CN104099634A - 氮化钒的制备方法 - Google Patents
氮化钒的制备方法 Download PDFInfo
- Publication number
- CN104099634A CN104099634A CN201410385472.3A CN201410385472A CN104099634A CN 104099634 A CN104099634 A CN 104099634A CN 201410385472 A CN201410385472 A CN 201410385472A CN 104099634 A CN104099634 A CN 104099634A
- Authority
- CN
- China
- Prior art keywords
- vanadium
- vanadium nitride
- nitrogen
- preparation
- electrolysis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及氮化钒的制备方法,属于有色金属冶炼技术领域。本发明解决的技术问题是提供氮化钒的制备方法。该方法将钒氧化物和碳质还原剂混合作为阳极,碳钢棒为阴极,在含低价氯化钒的碱金属/碱土金属氯化物熔盐体系中实施电解,并在阴极下方通入氮气,阴极析出的钒金属与氮气反应生成氮化钒。本发明氮化钒的制备方法,通过电解方法获得氮化钒,可有效降低氮化制备的温度,降低生产成本,同时由于电解的精炼及保护作用使得其产品质量较好,氧和碳等杂质元素含量较低,此外,还能通过控制电流密度等参数调节产品粒径,其产品粒径可控,适合做粉末冶金添加剂,具备较强应用前景。
Description
技术领域
本发明涉及氮化钒的制备方法,属于有色金属冶炼技术领域。
背景技术
氮化钒是一种新型合金添加剂,可以替代钒铁用于微合金化钢的生产。氮化钒添加于钢中能提高钢的强度、韧性、延展性及抗热疲劳性等综合机械性能,并使钢具有良好的可焊性。在达到相同强度下,添加氮化钒节约钒加入量30-40%,进而降低了成本。由于钢强度提高后,可有效节约钢材用量,即节约了原料和冶炼成本,收到资源节约和环境保护的双重效益。
氮化钒可由五氧化二钒、碳粉、活性剂等原材料制成的坯件,在常压、氮气氛保护下,经1500~1800℃高温状态下,反应生成钒氮合金。其关键工艺设备为连续式气氛推板高温炉,采用硅钼棒等电热元件获取热源。
申请号为201010548528.4的发明专利公开了一种氮化钒的制备方法,将氧化钒与有机氮化物混合经过热处理制得钒氮螯合物,结晶、过滤,然后在保护气体中煅烧,得到氮化钒,其煅烧的温度为500~600℃。
申请号为01139886.8的发明专利公开了氮化钒的生产方法,先将粉末状的钒氧化物、碳质粉剂和粘结剂混合均匀后压块、成型,再将成型后的物料加入制备炉中,同时制备炉通入保护和反应气体,制备炉需加热到一定的温度区域,物料在该温度区域发生碳化和氮化反应,最终生成氮化钒,该方法需要将物料加热到1000~1800℃,物料在此温度区域反应的持续时间为2~6h。
申请号为201110000961.9的发明专利公开了一种简易的氮化钒生产方法,将V2O5粉和石墨粉按4:1的重量比在干混机上充分混合,按100:15的重量比在上述混合粉中加入含量为4%的聚乙烯醇水溶液,并在湿混机混合10分钟,将湿混好的混合粉压球,干燥后分层装入料车、入炉、密封炉门,抽真空至?0.02MPa,通入氮气压力至0.04MPa,加温至800℃并在此温度下进行预还原5小时左右,然后继续升温到1350℃持续不少于6小时的深度还原和碳化,在过程中不断充入纯度99.99%以上的氮气,升温至1600℃进行6~10小时的氮化烧结,此过程压力控制在0.02Mpa,总时间在20小时内,反应完成,停电冷却至150℃出炉。
以上方法均需在高温下制备,生产成本较高,且获得的产品中杂质元素含量偏高,尤其碳含量,大大限制了其用于领域。
发明内容
本发明解决的技术问题是提供氮化钒的制备方法。
本发明氮化钒的制备方法,将钒氧化物和碳质还原剂混合作为阳极,碳钢棒为阴极,在含低价氯化钒的碱金属/碱土金属氯化物熔盐体系中实施电解,并在阴极下方通入氮气,阴极析出的钒金属与氮气反应生成氮化钒。
其中,钒氧化物为三氧化二钒和五氧化二钒中的至少一种,碳质还原剂为石墨、石油焦或炭黑,碳质还原剂和钒氧化物按C/O摩尔比为1:1进行混合。碳钢棒可采用市售。
在熔盐体系中,低价氯化钒为VCly,2≤y≤4,低价氯化钒的浓度为4.5~6.5wt%,碱金属/碱土金属氯化物为NaCl、KCl、CaCl2、MgCl2和LiCl中的至少一种。
电解过程电压为2.8~3.2V,阴极电流密度为0.1~0.5A/cm2,阳极电流密度为0.05~0.35A/cm2。
氮气为高纯氮气,氮气的流量为1~5L/min。
电解温度优选为700~850℃。
本发明氮化钒的制备方法,通过电解方法获得氮化钒,可有效降低氮化制备的温度,降低生产成本,同时由于电解的精炼及保护作用使得其产品质量较好,氧和碳等杂质元素含量较低,此外,还能通过控制电流密度等参数调节产品粒径,其产品粒径可控,适合做粉末冶金添加剂,具备较强应用前景。
具体实施方式
本发明氮化钒的制备方法,以钒氧化物和碳质还原剂混合为阳极,碳钢棒为阴极,在含低价氯化钒的碱金属/碱土金属氯化物熔盐体系中实施电解,并在阴极下方通入氮气,阴极析出的钒金属与氮气反应生成氮化钒。将电解质和氮化钒进行分离,即得氮化钒产品。
其中,钒氧化物为三氧化二钒、五氧化二钒中的至少一种,碳质还原剂为石墨、石油焦或炭黑,碳质还原剂和钒氧化物按C/O摩尔比为1:1进行混合,即按摩尔比,碳质还原剂中的C:钒氧化物中的O=1:1。为了保证阳极的质量,优选的混合方法如下:在混合过程中添加一定量的有机或无极粘结剂,在球磨机上压制为所需的料块,并在120℃条件下干燥12h以上。
本发明氮化钒的制备方法,以钒氧化物和碳质还原剂混合为阳极,碳钢棒为阴极,在含低价氯化钒的碱金属/碱土金属氯化物熔盐体系中实施电解,并在阴极下方通入氮气,此过程将发生下式的反应,(其中1.5≤x≤2.5)。通过湿法冶金洗去电解质便可获得氮化钒产品。
VOx+C=V+CO↑ (1)
2V+N2=2VN (2)
在熔盐体系中,低价氯化钒为VCly,2≤y≤4,即低价氯化钒为二氯化钒、三氯化钒和四氯化钒中的至少一种。低价氯化钒的浓度为4.5~6.5wt%,碱金属/碱土金属氯化物为碱金属氯化物和碱土金属氯化物中的至少一种,优选为NaCl、KCl、CaCl2、MgCl2和LiCl中的至少一种。
由于钒氧化物中添加了一定量的碳质还原剂,使得其自身导电可作为阳极,且碳在电化学作用下失去电子并与氧化钒中的氧结合,阳极以钒离子形式溶入电解质中,并在阴极析出,使得这样反应得以进行,电解过程电压控制在2.8~3.2V,阴极电流密度控制在0.1~0.5A/cm2,阳极电流密度控制在0.05~0.35A/cm2,以保证阳极的正常溶解。
电解的温度优选为700~850℃,这是由于钒在阴极以粉末固相物形式生成,其主要以三维核模型进行生长,其表面活性较高,在电解的700~850℃温度下,能用氮气较好反应生成氮化钒,有效降低了氮化钒的生产成本。
由于阴极先生成钒粉,通过控制电流密度等参数可对其生成粒径进行调节,从而可获得不同粒径的氮化钒。
为了提高氮化钒产品质量,所述氮气优选为高纯氮,氮气的流量为1~5L/min。在阴极下方通入氮气,不仅可与单质钒进行反应生成氮化钒,连续氮气的搅拌作用,使生成的氮化钒将脱落至槽底,可通过湿法冶金处理而实现电解质与氮化钒的分离,且氮气自身不与电解质体系中的低价钒发生反应,而不会对电极体系造成不良的影响。此外,氮气还可以起到保护气氛的作用。
下面结合实施例对本发明的具体实施方式做进一步的描述,并不因此将本发明限制在所述的实施例范围之中。如无特别说明,本发明中的百分数均为质量百分数。
实施例1
称取100gV2O5粉末(V2O5含量95%),-320目的石墨31.6g(碳含量≥99%),添加3wt%的PVA粘结剂混合,压制成Ф25的料柱,在烘箱内120℃条件下干燥12h以上,以其作为阳极,碳钢棒为阴极,在720℃的NaCl-KCl-VCl2体系(NaCl和KCl摩尔比为1:1,VCl2浓度为4.5wt%)中实施电解,电解条件为电压2.85V,阳极电流密度为0.2A/cm2,阴极电流密度为0.1A/cm2,氮气流量为1.5L/min,电解2h后,移去阴阳极后冷却,取出沉至电解槽底部的氮化钒和电解质,水洗除去电解质,获得产品60g,其粒径为45~75μm,参照GB/T20567-2006的分析方法,分析其主要成分为:V为78.2%,N为21.3,C为0.002%,P为0.002%,S为0.002%,VN含量大于99.9%。
实施例2
称取100gV2O3粉末((V2O5含量95%),-320目的炭黑25.3g(碳含量≥90%),添加2wt%的PVA粘结剂混合,压制成Ф25的料柱,在烘箱内120℃条件下干燥12h以上,以其作为阳极,碳钢棒为阴极,在720℃的NaCl-KCl-VCl2体系(NaCl和KCl摩尔比为1:1,VCl2浓度为4.5wt%)中实施电解,电解条件为电压2.85V,阳极电流密度为0.1A/cm2,阴极电流密度为0.15A/cm2,氮气流量为1.5L/min,电解2h后,移去阴阳极后冷却,取出沉至电解槽底部的氮化钒和电解质,水洗除去电解质,获得产品51g,其粒径为38~70μm,参照GB/T20567-2006的分析方法,分析其主要成分为:V为77.9%,N为20.8,C为0.003%,P为0.004%,S为0.003%,VN含量大于99.8%。
实施例3
称取50gV2O5粉末((V2O5含量95%)和50gV2O3粉末(V2O3含量95%),-320目的石油焦28.5g(碳含量≥95%),添加2wt%的PVA粘结剂混合,压制成Ф25的料柱,在烘箱内120℃条件下干燥12h以上,以其作为阳极,碳钢棒为阴极,在850℃的NaCl-CaCl2-VCl4体系(NaCl和CaCl2摩尔比为2:1,VCl4浓度为6.5wt%)中实施电解,电解条件为电压3.1V,阳极电流密度为0.35A/cm2,阴极电流密度为0.5A/cm2,氮气流量为2L/min,电解2h后,移去阴阳极后冷却,取出沉至电解槽底部的氮化钒和电解质,水洗除去电解质,获得产品65g,其粒径为75~830μm,参照GB/T20567-2006的分析方法,分析其主要成分为:V为78.1%,N为20.7,C为0.008%,P为0.003%,S为0.001%,VN含量大于99.8%。
Claims (6)
1.氮化钒的制备方法,其特征在于:将钒氧化物和碳质还原剂混合作为阳极,碳钢棒为阴极,在含低价氯化钒的碱金属/碱土金属氯化物熔盐体系中实施电解,并在阴极下方通入氮气,阴极析出的钒金属与氮气反应生成氮化钒。
2.根据权利要求1所述的氮化钒的制备方法,其特征在于:所述钒氧化物为三氧化二钒和五氧化二钒中的至少一种;所述碳质还原剂为石墨、石油焦或炭黑;碳质还原剂和钒氧化物按C/O摩尔比为1:1进行混合。
3.根据权利要求1所述的氮化钒的制备方法,其特征在于:所述熔盐体系中,低价氯化钒为VCly,2≤y≤4,低价氯化钒的浓度为4.5~6.5wt%,碱金属/碱土金属氯化物为NaCl、KCl、CaCl2、MgCl2和LiCl中的至少一种。
4.根据权利要求1所述的氮化钒的制备方法,其特征在于:所述电解的电压为2.8~3.2V,阴极电流密度为0.1~0.5A/cm2,阳极电流密度为0.05~0.35A/cm2。
5.根据权利要求1所述的氮化钒的制备方法,其特征在于:所述氮气为高纯氮气,氮气的流量为1~5L/min。
6.根据权利要求1所述的氮化钒的制备方法,其特征在于:电解温度为700~850℃。