CN104194682B - 一种环保型高性能高速卷烟接嘴胶的制备方法 - Google Patents
一种环保型高性能高速卷烟接嘴胶的制备方法 Download PDFInfo
- Publication number
- CN104194682B CN104194682B CN201410428936.4A CN201410428936A CN104194682B CN 104194682 B CN104194682 B CN 104194682B CN 201410428936 A CN201410428936 A CN 201410428936A CN 104194682 B CN104194682 B CN 104194682B
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- high performance
- aqueous solution
- filter tipping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种环保型高性能高速卷烟接嘴胶的制备方法,是通过以下步骤实现的:将交联型聚乙烯醇加到反应釜中溶解;将醋酸乙烯酯、丙烯酸、丙烯酸丁酯混合均匀后,加到滴加罐中;向反应釜中加入叔丁基过氧化氢水溶液、小苏打、柠檬酸三正丁酯,搅拌后分若干次加入亚硫酸氢钠水溶液,开始滴加单体;单体滴加分若干次进行,0.05~0.06mpa真空度下抽真空0.5~1小时,然后降温,检测、出料、包装,即得环保型高性能高速卷烟接嘴胶;本发明的有益效果为,本发明的制备方法能够满足车速在16000支/分钟及不同材质情况下的正常粘接需要,卷烟无漏气、掉嘴现象。
Description
技术领域
本发明涉及接嘴胶的制备方法,尤其涉及一种环保型高性能高速卷烟接嘴胶的制备方法。
背景技术
随着国家局对卷烟辅料环保性要求的提升,烟用水基胶作为卷烟生产中必不可少的材料,而且还是有机化工材料,对其环保性、安全性进行了严格规定,一方面是残留挥发性成分,如醋酸乙烯、甲醛等都进行了严格的限定,另一方面,对于允许添加物质,也进行了规定,出台了烟用水基胶许可使用名录。对于残留挥发性成分方面,大部分企业通过工艺调整、严格检测控制,可以满足要求,许可使用名录方面,仅局限于许可名录的材料,由于限制了硼砂等的使用,在车速高于10000支/分或高透滤棒、预打孔水松纸等粘接时,普遍存在粘接不够,有漏气掉嘴现象,并且设备脏车严重。针对以上问题,目前还没有好的解决方法。
发明内容
针对上述现有技术,本发明方提供了一种环保型高性能高速卷烟接嘴胶的制备方法,能够满足高速机及对不同材质的粘接要求,制备接嘴胶具有环保、高粘接、低渗透、持粘强等优点。
本发明是通过以下技术方案实现的:
一种环保型高性能高速卷烟接嘴胶,包括以下重量比的组分:
水40~45份,交联型聚乙烯醇2~10份,醋酸乙烯酯35~45份,丙烯酸0.5份~2份,丙烯酸丁酯5~10份,消泡剂0.1~1份,柠檬酸三正丁酯1.5~4.0份,质量浓度为2%的叔丁基过氧化氢水溶液0.01~0.08份,质量浓度为1%的亚硫酸氢钠水溶液0.02~0.08份,小苏打0.1~1份,异噻唑啉酮0.1~0.2份。
优选地,消泡剂为矿物油。
一种环保型高性能高速卷烟接嘴胶的制备方法,是通过以下步骤实现的:
将上述重量比的交联型聚乙烯醇加到反应釜中,升温到90±2℃,保温2小时,使其溶解;将醋酸乙烯酯、丙烯酸、丙烯酸丁酯混合均匀后,加到滴加罐中;在40~60℃时,加入叔丁基过氧化氢水溶液、小苏打、柠檬酸三正丁酯,搅拌30分钟后加入1/4亚硫酸氢钠水溶液,开始滴加单体,4~6小时滴加完毕;每小时加入1/4亚硫酸氢钠水溶液,滴加完后在50~60℃保温2~4小时,0.05~0.06mpa真空度下抽真空0.5~1小时,然后降温至35~40℃,加入消泡剂、异噻唑啉酮,搅拌30分钟检测、出料、包装,即得环保型高性能高速卷烟接嘴胶。
本发明提供了一种利用上述方法制备的环保型高性能高速卷烟接嘴胶。
一般来说,高速卷烟接嘴胶,一方面要满足不同机型、不同材质正常卷烟的要求,不漏气、无掉嘴,另一方面要保证卷接设备清洁。以往大家普遍采用硼砂交联以达到提升湿粘性、抗渗性等目的,保证在高速机、难粘材质上的粘接。在硼砂被限用后,在车速高于10000支/分钟或粘接高透滤棒和预打孔水松纸会出现掉嘴和漏气现象,严重影响到了卷烟质量。本发明通过选用交联型聚乙烯醇,采用醋酸乙烯酯和丙烯酸酯共聚的方式合成高粘接性醋丙共聚乳液,通过引发体系、除残措施等使产品残留单体量控制在小于300ppm,在行业规定要求范围内产品可以满足7000-16000支/分钟各种卷烟机及各种材料的粘结要求,卷烟卷接质量优异、上机适用性佳。
本发明使用的交联型聚乙烯醇,对部分羟基进行乙酰乙酰化处理,赋予了产品高粘接性、高抗渗透性,能够代替硼酸,解决了对难粘材质粘结问题及清洁生产问题。
本发明使用的醋酸乙烯、丙烯酸丁酯、丙烯酸,形成丙烯酸酯共聚体系,调节了产品玻璃化温度,赋予了产品高粘接性,可以保证在超高速运转情况下的粘接要求;
本发明使用的柠檬酸三正丁酯,绿色环保,可以在食品材料添加,能够降低产品成膜温度和柔韧性,以达到常温正常使用的目的;
本发明使用氧化还原引发体系,即叔丁基过氧化氢-亚硫酸氢钠,与传统的氧化剂需热引发相比,单一氧化剂温度在70℃以上,而氧化还原引发体系,用的还原剂能促使有机过氧化物在室温下分解而产生游离基,因此又称为促进剂,在50℃以下即可引发反应,反应效率高、产品转化率高,确保了低能耗和低残单;
本发明采用的后期氧化还原体系保温和通氮抽真空工艺,通过长时间、定期添加氧化还原引发剂进一步提高产品转化率,特殊的通氮抽空工艺可以进一步抽取残留的单体,通过以上措施确保将残留单体量控制在300ppm以下。
本发明的有益效果为,本发明的制备方法能够满足车速在7000-16000支/分钟及不同材质情况下的正常粘接需要,卷烟无漏气、掉嘴现象。
具体实施方式
下面结合实施例对本发明作进一步的说明。
将5份交联型聚乙烯醇加到反应釜中,加入40份的去离子水,升温到90±2℃,保温2小时,使其溶解;将36.5份醋酸乙烯酯、1份丙烯酸、7份丙烯酸丁酯混合均匀后,加到滴加罐中;降温至45℃,加入2份柠檬酸三正丁酯、0.1份小苏打、0.02份质量浓度为2%的叔丁基过氧化氢水溶液,搅拌30分钟后加入0.01份质量浓度为1%的亚硫酸氢钠水溶液、开始滴加单体;滴加过程每60分钟加一次0.01份质量浓度为1%的亚硫酸氢钠水溶液,4小时滴加完毕,升温至55℃,保温3小时,保温结束在0.05~0.06mpa真空度下抽真空1小时;降温至35℃,加入矿物油0.1份、异噻唑啉酮0.1份,搅拌30分钟,然后检验、出料、包装。
依据本发明制作的高速卷烟接嘴胶其各项指标均达到Q/SZ109001-2012烟用材料安全卫生要求,用料在烟用水基胶许可名录范围内,产品残单≤300ppm,甲醛≤5ppm,邻苯类、苯系物未检出。产品可以满足7000~16000支/分钟各种卷烟机组正常卷接要求,也可以满足预打孔和高透滤棒等难粘材质的粘结要求。具体指标见下表1:
表1本发明实施例1产品指标
项目名称 | 指标 |
粘度(mpa.s) | 2000-6000 |
固含量% | 50-55 |
最低成膜温度℃ | ≤15 |
残单(ppm) | ≤300 |
甲醛(ppm) | ≤5 |
苯系物 | 未检出 |
邻苯类 | 未检出 |
适合车速 | 7000-16000支/分钟 |
上述虽然对本发明的具体实施方式进行了描述,但并非对本发明保护范围的限制,所属领域技术人员应该明白,在本发明的技术方案的基础上,本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围以内。
Claims (4)
1.一种环保型高性能高速卷烟接嘴胶,其特征在于,包括以下重量比的组分:
水40~45份,交联型聚乙烯醇2~10份,醋酸乙烯酯35~45份,丙烯酸0.5份~2份,丙烯酸丁酯5~10份,消泡剂0.1~1份,柠檬酸三正丁酯1.5~4.0份,质量浓度为2%的叔丁基过氧化氢水溶液0.01~0.08份,质量浓度为1%的亚硫酸氢钠水溶液0.02~0.08份,小苏打0.1~1份,异噻唑啉酮0.1~0.2份;
所述交联型聚乙烯醇,对部分羟基进行乙酰乙酰化交联处理。
2.如权利要求1所述的一种环保型高性能高速卷烟接嘴胶,其特征在于,消泡剂为矿物油。
3.如权利要求1或2所述的一种环保型高性能高速卷烟接嘴胶的制备方法,其特征在于,是通过以下步骤实现的:
将上述重量比的交联型聚乙烯醇加到反应釜中,升温到90±2℃,保温2小时,使其溶解;将醋酸乙烯酯、丙烯酸、丙烯酸丁酯混合均匀后,加到滴加罐中;在40~60℃时,加入叔丁基过氧化氢水溶液、小苏打、柠檬酸三正丁酯,搅拌30分钟后加入1/4亚硫酸氢钠水溶液,开始滴加单体,4~6小时滴加完毕;每小时加入1/4亚硫酸氢钠水溶液,滴加完后在50~60℃保温2~4小时,0.05~0.06MPa真空度下抽真空0.5~1小时,然后降温至35~40℃,加入消泡剂、异噻唑啉酮,搅拌30分钟检测、出料、包装,即得环保型高性能高速卷烟接嘴胶。
4.如权利要求3所述的方法制备的一种环保型高性能高速卷烟接嘴胶。