CN104263062A - High-adsorption wear-resistant water-based environment-friendly photocuring tin printing ink - Google Patents
High-adsorption wear-resistant water-based environment-friendly photocuring tin printing ink Download PDFInfo
- Publication number
- CN104263062A CN104263062A CN201410445768.XA CN201410445768A CN104263062A CN 104263062 A CN104263062 A CN 104263062A CN 201410445768 A CN201410445768 A CN 201410445768A CN 104263062 A CN104263062 A CN 104263062A
- Authority
- CN
- China
- Prior art keywords
- ink
- parts
- deionized water
- environment
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of researching environment-friendly ink, and particularly relates to a high-adsorption wear-resistant water-based environment-friendly photocuring tin printing ink. The ink is prepared from the following raw materials in parts by weight: 0.1-0.2 part of tungsten disulfide, 5-8 parts of nanosilicon dioxide suspension with solid content of 30%, 1-2 parts of sodium p-styrene sulfonate, 0.1-0.2 part of alpha-methylglucoside, 20-26 parts of water-based polyurethane acrylate emulsion with solid content of 40%-50%, 3-6 parts of photoinitiator, 15-26 parts of deionized water, 8-10 parts of ethanol, 8-13 parts of environment-friendly pigment, and 1-2 parts of auxiliaries. The ink is water-based, high in environment-friendliness, the added tungsten disulfide has excellent lubrication property and can improve the compatibility of all raw materials, the adsorbability of the ink on the surface of a metal base material can be enhanced, and by combining the auxiliaries and other components, the ink not only has excellent printing adaptability, but also is fine and stable, difficult to cluster, uniform and fast to dry compared with the existing products, the coating is tough and wear-resistant and the printing is fast and efficient.
Description
Technical field
The present invention relates to a kind of environment-friendly ink, be specifically related to a kind of high absorption abrasion-resistance water environmental protection photocuring tin printing ink.
Background technology
Ink is widely used in printing industry, it is mainly by resin, pigment, solvent, the compositions such as auxiliary agent are formed, the ink major part that current printing industry uses is solvent type ink, this kind of ink can give out VOCs human body and environment being had to harm, some ink that is direct and human contact may work the mischief to health, some objectionable impurities even can penetrate into food by packaging, in the packing material such as cigarette and medicine, therefore the most important thing that feature of environmental protection ink is Future Development is developed, fundamentally to improve the feature of environmental protection of ink, need to set about from change ink formulations, Novel environment-friendlymaterial material is adopted to replace conventional toxic objectionable constituent, obtain gratifying rate of drying simultaneously, use properties and good printing adaptability.
Summary of the invention
The object of the invention is to, provide a kind of high absorption abrasion-resistance water environmental protection photocuring tin printing ink, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of high absorption abrasion-resistance water environmental protection photocuring tin printing ink, it is characterized in that, this ink is made up of the raw material of following weight part: nanometer titanium dioxide silicon suspension 5-8, the Sodium styrene sulfonate 1-2 of tungsten disulfide 0.1-0.2, solid content 30%, methyl glucose glucoside 0.1-0.2, solid content are aqueous polyurethane acrylate emulsion 20-26, light trigger 3-6, deionized water 15-26, ethanol 8-10, environmental-friendly pigment 8-13, the auxiliary agent 1-2 of 40-50%;
Described auxiliary agent is made up of the raw material of following weight part: propylene glycol phenylate 4-5, oxidized polyethlene wax 5-8, Ethylene glycol dimethacrylate 2-3, deionized water 15-18, Sodium dodecylbenzene sulfonate 1-3, ethylene glycol monomethyl ether 2-3, preparation method is: first oxidized polyethlene wax is heated to molten state, then dropwise Ethylene glycol dimethacrylate is added, do not stop to stir with the speed of 800-1000 rev/min in dropping process, after dropwising, constant temperature keeps 20-30min for subsequent use, again other remaining component is mixed with deionized water, after each composition dissolves completely, solution is heated to boiling, gained aqueous phase solution makes stable emulsion with oxidized polyethlene wax-dimethacrylate ethanol ester mixture mix and blend again.
Described one height absorption abrasion-resistance water environmental protection photocuring tin printing ink, its preparation process is: be first dissolved in by tungsten disulfide in the deionized water of 50-60 DEG C, add Sodium styrene sulfonate, methyl glucose glucoside subsequently, continue to be stirred to after material dissolves completely, add polyurethane-acrylate emulsion, continue dispersed with stirring to material cool to room temperature, the material of gained is mixed with other remaining component, after high-speed stirring dispersion 40-50min, drop into grinding machine for grinding, to particle diameter≤10 μm of gained slurry, to obtain final product.
First the advantage of ink of the present invention is its feature of environmental protection, and use deionized water as medium, avoid the use of organic solvent, the raw material chosen also is to human body and environment is nontoxic or the composition of low toxicity; Tungsten disulfide in raw material has good oilness, the consistency between each raw material can be improved, the adsorptivity of ink in metallic substrate surface can be increased simultaneously, prevent from coming off, be combined with drying aid, the auxiliary agent accelerating film forming effect and other composition again, make ink of the present invention compared with currently available products, not only have excellent printing adaptability, ink exquisiteness is stable, not easily reunite, uniform drying is quick, coating tough and hard wear resistant, prints quickness and high efficiency.
Embodiment
Embodiment
Ink prepared by the present embodiment is made up of the raw material of following weight part: the nanometer titanium dioxide silicon suspension 8 of tungsten disulfide 0.1, solid content 30%, Sodium styrene sulfonate 1, methyl glucose glucoside 0.1, solid content are aqueous polyurethane acrylate emulsion 24, light trigger 4, deionized water 26, ethanol 8, environmental-friendly pigment 12, the auxiliary agent 1 of 50%.
Wherein auxiliary agent is made up of the raw material of following weight part: propylene glycol phenylate 5, oxidized polyethlene wax 8, Ethylene glycol dimethacrylate 3, deionized water 18, Sodium dodecylbenzene sulfonate 1, ethylene glycol monomethyl ether 2, preparation method is: first oxidized polyethlene wax is heated to molten state, then dropwise Ethylene glycol dimethacrylate is added, do not stop to stir with the speed of 1000 revs/min in dropping process, after dropwising, constant temperature keeps 30min for subsequent use, again other remaining component is mixed with deionized water, after each composition dissolves completely, solution is heated to boiling, gained aqueous phase solution makes stable emulsion with oxidized polyethlene wax-dimethacrylate ethanol ester mixture mix and blend again.
The preparation process of this printing-ink is: be first dissolved in by tungsten disulfide in the deionized water of 50-60 DEG C, add Sodium styrene sulfonate, methyl glucose glucoside subsequently, continue to be stirred to after material dissolves completely, add polyurethane-acrylate emulsion, continue dispersed with stirring to material cool to room temperature, the material of gained is mixed with other remaining component, after high-speed stirring dispersion 50min, drop into grinding machine for grinding, to particle diameter≤10 μm of gained slurry, to obtain final product.
By the ink printing obtained by the present embodiment on thin aluminum sheet, after its complete drying, according to corresponding national examination criteria, this ink in the performance test results of substrate surface is:
Claims (2)
1. one kind high absorption abrasion-resistance water environmental protection photocuring tin printing ink, it is characterized in that, this printing-ink is made up of the raw material of following weight part: nanometer titanium dioxide silicon suspension 5-8, the Sodium styrene sulfonate 1-2 of tungsten disulfide 0.1-0.2, solid content 30%, methyl glucose glucoside 0.1-0.2, solid content are aqueous polyurethane acrylate emulsion 20-26, light trigger 3-6, deionized water 15-26, ethanol 8-10, environmental-friendly pigment 8-13, the auxiliary agent 1-2 of 40-50%;
Described auxiliary agent is made up of the raw material of following weight part: propylene glycol phenylate 4-5, oxidized polyethlene wax 5-8, Ethylene glycol dimethacrylate 2-3, deionized water 15-18, Sodium dodecylbenzene sulfonate 1-3, ethylene glycol monomethyl ether 2-3, preparation method is: first oxidized polyethlene wax is heated to molten state, then dropwise Ethylene glycol dimethacrylate is added, do not stop to stir with the speed of 800-1000 rev/min in dropping process, after dropwising, constant temperature keeps 20-30min for subsequent use, again other remaining component is mixed with deionized water, after each composition dissolves completely, solution is heated to boiling, gained aqueous phase solution makes stable emulsion with oxidized polyethlene wax-dimethacrylate ethanol ester mixture mix and blend again.
2. a kind of high absorption abrasion-resistance water environmental protection photocuring tin printing ink as claimed in claim 1, its preparation process is: be first dissolved in by tungsten disulfide in the deionized water of 50-60 DEG C, add Sodium styrene sulfonate, methyl glucose glucoside subsequently, continue to be stirred to after material dissolves completely, add polyurethane-acrylate emulsion, continue dispersed with stirring to material cool to room temperature, the material of gained is mixed with other remaining component, after high-speed stirring dispersion 40-50min, drop into grinding machine for grinding, to particle diameter≤10 μm of gained slurry, to obtain final product.