CN104194623A - 一种烘箱用耐高温涂料及其制备方法 - Google Patents

一种烘箱用耐高温涂料及其制备方法 Download PDF

Info

Publication number
CN104194623A
CN104194623A CN201410479256.5A CN201410479256A CN104194623A CN 104194623 A CN104194623 A CN 104194623A CN 201410479256 A CN201410479256 A CN 201410479256A CN 104194623 A CN104194623 A CN 104194623A
Authority
CN
China
Prior art keywords
parts
temperature resistant
resistant coating
oven
baking oven
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410479256.5A
Other languages
English (en)
Other versions
CN104194623B (zh
Inventor
费金华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Baochun New Material Technology Co ltd
Original Assignee
Suzhou Shengpula New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Shengpula New Material Technology Co Ltd filed Critical Suzhou Shengpula New Material Technology Co Ltd
Priority to CN201410479256.5A priority Critical patent/CN104194623B/zh
Publication of CN104194623A publication Critical patent/CN104194623A/zh
Application granted granted Critical
Publication of CN104194623B publication Critical patent/CN104194623B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种烘箱用耐高温涂料及其制备方法，该涂料以质量份计含有以下成分：甲基苯基有机硅树脂43～57份，聚酰胺树脂1.8～3.4份，钛白粉10～22份，海泡石15～25份，空心微粉3～7份，二甲基硅油0.25～0.7份，丙烯酸树脂0.5～1.3份，钛白粉1～3份，锶黄0.5～2份，银离子抗菌剂0.5～1.5份，安息香0.3～1份，二氧化硅1～4.3份。本发明提供的涂料不仅具有普通涂料的性能，而且具有优异的耐热性、耐候性和耐腐蚀性，能耐800℃高温，适用于烘箱的涂装，烘箱在长期使用后，其表面的涂料不易变色剥落。

Description

一种烘箱用耐高温涂料及其制备方法
技术领域
本发明涉及涂料领域，尤其涉及一种烘箱用耐高温涂料及其制备方法。
背景技术
甲基苯基有机硅树脂具有优异的热氧化稳定性和电绝缘性能，并且具有卓越的耐潮、防水、防锈、耐候性能，用其制备的涂料的应用范围广泛。
烘箱是人们在日常生活中用来烘烤食物的。随着人们对生活质量要求的不断提高，目前烘箱的使用量在不断增加。现有的烘箱表面用涂料的耐热性、耐候性和耐腐蚀性能普遍较低，烘箱在长期使用后其表面的涂料容易变色、剥落。
发明内容
解决的技术问题：针对现有烘箱表面用涂料耐热性、耐候性和耐腐蚀性能低的缺点，本发明提供一种烘箱用耐高温涂料及其制备方法。
技术方案：一种烘箱用耐高温涂料，以质量份计含有以下成分：甲基苯基有机硅树脂43～57份，聚酰胺树脂1.8～3.4份，钛白粉10～22份，海泡石15～25份，空心微粉3～7份，二甲基硅油0.25～0.7份，丙烯酸树脂0.5～1.3份，钛白粉1～3份，锶黄0.5～2份，银离子抗菌剂0.5～1.5份，安息香0.3～1份，二氧化硅1～4.3份。
上述所述的一种烘箱用耐高温涂料，以质量份计含有以下成分：甲基苯基有机硅树脂50份，聚酰胺树脂2.7份，钛白粉16份，海泡石20份，空心微粉5份，二甲基硅油0.5份，丙烯酸树脂0.9份，钛白粉2份，锶黄1.2份，银离子抗菌剂1份，安息香0.6份，二氧化硅2.7份。
上述所述的一种烘箱用耐高温涂料的制备步骤如下：将甲基苯基有机硅树脂、聚酰胺树脂、钛白粉、海泡石、空心微粉、二甲基硅油、丙烯酸树脂、钛白粉、锶黄、银离子抗菌剂、安息香和二氧化硅加入混合机中，在转速为200r/min，温度为30～40℃下混合10min，得到混合物料；然后将混合物料转入熔融挤出机，设置挤出机温度，I区为70～80℃，II区为90～100℃，螺杆转速为1000～1200r/min，物料挤出后冷却至室温，用压片机压成薄片，再用粉碎设备粉碎，接着过140目筛，即得成品。
有益效果：本发明提供的一种烘箱用耐高温涂料及其制备方法，该涂料不仅具有普通涂料的性能，而且具有优异的耐热性、耐候性和耐腐蚀性，能耐800℃高温，适用于烘箱的涂装，烘箱在长期使用后，其表面的涂料不易变色剥落。
具体实施方式
实施例1
本实施例提供一种烘箱用耐高温涂料，以质量份计含有以下成分：甲基苯基有机硅树脂43份，聚酰胺树脂1.8份，钛白粉10份，海泡石15份，空心微粉3份，二甲基硅油0.25份，丙烯酸树脂0.5份，钛白粉1份，锶黄0.5份，银离子抗菌剂0.5份，安息香0.3份，二氧化硅1份。
一种烘箱用耐高温涂料的制备步骤如下：将甲基苯基有机硅树脂、聚酰胺树脂、钛白粉、海泡石、空心微粉、二甲基硅油、丙烯酸树脂、钛白粉、锶黄、银离子抗菌剂、安息香和二氧化硅加入混合机中，在转速为200r/min，温度为30℃下混合10min，得到混合物料；然后将混合物料转入熔融挤出机，设置挤出机温度，I区为70～80℃，II区为90～100℃，螺杆转速为1000～1200r/min，物料挤出后冷却至室温，用压片机压成薄片，再用粉碎设备粉碎，接着过140目筛，即得成品。
实施例2
本实施例提供一种烘箱用耐高温涂料，以质量份计含有以下成分：甲基苯基有机硅树脂57份，聚酰胺树脂3.4份，钛白粉22份，海泡石25份，空心微粉7份，二甲基硅油0.7份，丙烯酸树脂1.3份，钛白粉3份，锶黄2份，银离子抗菌剂1.5份，安息香1份，二氧化硅4.3份。
一种烘箱用耐高温涂料的制备步骤如下：将甲基苯基有机硅树脂、聚酰胺树脂、钛白粉、海泡石、空心微粉、二甲基硅油、丙烯酸树脂、钛白粉、锶黄、银离子抗菌剂、安息香和二氧化硅加入混合机中，在转速为200r/min，温度为40℃下混合10min，得到混合物料；然后将混合物料转入熔融挤出机，设置挤出机温度，I区为70～80℃，II区为90～100℃，螺杆转速为1000～1200r/min，物料挤出后冷却至室温，用压片机压成薄片，再用粉碎设备粉碎，接着过140目筛，即得成品。
实施例3
本实施例提供一种烘箱用耐高温涂料，以质量份计含有以下成分：甲基苯基有机硅树脂50份，聚酰胺树脂2.7份，钛白粉16份，海泡石20份，空心微粉5份，二甲基硅油0.5份，丙烯酸树脂0.9份，钛白粉2份，锶黄1.2份，银离子抗菌剂1份，安息香0.6份，二氧化硅2.7份。
一种烘箱用耐高温涂料的制备步骤如下：将甲基苯基有机硅树脂、聚酰胺树脂、钛白粉、海泡石、空心微粉、二甲基硅油、丙烯酸树脂、钛白粉、锶黄、银离子抗菌剂、安息香和二氧化硅加入混合机中，在转速为200r/min，温度为35℃下混合10min，得到混合物料；然后将混合物料转入熔融挤出机，设置挤出机温度，I区为70～80℃，II区为90～100℃，螺杆转速为1000～1200r/min，物料挤出后冷却至室温，用压片机压成薄片，再用粉碎设备粉碎，接着过140目筛，即得成品。
上述实施例1～实施例3的一种烘箱用耐高温涂料的技术性能指标，其检测结果如下：
检测结果
以上对本发明实施例进行了详细介绍，对于本领域的一般技术人员，依据本发明实施例的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (3)

1.一种烘箱用耐高温涂料，其特征在于以质量份计含有以下成分：甲基苯基有机硅树脂43～57份，聚酰胺树脂1.8～3.4份，钛白粉10～22份，海泡石15～25份，空心微粉3～7份，二甲基硅油0.25～0.7份，丙烯酸树脂0.5～1.3份，钛白粉1～3份，锶黄0.5～2份，银离子抗菌剂0.5～1.5份，安息香0.3～1份，二氧化硅1～4.3份。
2.根据权利要求1所述的一种烘箱用耐高温涂料，其特征在于以质量份计含有以下成分：甲基苯基有机硅树脂50份，聚酰胺树脂2.7份，钛白粉16份，海泡石20份，空心微粉5份，二甲基硅油0.5份，丙烯酸树脂0.9份，钛白粉2份，锶黄1.2份，银离子抗菌剂1份，安息香0.6份，二氧化硅2.7份。
3.如权利要求1所述的一种烘箱用耐高温涂料的制备方法，其特征在于该方法的制备步骤如下：将甲基苯基有机硅树脂、聚酰胺树脂、钛白粉、海泡石、空心微粉、二甲基硅油、丙烯酸树脂、钛白粉、锶黄、银离子抗菌剂、安息香和二氧化硅加入混合机中，在转速为200r/min，温度为30～40℃下混合10min，得到混合物料；然后将混合物料转入熔融挤出机，设置挤出机温度，I区为70～80℃，II区为90～100℃，螺杆转速为1000～1200r/min，物料挤出后冷却至室温，用压片机压成薄片，再用粉碎设备粉碎，接着过140目筛，即得成品。
CN201410479256.5A 2014-09-18 2014-09-18 一种烘箱用耐高温涂料及其制备方法 Active CN104194623B (zh)