CN104194093B - 一种耐油橡胶 - Google Patents

一种耐油橡胶 Download PDF

Info

Publication number
CN104194093B
CN104194093B CN201410480133.3A CN201410480133A CN104194093B CN 104194093 B CN104194093 B CN 104194093B CN 201410480133 A CN201410480133 A CN 201410480133A CN 104194093 B CN104194093 B CN 104194093B
Authority
CN
China
Prior art keywords
oil
agent
resisting rubber
parts
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410480133.3A
Other languages
English (en)
Other versions
CN104194093A (zh
Inventor
张勇
梁高勇
秦蕾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Haida Rubber and Plastic Co Ltd
Original Assignee
Jiangyin Haida Rubber and Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Haida Rubber and Plastic Co Ltd filed Critical Jiangyin Haida Rubber and Plastic Co Ltd
Priority to CN201410480133.3A priority Critical patent/CN104194093B/zh
Publication of CN104194093A publication Critical patent/CN104194093A/zh
Application granted granted Critical
Publication of CN104194093B publication Critical patent/CN104194093B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐油橡胶，由下列重量份的原料制成：丁腈橡胶100-200份、偶联剂10-30份、增塑剂20-40份、硫化促进剂30-50份、防老剂15-35份、氧化锌10-20份、补强剂10-30份和耐油助剂15-35份。本发明提供一种配方科学，材料易得，具有优异的耐油性能和力学性能，并且加工性能好的耐油橡胶。同时在生产过程中，不会产生粘辊、粘膜的现象，易加工，大大提高了其加工性能。

Description

一种耐油橡胶
技术领域
本发明涉及橡胶领域，具体的说，本发明涉及一种耐油橡胶。
背景技术
这些年随着经济的发展，在石油勘探中对于橡胶产品的需求越来越旺盛，然而由于石油勘探的特殊性，其使用过程中不可避免地接触油性物质，如果橡胶产品的耐油性不足，则操作者容易出现打滑等现象，危及生产、甚至操作者的人身安全。
发明内容
本发明的目的在于提供一种耐油橡胶。
为了实现本发明的目的，本发明提供一种耐油橡胶，由下列重量份的原料制成：丁腈橡胶100-200份、偶联剂10-30份、增塑剂20-40份、硫化促进剂30-50份、防老剂15-35份、氧化锌10-20份、补强剂10-30份和耐油助剂15-35份。
优选地，本发明所述的耐油橡胶由下列重量份的原料制成：丁腈橡胶150份、偶联剂20份、增塑剂30份、硫化促进剂35份、防老剂20份、氧化锌15份、补强剂25份和耐油助剂30份。
更优选地，所述偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷。
更优选地，所述增塑剂为磷酸三苯酯。
更优选地，所述硫化促进剂为2-硫醇基苯并噻唑。
更优选地，所述防老剂为N，N’-二甲苯基对苯二胺。
更优选地，所述补强剂为炭黑。
更优选地，所述耐油助剂为1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐。
本发明还提供1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐在用作耐油助剂中的用途。
本发明提供一种配方科学，材料易得，具有优异的耐油性能和力学性能，并且加工性能好的耐油橡胶。同时在生产过程中，不会产生粘辊、粘膜的现象，易加工，大大提高了其加工性能。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1
称取丁腈橡胶1500克、γ-甲基丙烯酰氧基丙基三甲氧基硅烷200克、磷酸三苯酯300克、2-硫醇基苯并噻唑350克、N，N’-二甲苯基对苯二胺200克、氧化锌150克、炭黑250克和1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐300克；
采用GB-10型高速混合机，将高速混合机预热至95℃，将丁腈橡胶、2-硫醇基苯并噻唑、氧化锌和炭黑倒入高速混合机中，在400rpm下搅拌1.5分钟，然后在950rpm下搅拌30分钟，停机敞开盖1分钟，然后加入γ-甲基丙烯酰氧基丙基三甲氧基硅烷、磷酸三苯酯、N，N’-二甲苯基对苯二胺和1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐，在1200rpm下搅拌20分钟，出料到SK-160型双辊筒炼塑机中，加入两辊开炼机上进行混炼，开炼机前辊165℃，后辊155℃，塑炼20分钟，然后下片；将拉出的片放入QLB-D400X400X2型平板硫化机中压制片材，平板硫化机模板温度为165℃，模压力为1Mpa，模压时间20分钟。
实施例2
按照和实施例1相同的方式制备耐油橡胶，不同之处在于不使用1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐。
实验例
性能测试
(1)力学性能：拉伸强度、撕裂强度、邵尔A型硬度测试分别按相应国家标准(GB/T528-1998、GB/T529-1999、GB/T531-1999)测定。
(2)耐油性能按照ASTMD471-2006标准进行检测，单位为％。
结果
实施例1的样品：硬度(邵A)为96，拉伸强度为11.6Mpa，撕裂强度为46.8Mpa，耐油性能(油浸泡后的膨胀率)为6.7％。
实施例2的样品：硬度(邵A)为91，拉伸强度为10.7Mpa，撕裂强度为44.6Mpa，耐油性能(油浸泡后的膨胀率)为9.3％。
由上述结果可见，在加入耐油助剂之后，油浸泡后的膨胀率更低，说明耐油性更好。实施例1的样品和实施例2的样品的耐油性能结果进行比较，差异具有统计学意义(P＜0.01)。

Claims (8)

1.一种耐油橡胶，其特征在于，由下列重量份的原料制成：丁腈橡胶100-200份、偶联剂10-30份、增塑剂20-40份、硫化促进剂30-50份、防老剂15-35份、氧化锌10-20份、补强剂10-30份和耐油助剂15-35份，所述耐油助剂为1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐。
2.根据权利要求1所述的耐油橡胶，其特征在于，由下列重量份的原料制成：丁腈橡胶150份、偶联剂20份、增塑剂30份、硫化促进剂35份、防老剂20份、氧化锌15份、补强剂25份和耐油助剂30份。
3.根据权利要求2所述的耐油橡胶，其特征在于，所述偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷。
4.根据权利要求2所述的耐油橡胶，其特征在于，所述增塑剂为磷酸三苯酯。
5.根据权利要求2所述的耐油橡胶，其特征在于，所述硫化促进剂为2-硫醇基苯并噻唑。
6.根据权利要求2所述的耐油橡胶，其特征在于，所述防老剂为N，N’-二甲苯基对苯二胺。
7.根据权利要求2所述的耐油橡胶，其特征在于，所述补强剂为炭黑。
8.1-环丙基-4-[(4-吗啉基)甲基]-2-[(2，6-二氯苯基)硫甲基]-5-羟基-6-溴-1H-吲哚-3-羧酸乙酯盐酸盐在用作耐油助剂中的用途。
CN201410480133.3A 2014-09-18 2014-09-18 一种耐油橡胶 Expired - Fee Related CN104194093B (zh)