CN104151798B - 一种pet爽滑开口母粒及其制备方法 - Google Patents

一种pet爽滑开口母粒及其制备方法 Download PDF

Info

Publication number
CN104151798B
CN104151798B CN201410409621.5A CN201410409621A CN104151798B CN 104151798 B CN104151798 B CN 104151798B CN 201410409621 A CN201410409621 A CN 201410409621A CN 104151798 B CN104151798 B CN 104151798B
Authority
CN
China
Prior art keywords
pet
opening
master batch
agent
smooth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410409621.5A
Other languages
English (en)
Other versions
CN104151798A (zh
Inventor
覃碧勋
李卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN CITY PUCA PLASTIC TECHNOLOGY Co Ltd
Original Assignee
DONGGUAN CITY PUCA PLASTIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN CITY PUCA PLASTIC TECHNOLOGY Co Ltd filed Critical DONGGUAN CITY PUCA PLASTIC TECHNOLOGY Co Ltd
Priority to CN201410409621.5A priority Critical patent/CN104151798B/zh
Publication of CN104151798A publication Critical patent/CN104151798A/zh
Application granted granted Critical
Publication of CN104151798B publication Critical patent/CN104151798B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及塑料技术领域，特别是涉及一种PET爽滑开口母粒及其制备方法；包括按照重量百分比计算的爽滑剂5％～30％、开口剂10％～40％和载体30％～85％；本发明所述的PET爽滑开口母粒在PET塑料中使用，不仅提升了PET制品的爽滑性、开口性，并能保持很好的透明度；而且本发明制备方法简单，降低了制造成本。

Description

一种PET爽滑开口母粒及其制备方法
技术领域
本发明涉及塑料技术领域，特别是涉及一种PET爽滑开口母粒及其制备方法。
背景技术
PET即聚对苯二甲酸乙二醋是一种线型聚醋，表面平滑而有光泽。耐蠕变、抗疲劳性、耐摩擦性好，磨耗小而硬度高，具有热塑性塑料中最大的韧性；电绝缘性能好，受温度影响小，常用于纤维、挤出薄膜和薄片、吹塑等。由它制造的聚酷薄膜或薄片具有较好的韧性、力学强度和优良的透明性，但滑爽性比较差，给使用带来不便。所以在日常聚醋薄膜或薄片生产中须加入爽滑剂来进行解决。一般爽滑剂加入都通过事先制成爽滑色母粒的方法来加入，因为爽滑剂一般熔点都很低，直接加入聚醋薄膜或薄片中易使螺杆打滑而影响产品质量。
现有技术的PET爽滑母粒，由于其中的爽滑剂分子量低、熔点低、易挥发等缺点，容易产生挤出过程难以控制，产品质量不稳定；现有技术的PET开口母粒，开口剂一般选用沉淀二氧化硅，或者气相二氧化硅(白炭黑)，虽然开口效果不错，但由于二氧化硅的折光指数与PET折光指数相差较大，在其开口效果起效之前的添加量就已明显影响PET塑料产品的透明度，大大限制了它在PET透明片材和薄膜中的应用。
发明内容
为了解决上述问题，本发明的目的在于，提供一种PET爽滑开口母粒。
本发明的目的之二是提供所述PET爽滑开口母粒的制备方法，该方法简单，降低了制造成本。
本发明的目的之三是提供一种不仅爽滑性、开口性都很好，而且并能保持高透明度的爽滑PET塑料。
本发明是通过以下技术方案来实现的：
一种PET爽滑开口母粒，包括按照重量百分比计算的以下物质：
爽滑剂5％～30％
开口剂10％～40％
载体30％～85％；
所述爽滑剂为蒙旦蜡、聚酯蜡、聚酰胺蜡、多元醇脂肪酸酯中的一种或多种的混合物，所述开口剂为开口剂为折光指数1.55～1.65的无机粉体，优选云母、滑石粉、高岭土、硅藻土中的一种或多种的混合物；所述载体为PET和/或PETG。
制备所述PET爽滑开口母粒的方法，包括如下制备步骤：
先将所述量的爽滑剂、开口剂和载体在50℃下经混合1～5分钟，再将混合好的物料通过双螺杆挤出机熔融共混，挤出造粒，冷却、干燥制得所述PET爽滑开口母粒。
较佳地，所述挤出机各温度区设置为第一区50℃～100℃，第二区100℃～230℃，第三区230℃～260℃，其它各区200℃～250℃。
一种PET塑料，包括所述PET爽滑开口母粒。
本发明包括由蒙旦蜡、聚酯蜡、聚酰胺蜡、多元醇脂肪酸酯构成的爽滑剂，由云母、滑石粉、高岭土、硅藻土构成的开口剂和载体(PET和/或PETG)。其中载体PET和/或PETG，本身与聚酯化学结构相同，相容性好，不影响透明度，且PETG熔点较低，起到降低母粒熔融挤出温度的作用。爽滑剂在高温下不挥发不变色，与PET有适宜的相容性，其爽滑效果起效时间快、维持时间长。
其中，开口剂的折光指数在1.60左右，与PET的折光指数1.58非常接近，在较高用量下也不会影响PET片材或薄膜的透明度；如果选用二氧化硅，因二氧化硅折光率为1.42，与PET的折光指数偏差较大，故二氧化硅的微小添加量就会引起了PET片材或薄膜透明度下降。另一方面，本发明所用的开口剂是无机粉体，既可起开口作用，又可在挤出加工过程中吸收已熔化的爽滑剂，确保挤出造粒顺利进行。
本发明所述的PET爽滑开口母粒在PET塑料中使用，不仅提升了PET制品的爽滑性、开口性，并能保持很好的透明度；而已本发明制备方法简单，降低了制造成本。
具体的实施方式
下面结合具体实施方式对本发明作进一步的详细说明，以助于本领域技术人员理解本发明。
实施例1
一种PET爽滑开口母粒，包括按照重量百分比计算的爽滑剂(蒙旦蜡)5％、开口剂(高岭土)10％和载体(PETG)85％。
制备方法：先将所述量的爽滑剂、开口剂和载体在50℃下经混合1～5分钟，再将混合好的物料通过双螺杆挤出机熔融共混，挤出造粒，冷却、干燥制得所述PET爽滑开口母粒。其中，挤出机各温度区设置为第一区50℃～100℃，第二区100℃～230℃，第三区230℃～260℃，其它各区200℃～250℃。
实施例2
一种PET爽滑开口母粒，包括按照重量百分比计算的爽滑剂(聚酰胺蜡)30％、开口剂(滑石粉)40％和载体(PET)30％。
制备方法：同具体实施例1。
实施例3
一种PET爽滑开口母粒，包括按照重量百分比计算的爽滑剂(多元醇脂肪酸酯)10％、开口剂(云母)30％和载体(PETG)70％。
制备方法：同具体实施例1。
实施例4
一种PET爽滑开口母粒，包括按照重量百分比计算的爽滑剂(多元醇脂肪酸酯)20％、开口剂(硅藻土)20％和载体(PET)60％。
制备方法：同具体实施例1。
实施例5
一种PET爽滑开口母粒，包括按照重量百分比计算的爽滑剂(蒙旦蜡2％、聚酯蜡2％、聚酰胺蜡6％和多元醇脂肪酸酯15％)25％、开口剂(云母5％、滑石粉5％和高岭土15％)25％和载体(PET10％和PETG40％)50％。
制备方法：同具体实施例1。
上述实施例，只是本发明的较佳实施例，并非用来限制本发明实施范围，故凡以本发明权利要求所述的特征及原理所做的等效变化或修饰，均应包括在本发明权利要求范围之内。
对比例1将开口剂改为沉淀二氧化硅；对比例2将开口剂改为白炭黑。
具体对比结果如下表：
实施例1 实施例2 实施例3 实施例4 实施例5 对比例1 对比例2
爽滑性 佳 佳 佳 佳 佳 一般 一般
开口性 佳 佳 佳 佳 佳 一般 一般
透明性 好 好 好 好 好 差 差

Claims (5)

1.一种PET爽滑开口母粒，其特征在于，包括按照重量百分比计算的以下物质：
爽滑剂5％～30％
开口剂10％～40％
载体30％～85％；
所述爽滑剂为蒙旦蜡、聚酯蜡、聚酰胺蜡、多元醇脂肪酸酯中的一种或多种的混合物；
所述开口剂为折光指数是1.55～1.65的无机粉体，所述载体为PET和/或PETG。
2.根据权利要求1所述的PET爽滑开口母粒，其特征在于，所述开口剂为云母、滑石粉、高岭土、硅藻土中的一种或多种的混合物。
3.制备权利要求1或2所述PET爽滑开口母粒的方法，其特征在于，具体为：先将所述量的爽滑剂、开口剂和载体在50℃下混合1～5分钟，再将混合好的物料通过双螺杆挤出机熔融共混，挤出造粒，冷却、干燥制得所述PET爽滑开口母粒。
4.权利要求3所述PET爽滑开口母粒的制备方法，其特征在于，所述挤出机各温度区设置为第一区50℃～100℃，第二区100℃～230℃，第三区230℃～260℃，其它各区200℃～250℃。
5.一种PET塑料，其特征在于，包括权利要求1-4中任意一项所述PET爽滑开口母粒。
CN201410409621.5A 2014-08-19 2014-08-19 一种pet爽滑开口母粒及其制备方法 Active CN104151798B (zh)