CN104018000A - 一种真空分离处理贵铅物料的工艺 - Google Patents
一种真空分离处理贵铅物料的工艺 Download PDFInfo
- Publication number
- CN104018000A CN104018000A CN201410275084.XA CN201410275084A CN104018000A CN 104018000 A CN104018000 A CN 104018000A CN 201410275084 A CN201410275084 A CN 201410275084A CN 104018000 A CN104018000 A CN 104018000A
- Authority
- CN
- China
- Prior art keywords
- vacuum
- lead
- silver
- gold
- hybrid metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种真空分离处理贵铅物料的工艺。采用了破碎解离-真空冶金分离回收法，其原理是首先将贵铅物料经过破碎，得到粒径为0.01-0.2mm的混合金属物料；然后，基于混合金属物料各组分在同一温度下具有不同的蒸气压，在真空中通过蒸发与冷凝，可使易挥发金属铅在适宜的温度下进行蒸发，与金、银金属相互分离。本发明实现对贵铅中金属铅、金、银、的回收，具有分离效果好、生产工艺简单、成本小、无污染等特点。
Description
技术领域
本发明涉及贵铅物料的处理方法，特别是一种真空分离处理贵铅物料的工艺。
背景技术
铅与贵金属形成的铅合金，通常称贵铅。熔融的金属铅是贵金属的良好捕集剂，这一特性被用于试金分析和贵金属的提炼，称为贵铅熔炼。早在古代就知道了从贵铅中提取金、银的灰吹法。在近代，贵铅熔炼成为处理铜、铅阳极泥的一个重要过程，也是从各种废旧金属器件中回收金、银的主要方法之一。
目前常见的处理贵铅的工艺方法是通过分银炉火法精炼、灰吹炉或湿法电解等，在这些处理工艺过程中往往会产生的多种氧化渣都含有较高的金银，致使其直收率降低，且生产成本较高，分离不完全等。
更为重要的是，这些方法主要侧重于从贵铅中提取贵金属和稀有金属，而随着生产水平的提高，生产工艺的改进，贵铅中贵金属、稀有金属的含量相对逐渐减少，而由于铅等重金属造成的污染事件时有发生，导致水体、土壤、大气的铅污染，进而造成人类特别是儿童体内的血铅严重超标。因此，如何有效分离和回收有毒有害重金属铅显得格外重要。
发明内容
本发明的目的在于针对上述现有技术的不足，提供一种真空分离处理贵铅物料的工艺，利用真空蒸馏技术来浓缩和分离物料，将铅得以分离回收，同时将贵铅物料中的金、银进行富集，实现对贵铅中金属铅、金、银、的回收，具有分离效果好、生产工艺简单、成本小、无污染等特点。
为实现这一目的，本发明的技术解决方案如下：
一种真空分离处理贵铅物料的工艺，采用了破碎解离-真空冶金分离回收法，其原理是首先将贵铅物料经过破碎，得到粒径为0.01-0.2mm的混合金属物料；然后，基于混合金属物料各组分在同一温度下具有不同的蒸气压，在真空中通过蒸发与冷凝，可使易挥发金属铅在适宜的温度下进行蒸发，与金、银金属相互分离，从而实现综合利用和回收。
针对贵铅物料混合金属粉粒中铅的分离，本发明首先将粒径为0.01-0.2mm的混合金属物料在真空炉中进行加热，在真空度为0.01-1Pa、温度为800-1000℃条件下进行铅蒸发，同时通过冷凝器进行铅蒸气冷凝，冷凝温度为200-400℃；由此铅从金、银混合金属中分离出来，金、银得到富集，形成富集体；
具体包括以下步骤：
1、将贵铅物料经过破碎，得到粒径为0.01-0.2mm的混合金属物料；
2、将所述的混合金属物料的粉体为原料，放入石墨坩埚或采用高温耐火材料打底的坩埚中，再把坩埚放入真空炉中；
3、真空炉密封后启动真空系统抽气，使真空炉的压力为0.01-1Pa；
4、启动真空加热炉电源，把坩埚中混合金属粉末加热到800-1000℃，然后保持温度不变，使原料中铅蒸发，蒸发时间为2-4小时；
5、所述的铅蒸气在冷凝器上得以冷凝，冷凝温度为200-400℃，铅回收率达到98％以上，纯度达99％以上，混合金属中的金、银得到富集，形成富集体；富集体中银的含量上升至80％以上，可送贵冶车间进一步分离金、银。
与现有技术相比，本发明贵铅物料中铅的回收方法简单易行，具有成本低、高效、无污染等特点，真空分离完毕的混合金属可以继续用于下一步具有针对性的提纯分离。
相比采用火法和湿法等方法回收贵铅物料中有价金属的方法，本发明在减少环境污染方面尤其具有优势，并且最大限度避免了有毒重金属铅的二次污染问题。
具体实施方式
下面结合实施例对本发明作进一步描述，但不应以此限制本发明的保护范围。
首先将将贵铅物料200g经过破碎，得到粒径为0.01-0.2mm的混合金属物料，然后，经过磁选，分离铁质金属；得到含铅、金、银混合金属富集体原料194g，铅占93wt％，银占4wt％，金占0.7wt％,其它杂质2.3wt％，放入坩埚中，再把坩埚放入真空炉中。真空炉密封后启动真空系统抽气，使真空炉的真空度为0.01Pa。启动真空炉中的加热体加热坩埚，把坩埚中混合金属颗粒加热到900℃。然后保持温度不变，使原料中铅蒸发，蒸发时间为3小时。铅蒸气在冷凝器上得以冷凝，冷凝温度为350℃，回收铅178．3g，铅回收率为98．8％，纯度为99．5％，得到金、银混合金属富集体9.2g，混合金属富集体中银的含量上升至84％。蒸发完毕的混合金属富集体进行下一步继续提纯分离金、银。
Claims (1)
1.一种真空分离处理贵铅物料的工艺，其特征是：首先将粒径为0.01-0.2mm的混合金属物料在真空炉中进行加热，在真空度为0.01-1Pa、温度为800-1000℃条件下进行铅蒸发，同时通过冷凝器进行铅蒸气冷凝，冷凝温度为200-400℃；由此铅从金、银混合金属中分离出来，金、银得到富集，形成富集体；具体包括以下步骤：
1）将贵铅物料经过破碎，得到粒径为0.01-0.2mm的混合金属物料；
2）将所述的混合金属物料的粉体为原料，放入石墨坩埚或采用高温耐火材料打底的坩埚中，再把坩埚放入真空炉中；
3）真空炉密封后启动真空系统抽气，使真空炉的压力为0.01-1Pa；
4）启动真空加热炉电源，把坩埚中混合金属粉末加热到800-1000℃，然后保持温度不变，使原料中铅蒸发，蒸发时间为2-4小时；
5）所述的铅蒸气在冷凝器上得以冷凝，冷凝温度为200-400℃，铅回收率达到98％以上，纯度达99％以上，混合金属中的金、银得到富集，形成富集体；富集体中银的含量上升至80％以上，可送贵冶车间进一步分离金、银。