CN103603205B - 一种体操垫面料用涂料 - Google Patents

一种体操垫面料用涂料 Download PDF

Info

Publication number
CN103603205B
CN103603205B CN201310506874.XA CN201310506874A CN103603205B CN 103603205 B CN103603205 B CN 103603205B CN 201310506874 A CN201310506874 A CN 201310506874A CN 103603205 B CN103603205 B CN 103603205B
Authority
CN
China
Prior art keywords
powder
raw material
mat fabric
add
fabric coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310506874.XA
Other languages
English (en)
Other versions
CN103603205A (zh
Inventor
吴文中
王旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PLATO COATED FABRICS Co Ltd
Original Assignee
ANHUI PLATO COATED FABRICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI PLATO COATED FABRICS Co Ltd filed Critical ANHUI PLATO COATED FABRICS Co Ltd
Priority to CN201310506874.XA priority Critical patent/CN103603205B/zh
Publication of CN103603205A publication Critical patent/CN103603205A/zh
Application granted granted Critical
Publication of CN103603205B publication Critical patent/CN103603205B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种体操垫面料用涂料，它是由下述重量份的原料组成的：双酚A环氧树脂70-80、四甲基乙二胺10-15、丙二醇苯醚1-2、单硬脂酸甘油单酯10-13、竹炭粉4-5、缬草油1-2、硅酸三钙1.5-2、聚溴化苯乙烯2-3、马来酸酐0.7-1、硅酸铝纤维3-5、天青石粉12-20、复合填料10-14；本发明的涂料消光性好，无折白现象，价格低廉，特别适用于体操垫面料用，抗压性、抗冲击性强。

Description

一种体操垫面料用涂料
技术领域
本发明主要涉及一种涂料，尤其涉及一种体操垫面料用涂料。
背景技术
物件暴露在大气之中，受到氧气、水分等的侵蚀，造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料，形成一层保护膜，能够阻止或延迟这些破坏现象的发生和发展，使各种材料的使用寿命延长，随着社会的发展，对于涂料质量的要求也越来越高，对于防腐、防水、防油、耐化学品、耐光、耐温等性能的追求也越来越高。
发明内容
本发明目的就是提供一种体操垫面料用涂料。
本发明是通过以下技术方案实现的：
一种体操垫面料用涂料，它是由下述重量份的原料组成的：
双酚A环氧树脂70-80、四甲基乙二胺10-15、丙二醇苯醚1-2、单硬脂酸甘油单酯10-13、竹炭粉4-5、缬草油1-2、硅酸三钙1.5-2、聚溴化苯乙烯2-3、马来酸酐0.7-1、硅酸铝纤维3-5、天青石粉12-20、复合填料10-14；
所述的复合填料是由下述重量份的原料组成的：
黑沙5-7、温石棉10-16、玉石粉10-15、陶瓷粉3-5、烷醇酰胺2-3、辛基异噻唑啉酮1-2、2,6-二叔丁基对甲酚1-2；
将上述黑沙、玉石粉、温石棉混合，在500-600℃下煅烧2-3小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加10-15％的盐酸调节pH为4-5，加入陶瓷粉，在80-100℃下保温10-20分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过80-100目筛，即得所述复合填料。
一种体操垫面料用涂料的制备方法，包括以下步骤：
将上述竹炭粉、硅酸三钙与单硬脂酸甘油单酯混合，在90-120℃下保温搅拌10-14分钟，加入缬草油、天青石粉，球磨均匀，再加入剩余各原料，熔融挤出，压片，风冷、磨粉，过60-100目筛，即得所述体操垫面料用涂料。
本发明的优点是：
本发明的涂料消光性好，无折白现象，价格低廉，特别适用于体操垫面料用，抗压性、抗冲击性强。
具体实施方式
实施例1
一种体操垫面料用涂料，它是由下述重量份(公斤)的原料组成的：
双酚A环氧树脂80、四甲基乙二胺15、丙二醇苯醚2、单硬脂酸甘油单酯13、竹炭粉5、缬草油1-2、硅酸三钙1.5、聚溴化苯乙烯3、马来酸酐0.7、硅酸铝纤维5、天青石粉20、复合填料14；
所述的复合填料是由下述重量份的原料组成的：
黑沙5、温石棉16、玉石粉15、陶瓷粉5、烷醇酰胺2、辛基异噻唑啉酮2、2,6-二叔丁基对甲酚1；
将上述黑沙、玉石粉、温石棉混合，在600℃下煅烧2小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加15％的盐酸调节pH为5，加入陶瓷粉，在100℃下保温20分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过100目筛，即得所述复合填料。
一种体操垫面料用涂料的制备方法，包括以下步骤：
将上述竹炭粉、硅酸三钙与单硬脂酸甘油单酯混合，在120℃下保温搅拌10分钟，加入缬草油、天青石粉，球磨均匀，再加入剩余各原料，熔融挤出，压片，风冷、磨粉，过100目筛，即得所述体操垫面料用涂料。
性能测试：
抗冲击性：≥50kg/cm；
硬度：2H。

Claims (2)

1.一种体操垫面料用涂料，其特征在于它是由下述重量份的原料组成的：双酚A环氧树脂70-80、四甲基乙二胺10-15、丙二醇苯醚1-2、单硬脂酸甘油单酯10-13、竹炭粉4-5、缬草油1-2、硅酸三钙1.5-2、聚溴化苯乙烯2-3、马来酸酐0.7-1、硅酸铝纤维3-5、天青石粉12-20、复合填料10-14；所述的复合填料是由下述重量份的原料组成的：黑沙5-7、温石棉10-16、玉石粉10-15、陶瓷粉3-5、烷醇酰胺2-3、辛基异噻唑啉酮1-2、2,6-二叔丁基对甲酚1-2；将上述黑沙、玉石粉、温石棉混合，在500-600℃下煅烧2-3小时，出料冷却后加入辛基异噻唑啉酮，再加适量水充分研磨，加10-15%的盐酸调节pH为4-5，加入陶瓷粉，在80-100℃下保温10-20分钟，研磨，再加氢氧化钠调节为中性，喷雾干燥，得粉末，与剩余各原料混合，充分研磨，过80-100目筛，即得所述复合填料。
2.一种如权利要求1所述的体操垫面料用涂料的制备方法，其特征在于包括以下步骤：将上述竹炭粉、硅酸三钙与单硬脂酸甘油单酯混合，在90-120℃下保温搅拌10-14分钟，加入缬草油、天青石粉，球磨均匀，再加入剩余各原料，熔融挤出，压片，风冷、磨粉，过60-100目筛，即得所述体操垫面料用涂料。
CN201310506874.XA 2013-10-24 2013-10-24 一种体操垫面料用涂料 Active CN103603205B (zh)