CN103173094A - 一种含二甲基亚砜的防腐涂料 - Google Patents
一种含二甲基亚砜的防腐涂料 Download PDFInfo
- Publication number
- CN103173094A CN103173094A CN2013100606515A CN201310060651A CN103173094A CN 103173094 A CN103173094 A CN 103173094A CN 2013100606515 A CN2013100606515 A CN 2013100606515A CN 201310060651 A CN201310060651 A CN 201310060651A CN 103173094 A CN103173094 A CN 103173094A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- mentioned
- raw material
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含二甲基亚砜的防腐涂料，它是由甲乙两组份组成，所述的甲组份是由下述重量份的原料组成：环氧树脂E4484-90、高氯化聚乙烯树脂10-15、沉淀硫酸钡10-15、四氟化钛1-2、单氟磷酸钠2-4、二甲基亚砜2-4、乙二醇单丁醚2-3、丙烯酸乙酯2-4、尿素3-5、聚丙烯酰胺2-3、二乙胺2-3、二苯基甲烷二异氰酸酯2-3、邻苯二甲酸二异辛酯3-5、乙二胺四亚甲基叉膦酸钠1-2、水滑石5-7、二甲基乙醇胺1-2、复合改性剂15-20、二甲苯25-30、醋酸正丁酯10-15、硫代二丙酸二月桂酯0.8-1、乙烯基三乙氧基硅烷0.8-1、甲基硅油0.5-1；本发明生产的漆膜对金属附着力好，结构气孔小，结构致密，具有优良的附着力，柔韧性好、抗冲击强度高、耐腐蚀性能强，对基体金属起到高效的保护作用。
Description
技术领域
本发明主要涉及一种涂料，尤其涉及一种含二甲基亚砜的防腐涂料。
背景技术
随着工业技术进步，金属材料的使用越来越广泛，金属及其构件的腐蚀问题已遍及国民经济的各个领域，给人类社会造成了巨大损失。为了减少腐蚀的损失，人们采取了很多防护措施，但迄今为止最普遍、最经济、最实用的保护措施还是涂料保护，在各种防腐技术中，涂料的防腐技术应用最广泛。涂料防腐以其施工简便、经济适用、不受设备面积、形状的约束等特点而被广泛的应用；
在众多涂料品种中环氧树脂在防腐涂料中占据重要地位，是被广泛作为金属防腐用的一种涂层材料，具有优异的粘结力、耐化学药品、防腐蚀和耐水性能，其产量日增，新品种相继出现，是极有发展前途的涂料品种，通过添加不同的填料和调整固化剂的品种，可以制成性能各异的环氧树脂防腐涂料，适用于不同场合的防腐需要，达到良好的保护效果。
但目前金属用防腐涂料技术存在防腐期限短、耐冲刷性差、漆膜不稳定、环境污染等问题限制了其快速发展，为了提高环氧系涂料的性能，对其进行改性具有重要的科学意义和商业价值。
发明内容
本发明目的就是提供一种含二甲基亚砜的防腐涂料。
本发明是通过以下技术方案实现的：
一种含二甲基亚砜的防腐涂料，它是由甲乙两组份组成，所述的甲组份是由下述重量份的原料组成：
环氧树脂E44 84-90、高氯化聚乙烯树脂10-15、沉淀硫酸钡10-15、四氟化钛1-2、单氟磷酸钠2-4、二甲基亚砜2-4、乙二醇单丁醚2-3、丙烯酸乙酯2-4、尿素3-5、聚丙烯酰胺2-3、二乙胺2-3、二苯基甲烷二异氰酸酯2-3、邻苯二甲酸二异辛酯3-5、乙二胺四亚甲基叉膦酸钠1-2、水滑石5-7、二甲基乙醇胺1-2、复合改性剂15-20、二甲苯25-30、醋酸正丁酯10-15、硫代二丙酸二月桂酯0.8-1、乙烯基三乙氧基硅烷0.8-1、甲基硅油0.5-1；
所述的复合改性剂是由下述重量份的原料组成的：
35-45波美度水玻璃40-50、硫酸铝90-100、纳米二氧化硅颗粒35-45、失水山梨醇单油酸酯1-2、聚氧乙烯醚1-2、羧甲基纤维素钠1-2、十二烷基苯磺酸钠2-4、过氧化二异丙苯1-2、N- 苯基-3- 氨基丙基三甲氧基硅烷0.8-1、乙烯基三乙氧基硅烷0.6-1、盐酸、水适量；
所述的复合改性剂的制备方法包括以下步骤：
（1）在上述重量份的35-45波美度水玻璃中逐滴加入浓度为8-10%的盐酸溶液，不断的测定混合液的PH，当PH为4.5-5时，停止加入，备用；
（2）将上述重量份的羧甲基纤维素钠和十二烷基苯磺酸钠混合溶于15-20倍水中，得料B；
（3）在上述重量份的硫酸铝中加入适量水，在搅拌条件下缓慢加入上述酸化后的35-45波美度水玻璃溶液，期间不断滴加上述料B，体系的反应温度为75-85℃，上述酸化后的35-45波美度水玻璃溶液滴加完毕后继续搅拌3-5分钟，反应结束；
（4）将反应结束后的混合液在85-95℃下陈化2-3小时；
（5）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与上述陈化后的混料混合，加入剩余各原料，高速1500-2000转/分离心搅拌20-30分钟，烘干脱水，粉碎成超细粉末，即为所述复合改性剂；
所述的甲组份的制备方法为：
（1）将上述重量份的环氧树脂E44、高氯化聚乙烯树脂、二甲苯与醋酸正丁酯混合搅拌均匀；
（2）再加入剩余各原料充分分散均匀，然后进行研磨至细度达50-60μm，即得所述甲组份；
所述的乙组份是由下述重量份的原料组成：
间苯二甲胺90-98、二甲苯10-16、醋酸乙酯6-10；
所述的乙组份的制备方法为：
将上述重量份的各原料混合加入分散罐中，开动高搅，分散均匀，过滤，即得所述乙组份；
将上述得到的甲乙两组份按照6-10：1重量比混合，搅拌30-40分钟至均匀，即可涂覆或喷涂在经除油、除锈处理的金属表面。
本发明的优点是：
本发明生产的漆膜对金属附着力好，结构气孔小，结构致密，具有优良的附着力，柔韧性好、抗冲击强度高、耐腐蚀性能强，对基体金属起到高效的保护作用，加入的复合改性剂进一步提高了漆膜的表面光泽度和物理机械性能，使得漆膜具有更好的耐擦洗性、耐候性，增强了漆膜的品质。
具体实施方式
实施例1
一种含二甲基亚砜的防腐涂料，它是由甲乙两组份组成，所述的甲组份是由下述重量份(公斤)的原料组成：
环氧树脂E44 90、高氯化聚乙烯树脂（氯65M）15、沉淀硫酸钡15、四氟化钛2、单氟磷酸钠4、二甲基亚砜4、乙二醇单丁醚3、丙烯酸乙酯4、尿素5、聚丙烯酰胺3、二乙胺3、二苯基甲烷二异氰酸酯3、邻苯二甲酸二异辛酯5、乙二胺四亚甲基叉膦酸钠2、水滑石7、二甲基乙醇胺2、复合改性剂20、二甲苯30、醋酸正丁酯15、硫代二丙酸二月桂酯0.8、乙烯基三乙氧基硅烷0.8、甲基硅油0.5；
所述的复合改性剂是由下述重量份的原料组成的：
35-45波美度水玻璃50、硫酸铝100、纳米二氧化硅颗粒45、失水山梨醇单油酸酯2、聚氧乙烯醚2、羧甲基纤维素钠1、十二烷基苯磺酸钠4、过氧化二异丙苯2、N- 苯基-3- 氨基丙基三甲氧基硅烷0.8、乙烯基三乙氧基硅烷1、盐酸、水适量；
所述的复合改性剂的制备方法包括以下步骤：
（1）在上述重量份的35-45波美度水玻璃中逐滴加入浓度为10%的盐酸溶液，不断的测定混合液的PH，当PH为4.5时，停止加入，备用；
（2）将上述重量份的羧甲基纤维素钠和十二烷基苯磺酸钠混合溶于20倍水中，得料B；
（3）在上述重量份的硫酸铝中加入适量水，在搅拌条件下缓慢加入上述酸化后的35-45波美度水玻璃溶液，期间不断滴加上述料B，使体系的PH在10之间，体系的反应温度为85℃，上述酸化后的35-45波美度水玻璃溶液滴加完毕后继续搅拌5分钟，反应结束；
（4）将反应结束后的混合液在95℃下陈化3小时；
（5）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与上述陈化后的混料混合，加入剩余各原料，高速2000转/分离心搅拌30分钟，烘干脱水，粉碎成超细粉末，即为所述复合改性剂；
所述的甲组份的制备方法为：
（1）将上述重量份的环氧树脂E44、高氯化聚乙烯树脂、二甲苯与醋酸正丁酯混合搅拌均匀；
（2）再加入剩余各原料充分分散均匀，然后进行研磨至细度达60μm，即得所述甲组份；
所述的乙组份是由下述重量份的原料组成：
间苯二甲胺98、二甲苯16、醋酸乙酯6；
所述的乙组份的制备方法为：
将上述重量份的各原料混合加入分散罐中，开动高搅，分散均匀，过滤，即得所述乙组份；
将上述得到的甲乙两组份按照10：1重量比混合，搅拌40分钟至均匀，即可涂覆或喷涂在经除油、除锈处理的金属表面。
性能测试：
100天划痕盐雾实验，漆膜无起泡、无脱落、划痕处锈蚀扩散0.9mm；
100天盐雾实验，漆膜无起泡、无脱落、无锈蚀；
耐酸性（5%的硫酸溶液、25℃、50h）：漆膜无起泡、无脱落、无锈蚀；
耐碱性（5%的氢氧化钠溶液、25℃、600h）：漆膜无起泡、无脱落、无锈蚀；
耐盐水性（5%的氯化钠溶液、25℃、800h）：漆膜无起泡、无脱落、无锈蚀；
柔韧性1mm；
附着力13Mpa。
Claims (1)
1.一种含二甲基亚砜的防腐涂料，其特征在于它是由甲乙两组份组成，所述的甲组份是由下述重量份的原料组成：
环氧树脂E44 84-90、高氯化聚乙烯树脂10-15、沉淀硫酸钡10-15、四氟化钛1-2、单氟磷酸钠2-4、二甲基亚砜2-4、乙二醇单丁醚2-3、丙烯酸乙酯2-4、尿素3-5、聚丙烯酰胺2-3、二乙胺2-3、二苯基甲烷二异氰酸酯2-3、邻苯二甲酸二异辛酯3-5、乙二胺四亚甲基叉膦酸钠1-2、水滑石5-7、二甲基乙醇胺1-2、复合改性剂15-20、二甲苯25-30、醋酸正丁酯10-15、硫代二丙酸二月桂酯0.8-1、乙烯基三乙氧基硅烷0.8-1、甲基硅油0.5-1；
所述的复合改性剂是由下述重量份的原料组成的：
35-45波美度水玻璃40-50、硫酸铝90-100、纳米二氧化硅颗粒35-45、失水山梨醇单油酸酯1-2、聚氧乙烯醚1-2、羧甲基纤维素钠1-2、十二烷基苯磺酸钠2-4、过氧化二异丙苯1-2、N- 苯基-3- 氨基丙基三甲氧基硅烷0.8-1、乙烯基三乙氧基硅烷0.6-1、盐酸、水适量；
所述的复合改性剂的制备方法包括以下步骤：
（1）在上述重量份的35-45波美度水玻璃中逐滴加入浓度为8-10%的盐酸溶液，不断的测定混合液的PH，当PH为4.5-5时，停止加入，备用；
（2）将上述重量份的羧甲基纤维素钠和十二烷基苯磺酸钠混合溶于15-20倍水中，得料B；
（3）在上述重量份的硫酸铝中加入适量水，在搅拌条件下缓慢加入上述酸化后的35-45波美度水玻璃溶液，期间不断滴加上述料B，体系的反应温度为75-85℃，上述酸化后的35-45波美度水玻璃溶液滴加完毕后继续搅拌3-5分钟，反应结束；
（4）将反应结束后的混合液在85-95℃下陈化2-3小时；
（5）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与上述陈化后的混料混合，加入剩余各原料，高速1500-2000转/分离心搅拌20-30分钟，烘干脱水，粉碎成超细粉末，即为所述复合改性剂；
所述的甲组份的制备方法为：
（1）将上述重量份的环氧树脂E44、高氯化聚乙烯树脂、二甲苯与醋酸正丁酯混合搅拌均匀；
（2）再加入剩余各原料充分分散均匀，然后进行研磨至细度达50-60μm，即得所述甲组份；
所述的乙组份是由下述重量份的原料组成：
间苯二甲胺90-98、二甲苯10-16、醋酸乙酯6-10；
所述的乙组份的制备方法为：
将上述重量份的各原料混合加入分散罐中，开动高搅，分散均匀，过滤，即得所述乙组份；
将上述得到的甲乙两组份按照7-10：1重量比混合，搅拌30-40分钟至均匀，即可涂覆或喷涂在经除油、除锈处理的金属表面。