CN104292806A - 一种吸水树脂的制作方法 - Google Patents
一种吸水树脂的制作方法 Download PDFInfo
- Publication number
- CN104292806A CN104292806A CN201410459090.0A CN201410459090A CN104292806A CN 104292806 A CN104292806 A CN 104292806A CN 201410459090 A CN201410459090 A CN 201410459090A CN 104292806 A CN104292806 A CN 104292806A
- Authority
- CN
- China
- Prior art keywords
- water
- resin
- clay
- steps
- carboxylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种吸水树脂的制作方法，包括以下步骤：粘合剂2-6g、碎陶瓷3-5g、吡咯烷酮羧酸一三乙醇胺盐5-12g、苯甲酸钠树脂5-10g、粘土3-5g、聚氨酯短纤维12-16g、呢子料纤维5-12g、氢氧化钠0.2-0.6g和氧化铋1-5g。上述的原材料共同混合以后，加入氧化钙5-12g作为催化剂，在反应釜中加热100-240摄氏度，反应10-26分钟，冷却。然后进行纯化处理，时间10-20分钟，得到的材料倒入模具中压铸成型。本方法制作的步骤，创新的利用了纯化处理，本方法制作的树脂具有吸水的功能，非常奇特。可以广泛应用在需要吸潮的地方使用。
Description
技术领域
本发明属于材料领域，特别涉及一种吸水树脂的制作方法。
背景技术
通常大家会认为树脂是一种不吸水的材料，但是如果当树脂做成孔状并且，添加了细致的吸水材料，则可以起到意想不到的效果。
发明内容
本发明的目的是提供一种吸水树脂的制作方法，本方法制作的树脂具有吸水的功能，非常奇特。
采用的技术方案是：
一种吸水树脂的制作方法，包括以下步骤：
粘合剂2-6g、碎陶瓷3-5g、吡咯烷酮羧酸一三乙醇胺盐5-12g、苯甲酸钠树脂5-10g、粘土3-5g、聚氨酯短纤维12-16g、呢子料纤维5-12g、氢氧化钠0.2-0.6g和氧化铋1-5g。
上述的原材料共同混合以后，加入氧化钙5-12g作为催化剂，在反应釜中加热100-240摄氏度，反应10-26分钟，冷却。
然后进行纯化处理，时间10-20分钟，得到的材料倒入模具中压铸成型。
其优点在于：
本方法制作的步骤，创新的利用了纯化处理，本方法制作的树脂具有吸水的功能，非常奇特。可以广泛应用在需要吸潮的地方使用。
具体实施方式
实施例1
一种吸水树脂的制作方法，包括以下步骤：
粘合剂2g、碎陶瓷3g、吡咯烷酮羧酸一三乙醇胺盐5g、苯甲酸钠树脂5g、粘土3g、聚氨酯短纤维12g、呢子料纤维5g、氢氧化钠0.2和氧化铋1g。
上述的原材料共同混合以后，加入氧化钙5g作为催化剂，在反应釜中加热100摄氏度，反应10分钟，冷却。
然后进行纯化处理，时间10分钟，得到的材料倒入模具中压铸成型。
实施例2
一种吸水树脂的制作方法，包括以下步骤：
粘合剂6g、碎陶瓷5g、吡咯烷酮羧酸一三乙醇胺盐12g、苯甲酸钠树脂10g、粘土5g、聚氨酯短纤维16g、呢子料纤维12g、氢氧化钠0.6g和氧化铋5g。
上述的原材料共同混合以后，加入氧化钙12g作为催化剂，在反应釜中加热240摄氏度，反应26分钟，冷却。
然后进行纯化处理，时间20分钟，得到的材料倒入模具中压铸成型。
实施例3
一种吸水树脂的制作方法，包括以下步骤：
粘合剂5g、碎陶瓷4g、吡咯烷酮羧酸一三乙醇胺盐9g、苯甲酸钠树脂6g、粘土4g、聚氨酯短纤维13g、呢子料纤维10g、氢氧化钠0.3g和氧化铋4g。
上述的原材料共同混合以后，加入氧化钙6g作为催化剂，在反应釜中加热137摄氏度，反应13分钟，冷却。
然后进行纯化处理，时间16分钟，得到的材料倒入模具中压铸成型。
Claims (4)
1.一种吸水树脂的制作方法，其特征在于包括以下步骤：
粘合剂2-6g、碎陶瓷3-5g、吡咯烷酮羧酸一三乙醇胺盐5-12g、苯甲酸钠树脂5-10g、粘土3-5g、聚氨酯短纤维12-16g、呢子料纤维5-12g、氢氧化钠0.2-0.6g和氧化铋1-5g；
上述的原材料共同混合以后，加入氧化钙5-12g作为催化剂，在反应釜中加热100-240摄氏度，反应10-26分钟，冷却；
然后进行纯化处理，时间10-20分钟，得到的材料倒入模具中压铸成型。
2.根据权利要求1所述的一种吸水树脂的制作方法，其特征在于包括以下步骤：
粘合剂2g、碎陶瓷3g、吡咯烷酮羧酸一三乙醇胺盐5g、苯甲酸钠树脂5g、粘土3g、聚氨酯短纤维12g、呢子料纤维5g、氢氧化钠0.2和氧化铋1g；
上述的原材料共同混合以后，加入氧化钙5g作为催化剂，在反应釜中加热100摄氏度，反应10分钟，冷却。
3.根据权利要求1所述的一种吸水树脂的制作方法，其特征在于包括以下步骤：
粘合剂6g、碎陶瓷5g、吡咯烷酮羧酸一三乙醇胺盐12g、苯甲酸钠树脂10g、粘土5g、聚氨酯短纤维16g、呢子料纤维12g、氢氧化钠0.6g和氧化铋5g；
上述的原材料共同混合以后，加入氧化钙12g作为催化剂，在反应釜中加热240摄氏度，反应26分钟，冷却。
4.根据权利要求1所述的一种吸水树脂的制作方法，其特征在于包括以下步骤：
粘合剂5g、碎陶瓷4g、吡咯烷酮羧酸一三乙醇胺盐9g、苯甲酸钠树脂6g、粘土4g、聚氨酯短纤维13g、呢子料纤维10g、氢氧化钠0.3g和氧化铋4g；
上述的原材料共同混合以后，加入氧化钙6g作为催化剂，在反应釜中加热137摄氏度，反应13分钟，冷却。