CN103333605A - 一种耐高温甲基苯基聚硅氧烷树脂粉末涂料及其制备方法 - Google Patents
一种耐高温甲基苯基聚硅氧烷树脂粉末涂料及其制备方法 Download PDFInfo
- Publication number
- CN103333605A CN103333605A CN2013102074861A CN201310207486A CN103333605A CN 103333605 A CN103333605 A CN 103333605A CN 2013102074861 A CN2013102074861 A CN 2013102074861A CN 201310207486 A CN201310207486 A CN 201310207486A CN 103333605 A CN103333605 A CN 103333605A
- Authority
- CN
- China
- Prior art keywords
- methyl phenyl
- parts
- phenyl polysiloxane
- methyl
- polysiloxane resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温甲基苯基聚硅氧烷树脂粉末涂料及其制备方法,其组成原料为:甲基苯基聚硅氧烷树脂47-53、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、有机硅流平剂1.1-1.3、聚硅氧烷2.5-3.0、异氰脲酸三缩水甘油酯3.3-3.8、氮化铝粉末9-10、纳米砖渣粉末5.5-7.5、1-甲基戊醇1.3-1.8和丙二醇甲醚醋酸酯2-3。本发明甲基苯基聚硅氧烷树脂具有卓越的耐潮、防水、防锈、耐寒、耐臭氧和耐候性能,甲基苯基聚硅氧烷树脂的耐高温性好,耐热温度达到550℃以上。
Description
技术领域
本发明涉及粉末涂料领域,尤其涉及一种耐高温甲基苯基聚硅氧烷树脂粉末涂料及其制备方法。
背景技术
随着我国经济的持续稳定增长以及人民生活水平的不断提高,金属构件的粉末涂装业务也不断增加,尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业,粉末涂层能给金属提供优良的防腐保护及装饰性能,但由于用于上述领域的现有涂料的抗污染性能不理想,涂层上经常附着各类灰尘、污垢甚至是油污;抗粘贴能力也不理想,且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象,因此,涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足,提供一种耐高温甲基苯基聚硅氧烷树脂粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案:
一种耐高温甲基苯基聚硅氧烷树脂粉末涂料,其特征在于其组成原料的重量份为:甲基苯基聚硅氧烷树脂47-53、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、有机硅流平剂1.1-1.3、聚硅氧烷2.5-3.0、异氰脲酸三缩水甘油酯3.3-3.8、氮化铝粉末9-10、纳米砖渣粉末5.5-7.5、1-甲基戊醇1.3-1.8和丙二醇甲醚醋酸酯2-3。
所述的耐高温甲基苯基聚硅氧烷树脂粉末涂料,其特征在于其组成原料的重量份为:耐高温甲基苯基聚硅氧烷树脂50、过氧化叔丁基0.5、甲基三丁酮肟基硅烷10、有机硅流平剂1.2、聚硅氧烷2.8、异氰脲酸三缩水甘油酯3.5、氮化铝粉末10、纳米砖渣粉末6.5、1-甲基戊醇1.5和丙二醇甲醚醋酸酯2。
所述的耐高温甲基苯基聚硅氧烷树脂粉末涂料的制备方法,其特征在于包括以下步骤:
(1)将纳米砖渣粉末、1-甲基戊醇和丙二醇甲醚醋酸酯混合,加入过氧化叔丁基混合搅拌反应1-2小时,冷却;
(2)按组成原料的重量份称取各组成原料与步骤(1)物料混合,然后混合搅拌均匀,送入挤出机挤出造粒,挤出机温度为150-170℃,冷却后,研磨至240-300目时;停止研磨,包装。
本发明的有益效果:
本发明甲基苯基聚硅氧烷树脂具有卓越的耐潮、防水、防锈、耐寒、耐臭氧和耐候性能,甲基苯基聚硅氧烷树脂的耐高温性好,耐热温度达到550℃以上。可以大大提高甲基苯基聚硅氧烷树脂的抗低温变形能力、抗疲劳性、抗水损害能力、抗老化能力等综合性能,减少涂料的掉落和开裂现象,延迟涂料的使用寿命。
具体实施方式
实施例1:耐高温甲基苯基聚硅氧烷树脂粉末涂料,其组成原料的重量份(kg)为:耐高温甲基苯基聚硅氧烷树脂50、过氧化叔丁基0.5、甲基三丁酮肟基硅烷10、有机硅流平剂1.2、聚硅氧烷2.8、异氰脲酸三缩水甘油酯3.5、氮化铝粉末100、纳米砖渣粉末6.5、1-甲基戊醇1.5和丙二醇甲醚醋酸酯28。
耐高温甲基苯基聚硅氧烷树脂粉末涂料的制备方法,包括以下步骤:
(1)耐高温甲基苯基聚硅氧烷树脂的制备:
配方(kg):甲基苯基聚硅氧烷树脂95、无醛胶20、防老剂OD 2.0、甘油三酯2.0和氨丙基三乙氧基硅烷4.0;
耐高温方法如下:
将组成原料重量份称取甲基苯基聚硅氧烷树脂并升温至熔融状态,依次按重量份加入所述的无醛胶、防老剂OD和甘油三酯,搅拌35分钟,再按配方重量份加入上述的氨丙基三乙氧基硅烷,高速搅拌11小时,冷却至室温;
(2)按组成原料的重量份称取步骤(1)中的耐高温甲基苯基聚硅氧烷树脂和其他剩余组成原料与步骤(1)物料混合,然后混合并在反应釜中搅拌均匀,研磨至40μm时;停止研磨,包装。
将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的标志牌上,经185℃的充分固化,自然冷却至室温,放置20h 后,测定涂层性能,其涂层冲击强度≥ 87.2cm,耐盐雾时间≥ 3500h,人工加速老化时间≥ 3350h,耐热性能≥560℃,天然曝晒20个月不起泡、不生锈、不开裂、不剥离,对油污的分解率≥97.0%。耐热温度达到550℃以上。
Claims (3)
1.一种耐高温甲基苯基聚硅氧烷树脂粉末涂料,其特征在于其组成原料的重量份为:甲基苯基聚硅氧烷树脂47-53、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、有机硅流平剂1.1-1.3、聚硅氧烷2.5-3.0、异氰脲酸三缩水甘油酯3.3-3.8、氮化铝粉末9-10、纳米砖渣粉末5.5-7.5、1-甲基戊醇1.3-1.8和丙二醇甲醚醋酸酯2-3。
2.根据权利要求1所述的耐高温甲基苯基聚硅氧烷树脂粉末涂料,其特征在于其组成原料的重量份为:耐高温甲基苯基聚硅氧烷树脂50、过氧化叔丁基0.5、甲基三丁酮肟基硅烷10、有机硅流平剂1.2、聚硅氧烷2.8、异氰脲酸三缩水甘油酯3.5、氮化铝粉末10、纳米砖渣粉末6.5、1-甲基戊醇1.5和丙二醇甲醚醋酸酯2。
3.一种如权利要求1所述的耐高温甲基苯基聚硅氧烷树脂粉末涂料的制备方法,其特征在于包括以下步骤:
(1)将纳米砖渣粉末、1-甲基戊醇和丙二醇甲醚醋酸酯混合,加入过氧化叔丁基混合搅拌反应1-2小时,冷却;
(2)按组成原料的重量份称取各组成原料与步骤(1)物料混合,然后混合搅拌均匀,送入挤出机挤出造粒,挤出机温度为150-170℃,冷却后,研磨至240-300目时;停止研磨,包装。