CN104020033A - 一种常温9Cr-1Mo类钢晶界显示腐蚀剂 - Google Patents
一种常温9Cr-1Mo类钢晶界显示腐蚀剂 Download PDFInfo
- Publication number
- CN104020033A CN104020033A CN201410229071.9A CN201410229071A CN104020033A CN 104020033 A CN104020033 A CN 104020033A CN 201410229071 A CN201410229071 A CN 201410229071A CN 104020033 A CN104020033 A CN 104020033A
- Authority
- CN
- China
- Prior art keywords
- grain boundary
- normal temperature
- corrosive agent
- high temperature
- steel grain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种常温9Cr-1Mo类钢晶界显示腐蚀剂，其特征在于：以比例为：盐酸(分析纯)50毫升，氯化铁5克，硫酸铜4克，十二烷基磺酸钠1克，蒸馏水100毫升。与现有技术相比，通过使用本发明所示的腐蚀剂，在不将试样进行高温处理的情况下，直接打磨抛光侵蚀出晶界，进而进行观察评定。无需高温处理的工序，即可腐蚀出9Cr-1Mo类钢试样的晶界，避免了对高温加热设备的依赖，节约了时间和成本。
Description
技术领域
本发明涉及金相腐蚀剂及9Cr-1Mo类钢晶粒度检验的晶界显示方法。
背景技术
对于9Cr-1Mo类钢的金相晶粒度检验，目前一般采用GB/T6394-2002附录C中所推荐的氧化法，需要将试样加热到900℃淬火，然后再进行打磨抛光侵蚀出晶界，再进行观察。对于加热设备的依赖度较高，工序时间较长。
发明内容
为了克服上述现有技术的不足，本发明提供了一种常温9Cr-1Mo类钢晶界显示腐蚀剂，以解决在9Cr-1Mo类钢的金相晶粒度检验中需要将试样高温处理的问题。
本发明所采取的技术方案是：
一种常温9Cr-1Mo类钢晶界显示腐蚀剂，其特征在于：以比例为：
盐酸(分析纯)50毫升，
氯化铁5克，硫酸铜4克，
十二烷基磺酸钠1克，
蒸馏水100毫升。
与现有技术相比，通过使用本发明所示的腐蚀剂，在不将试样进行高温处理的情况下，直接打磨抛光侵蚀出晶界，进而进行观察评定。
无需高温处理的工序，即可腐蚀出9Cr-1Mo类钢试样的晶界，避免了对高温加热设备的依赖，节约了时间和成本。
具体实施方式：
本发明一种常温9Cr-1Mo类钢晶界显示腐蚀剂，以其比例：盐酸(分析纯)50毫升，氯化铁5克，硫酸铜4克，十二烷基磺酸钠1克，蒸馏水100毫升。如需较多或较少腐蚀液，可按倍比配置。
本金相腐蚀剂为盐酸、氯化铁、硫酸铜、十二烷基磺酸钠的混合溶液，能够在常温状态下腐蚀出9Cr-1Mo类钢的晶界，可在500倍以上显微镜下清晰的观察到。
对9Cr-1Mo类钢的试块依次使用砂轮、千叶轮、200#砂纸、400#砂纸、600#砂纸、800#砂纸打磨光滑，使用2微米直径金刚石抛光剂抛光至镜面，用酒精将试样表面冲洗干净，使用脱脂棉蘸取本发明腐蚀剂擦拭试样表面5～30秒，至试样表面灰暗，再用酒精棉球将试样表面多余腐蚀剂擦去，将试样表面用吹风机吹干或者自然风干，即可放到显微镜下观察。晶粒较小时，在低倍镜头下观察效果不明显，在500倍以上镜头中可观察到明显的晶界。
本发明的技术原理是由于晶界位置的原子能量较高，优先与酸、铁离子、铜离子发生反应，同时十二烷基磺酸钠对晶界内部的原子反应有一定的抑制作用，互相结合，使晶界能够较明显的显示出来。
Claims (1)
1.一种常温9Cr-1Mo类钢晶界显示腐蚀剂，其特征在于：比例为：
分析纯盐酸，50毫升，氯化铁5克，硫酸铜4克，
十二烷基磺酸钠1克，
蒸馏水100毫升。