CN103589316B - 一种多纤维聚氨酯树脂涂料 - Google Patents

一种多纤维聚氨酯树脂涂料 Download PDF

Info

Publication number
CN103589316B
CN103589316B CN201310506794.4A CN201310506794A CN103589316B CN 103589316 B CN103589316 B CN 103589316B CN 201310506794 A CN201310506794 A CN 201310506794A CN 103589316 B CN103589316 B CN 103589316B
Authority
CN
China
Prior art keywords
polyurethane resin
raw material
resin coating
multifilament polyurethane
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310506794.4A
Other languages
English (en)
Other versions
CN103589316A (zh
Inventor
吴文中
王旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PLATO COATED FABRICS Co Ltd
Original Assignee
ANHUI PLATO COATED FABRICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI PLATO COATED FABRICS Co Ltd filed Critical ANHUI PLATO COATED FABRICS Co Ltd
Priority to CN201310506794.4A priority Critical patent/CN103589316B/zh
Publication of CN103589316A publication Critical patent/CN103589316A/zh
Application granted granted Critical
Publication of CN103589316B publication Critical patent/CN103589316B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种多纤维聚氨酯树脂涂料，它是由下述重量份的原料组成的：P9335聚酯树脂56-60、异氰脲酸三缩水甘油酯5-10、聚四氟乙烯纤维4-6、衣康酸1-2、氨乙基哌嗪2-3、聚甲基苯基硅氧烷液体1-2、三乙烯四胺8-10、偶氮二甲酰胺1-2、玻璃纤维2-3、均苯四酸二酐0.3-0.4、安息香1-2、环烷酸铜2-3、复合填料16-24；本发明的涂料含有聚四氟乙烯纤维和玻璃纤维，极大的改善了涂料的韧性和强度，增强了对基材的保护效果，耐候性强。

Description

一种多纤维聚氨酯树脂涂料
技术领域
本发明主要涉及一种涂料，尤其涉及一种多纤维聚氨酯树脂涂料。
背景技术
物件暴露在大气之中，受到氧气、水分等的侵蚀，造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料，形成一层保护膜，能够阻止或延迟这些破坏现象的发生和发展，使各种材料的使用寿命延长，随着社会的发展，对于涂料质量的要求也越来越高，对于防腐、防水、防油、耐化学品、耐光、耐温等性能的追求也越来越高。
发明内容
本发明目的就是提供一种多纤维聚氨酯树脂涂料。
本发明是通过以下技术方案实现的：
一种多纤维聚氨酯树脂涂料，它是由下述重量份的原料组成的：
P9335聚酯树脂56-60、异氰脲酸三缩水甘油酯5-10、聚四氟乙烯纤维4-6、衣康酸1-2、氨乙基哌嗪2-3、聚甲基苯基硅氧烷液体1-2、三乙烯四胺8-10、偶氮二甲酰胺1-2、玻璃纤维2-3、均苯四酸二酐0.3-0.4、安息香1-2、环烷酸铜2-3、复合填料16-24；
所述的复合填料是由下述重量份的原料组成的：
黑沙5-7、温石棉10-16、玉石粉10-15、陶瓷粉3-5、烷醇酰胺2-3、辛基异噻唑啉酮1-2、2,6-二叔丁基对甲酚1-2；
将上述黑沙、玉石粉、温石棉混合，在500-600℃下煅烧2-3小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加10-15%的盐酸调节PH为4-5，加入陶瓷粉，在80-100℃下保温10-20分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过80-100目筛，即得所述复合填料。
一种多纤维聚氨酯树脂涂料的制备方法，包括以下步骤：
将上述各原料混合，加热至40-50℃，保温1-2小时，加热至熔融挤出，压片，风冷、磨粉，过60-100目筛，即得所述多纤维聚氨酯树脂涂料。
本发明的优点是：
本发明的涂料含有聚四氟乙烯纤维和玻璃纤维，极大的改善了涂料的韧性和强度，增强了对基材的保护效果，耐候性强。
具体实施方式
实施例1
一种多纤维聚氨酯树脂涂料，它是由下述重量份（公斤）的原料组成的：
P9335聚酯树脂60、异氰脲酸三缩水甘油酯10、聚四氟乙烯纤维6、衣康酸1、氨乙基哌嗪3、聚甲基苯基硅氧烷液体2、三乙烯四胺10、偶氮二甲酰胺2、玻璃纤维2-3、均苯四酸二酐0.4、安息香2、环烷酸铜2、复合填料24；
所述的复合填料是由下述重量份的原料组成的：
黑沙7、温石棉16、玉石粉15、陶瓷粉3、烷醇酰胺3、辛基异噻唑啉酮1、2,6-二叔丁基对甲酚1；
将上述黑沙、玉石粉、温石棉混合，在600℃下煅烧3小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加10-15%的盐酸调节PH为4-5，加入陶瓷粉，在80-100℃下保温10分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过100目筛，即得所述复合填料。
一种多纤维聚氨酯树脂涂料的制备方法，包括以下步骤：
将上述各原料混合，加热至40-50℃，保温1-2小时，加热至熔融挤出，压片，风冷、磨粉，过100目筛，即得所述多纤维聚氨酯树脂涂料。
性能测试：
抗冲击性：≥50kg/cm；
硬度：2H。

Claims (1)

1.一种多纤维聚氨酯树脂涂料，其特征在于它是由下述重量份的原料组成的：P9335聚酯树脂56-60、异氰脲酸三缩水甘油酯5-10、聚四氟乙烯纤维4-6、衣康酸1-2、氨乙基哌嗪2-3、聚甲基苯基硅氧烷液体1-2、三乙烯四胺8-10、偶氮二甲酰胺1-2、玻璃纤维2-3、均苯四酸二酐0.3-0.4、安息香1-2、环烷酸铜2-3、复合填料16-24；所述的复合填料是由下述重量份的原料组成的：黑沙5-7、温石棉10-16、玉石粉10-15、陶瓷粉3-5、烷醇酰胺2-3、辛基异噻唑啉酮1-2、2,6-二叔丁基对甲酚1-2；将上述黑沙、玉石粉、温石棉混合，在500-600℃下煅烧2-3小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加10-15%的盐酸调节PH为4-5，加入陶瓷粉，在80-100℃下保温10-20分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过80-100目筛，即得所述复合填料；
所述的多纤维聚氨酯树脂涂料的制备方法包括以下步骤：将上述各原料混合，加热至40-50℃，保温1-2小时，加热至熔融状态，挤出，压片，风冷、磨粉，过60-100目筛，即得所述多纤维聚氨酯树脂涂料。
CN201310506794.4A 2013-10-24 2013-10-24 一种多纤维聚氨酯树脂涂料 Active CN103589316B (zh)