盐类抗静电树脂，不仅能够满足抗静电的要求，而且与UV固化体系具有良好的相容性，本发明中采用的抗静电树脂不仅具有良好的抗静电作用，而且能够稀释低聚物、调节体系粘度、参与光固化过程，最终影响体系光固化速度；抗静电树脂的加入，能和光固化体系形成一个完整的体系，而不是在完整的体系中添加额外的抗静电剂，使UV固化体系具有良好的相容性；并且本发明的UV固化抗静电涂料无色透明，能快速固化干燥，环保无毒，抗静电性能优异且持久稳定，涂料表面电阻能达到106-109Ω/cm2；表干好、不发粘、返粘，抗划伤耐磨。可用于PVC抗静电地板、PVC抗静电贴面板、三聚氰胺抗静电贴面板等的涂装。
具体实施方式
下面结合实施例进一步阐述本发明：
本发明采用的抗静电树脂的制备方法可以为：
1)配制季铵盐水溶液，质量百分比为40％。；
2)将丙烯酸酯40g、配制好的季铵盐水溶液100g、对羟基苯甲醚0.5g、有机溶剂65g、BHT抗氧剂0.2g加入四口烧瓶，搅拌升温，100-120度回流5-6小时除去水分，脱溶剂30min，降温至常温，过滤出料，得到丙烯酸酯季铵盐抗静电树脂。
其中丙烯酸酯可以为1,6-乙二醇二丙烯酸酯、三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、甲基丙烯酸羟乙酯中的一种或几种；有机溶剂可以为甲苯、环己烷、二甲苯中的一种或几种。
实施例1
UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸酯(长兴6145产品)25％，多官能团氨基丙烯酸酯(江门恒光2600产品)20％，光引发剂184(CIBA公司产品)5％，甲基丙烯酸羟乙酯季铵盐抗静电树脂45％，流平剂(BYK333产品)0.5％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)4％。
实施例2
UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸酯(长兴6145产品)25％，多官能团氨基丙烯酸酯(江门恒光2600产品)15％，光引发剂184(CIBA公司产品)5％，甲基丙烯酸羟乙酯季铵盐抗静电树脂50％，流平剂(BYK333产品)0.5％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)4％。
实施例3
UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸树脂(江门恒光7162产品)33％，多官能团氨基丙烯酸酯(江门恒光2600产品)18％，光引发剂二苯甲酮(长沙新宇)6％，三丙二醇二丙烯酸酯季铵盐抗静电树脂35％，流平剂(BYK306产品)0.3％，防沉剂(BYK410产品)0.2％，哑光粉(BYK965产品)4.5％。
实施例4
UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸树脂(江门恒光7160产品)32％，多官能团氨基丙烯酸酯(江门恒光2600产品)10％，光引发剂TPO(CIBA公司产品)4％，三羟甲基丙烷三丙烯酸酯季铵盐抗静电树脂50％，流平剂(BYK306产品)0.5％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)3％。
实施例5
UV固化抗静电涂料的质量百分比组成为：多官能团聚氨酯丙烯酸树脂(长兴6148产品)35％，多官能团氨基丙烯酸酯(江门恒光2600产品)14％，光引发剂1173(北京英力)1％，1,6-乙二醇二丙烯酸酯季铵盐抗静电树脂42％，流平剂(BYK306产品)0.2％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)6％。
对比例1
UV固化涂料的质量百分比组成为：多官能团聚氨酯丙烯酸酯(长兴6145产品)35％，多官能团氨基丙烯酸酯(江门恒光2600产品)20％，光引发剂184(CIBA公司产品)5％，甲基丙烯酸羟乙酯15％，季铵盐30％，流平剂(BYK333产品)0.5％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)4％。
对比例2
UV固化涂料的质量百分比组成为：多官能团聚氨酯丙烯酸酯(长兴6145产品)35％，多官能团氨基丙烯酸酯(江门恒光2600产品)20％，光引发剂184(CIBA公司产品)5％，甲基丙烯酸羟乙酯45％，流平剂(BYK333产品)0.5％，防沉剂(BYK410产品)0.5％，哑光粉(BYK965产品)4％。
将PVC素板除尘，辊涂两层抗静电涂料，涂布量共10-15g/m2，紫外灯固化完全(一般固化时间为3-5s)，固化能量300-350mJ/cm2，得到辊涂有抗静电层的PVC板。
测试方法：
硬度测试：根据GB/T6739测试标准进行。
附着力测试：根据GB/T9286测试标准进行。
表面电阻测试：根据GB50611测试标准进行；同时对辊涂有抗静电层的PVC板进行了酒精擦拭测试，擦拭次数为50次，并测得其电阻。
测试结果如下：
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (7)
1.一种UV固化抗静电涂料，由以下原料按质量百分比组成：
多官能团聚氨酯丙烯酸酯25-35％
多官能团氨基丙烯酸酯10-20％
光引发剂1-6％
抗静电树脂35-50％
流平剂0.2-0.5％
防沉剂0.2-0.5％
哑光粉3-6％
所述抗静电树脂由丙烯酸酯和季铵盐在有机溶剂中反应而成。
2.如权利要求1所述一种UV固化抗静电涂料，其特征在于：所述多官能团聚氨酯丙烯酸酯为芳香族聚氨酯丙烯酸酯或脂肪族聚氨酯丙烯酸酯。
3.如权利要求1所述一种UV固化抗静电涂料，其特征在于：所述流平剂为有机硅流平剂或丙烯酸酯流平剂。
4.如权利要求1所述一种UV固化抗静电涂料，其特征在于：所述光引发剂为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、二苯基-(2,4,6-三甲基苯甲酰)氧膦、二苯甲酮中的一种或几种。
5.如权利要求1所述一种UV固化抗静电涂料，其特征在于：所述有机溶剂为甲苯、环己烷、二甲苯中的一种或几种。
6.如权利要求1所述一种UV固化抗静电涂料，其特征在于：所述丙烯酸酯为三丙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、甲基丙烯酸羟乙酯中的一种或几种。
7.一种如权利要求1-6任一项所述UV固化抗静电涂料的用途，其特征在于：所述UV固化抗静电涂料用于PVC抗静电地板、PVC抗静电贴面板、三聚氰胺抗静电贴面板的涂装。