CN103991887B - 酸化后的铝矾土 - Google Patents

酸化后的铝矾土 Download PDF

Info

Publication number
CN103991887B
CN103991887B CN201410237836.3A CN201410237836A CN103991887B CN 103991887 B CN103991887 B CN 103991887B CN 201410237836 A CN201410237836 A CN 201410237836A CN 103991887 B CN103991887 B CN 103991887B
Authority
CN
China
Prior art keywords
bauxite
acidifying
dispensing
tablet
pulverizing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410237836.3A
Other languages
English (en)
Other versions
CN103991887A (zh
Inventor
黄飞翔
黄允金
陈丽萍
许盛英
许庆华
蒋文兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuyi Oubaite Clay Materials Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410237836.3A priority Critical patent/CN103991887B/zh
Publication of CN103991887A publication Critical patent/CN103991887A/zh
Application granted granted Critical
Publication of CN103991887B publication Critical patent/CN103991887B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种酸化后的铝矾土，其技术方案的要点是，酸化后的铝矾土配料由铝矾土、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成。将酸化后的铝矾土配料输入磨机中磨粉，磨粉后的粉状物为酸化后的铝矾土。采取先酸化再进行复合配料，可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应，充分发挥配料中原材料的各自特性，确保酸化后的铝矾土内在质量。根据产品质量的需要，采用碳酸钠调整酸化后的铝矾土pH值，方法简单易行。酸化后的铝矾土具有热稳定性好、导热率低、化学稳定性强、物理性能良好和可塑性特点。酸化后的铝矾土适用于生产国防、航空、汽车、电器、化工、日常生活用品和消防材料。

Description

酸化后的铝矾土
技术领域
本发明涉及酸化处理，具体涉及一种酸化后的铝矾土。
背景技术
矾土矿学名铝土矿、铝矾土，其组成成分异常复杂，是多种地质来源极不相同的含水氧化铝矿石的总称，如一水软铝石、一水硬铝石和三水铝石；有的是水铝石和高岭石相伴构成；有的以高岭石为主，且随着高岭石含量的增高，构成为一般的铝土岩或高岭石质粘土。铝土矿一般是化学风化或外生作用形成的，很少有纯矿物，总是含有一些杂质矿物，或多或少含有粘土矿物、铁矿物、钛矿物及碎屑重矿物等等。
为了提高铝矾土的热稳定性、化学和物理性能，铝矾土需要进行酸化处理。
酸化处理后没有进行后续的辅助性改性处理，不能全面提高铝矾土产品的质量。
发明内容
本发明的目的是克服现有技术中不足之处，提供一种酸化后的铝矾土。
酸化后的铝矾土配料由铝矾土、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成。
酸化后的铝矾土的生产方法：将酸化后的铝矾土配料输入磨机中磨粉，磨粉后的粉状物为酸化后的铝矾土。
铝矾土主要成分是氧化铝，系含有杂质的水合氧化铝，是一种土状矿物。白色或灰白色，因含铁而呈褐黄或浅红色，极难熔化，不溶于水，能溶于硫酸、氢氧化钠溶液，本发明选用铝矾土的颗粒细度≤5毫米。
硫酸选用浓度为98%的浓硫酸。
速溶硅酸钠为白色粉状物料，能快速溶解于水，具有粘结力强、强度较高，耐酸性、耐热性好，耐碱性和耐水性差的特点。
聚乙烯醇系白色固体，外型分絮状、颗粒状、粉末状三种；无毒无味、颗粒状可在80--90℃水中溶解，粉末状的在其他粉料的预分散后可在常温下溶解。具有较好的粘稠度、聚合性、粘结性及保水性。
羟丙基甲基纤维素具有增稠能力、排盐性、pH稳定性、保水性、尺寸稳定性、优良的成膜性以及广泛的耐酶性、分散性和粘结性等特点。
碳酸钠具有盐的通性和热稳定性，易溶于水，其水溶液呈碱性，在本发明中用于调整酸化后的铝矾土pH值。
本发明通过下述技术方案予以实现：
1、酸化后的铝矾土配料按重量百分比由下列组分组成：酸化后的铝矾土半成品90～98％、速溶硅酸钠0.1～5％、聚乙烯醇0.1～5％、羟丙基甲基纤维素0.01～3％和碳酸钠0～3％。
2、酸化后的铝矾土的生产方法：将酸化后的铝矾土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的铝矾土成品。
3、酸化后的铝矾土半成品的生产方法：⑴先将铝矾土输入已经运转的搅拌机中，再将稀硫酸缓慢加入铝矾土中进行酸化处理；⑵将酸化处理后的铝矾土，通过对辊机挤压为铝矾土片状物，铝矾土片状物的厚度≤3毫米；⑶将铝矾土片状物输送到回转式烘干炉内焙烧，焙烧时间为1～3小时，焙烧温度控制在250～350℃，焙烧后的铝矾土片状物含水量≤5％，焙烧后的铝矾土片状物为酸化后的铝矾土半成品，含水量百分比为重量百分比。
4、铝矾土片状物的配料按重量百分比由下列组分组成：铝矾土55～75％和稀硫酸25～45％。
5、稀硫酸的配料按重量百分比由下列组分组成：浓度为98%的浓硫酸1～5％，水95～99％，浓度为98%的浓硫酸百分比为重量百分比。
酸化后的铝矾土的生产方法采取先酸化再进行复合配料，可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应，充分发挥配料中原材料的各自特性，并得到互补，确保酸化后的铝矾土内在质量。
根据产品质量的需要，采用碳酸钠调整酸化后的铝矾土pH值，方法简单易行。
酸化后的铝矾土具有热稳定性好、导热率低、化学稳定性强、物理性能良好和可塑性特点。
酸化后的铝矾土适用于生产国防、航空、汽车、电器、化工、日常生活用品和消防材料。
具体实施方式
下面结合实施例对本发明作进一步的描述：
1、酸化后的铝矾土配料按重量百分比由下列组分组成：酸化后的铝矾土半成品94.5％、速溶硅酸钠2.3％、聚乙烯醇2％、羟丙基甲基纤维素1％和碳酸钠0.2％。
2、酸化后的铝矾土的生产方法：将酸化后的铝矾土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的铝矾土成品。
3、酸化后的铝矾土半成品的生产方法：⑴先将铝矾土输入已经运转的搅拌机中，再将稀硫酸缓慢加入铝矾土中进行酸化处理；⑵将酸化处理后的铝矾土，通过对辊机挤压为铝矾土片状物，铝矾土片状物的厚度≤3毫米；⑶将铝矾土片状物输送到回转式烘干炉内焙烧，焙烧时间为2小时，焙烧温度控制在280～320℃，焙烧后的铝矾土片状物含水量≤5％，焙烧后的铝矾土片状物为酸化后的铝矾土半成品。
4、铝矾土片状物的配料按重量百分比由下列组分组成：铝矾土68％和稀硫酸32％。
5、稀硫酸的配料按重量百分比由下列组分组成：浓度98﹪的硫酸2％，水98％。

Claims (3)

1.一种酸化后的铝矾土，其特征在于，酸化后的铝矾土配料按重量百分比由下列组分组成：酸化后的铝矾土半成品90～98％、速溶硅酸钠0.1～5％、聚乙烯醇0.1～5％、羟丙基甲基纤维素0.01～3％和碳酸钠0～3％；
酸化后的铝矾土的生产方法：将酸化后的铝矾土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的铝矾土成品；
酸化后的铝矾土半成品的生产方法：⑴先将铝矾土输入已经运转的搅拌机中，再将稀硫酸缓慢加入铝矾土中进行酸化处理；⑵将酸化处理后的铝矾土，通过对辊机挤压为铝矾土片状物，铝矾土片状物的厚度≤3毫米；⑶将铝矾土片状物输送到回转式烘干炉内焙烧，焙烧时间为1～3小时，焙烧温度控制在250～350℃，焙烧后的铝矾土片状物含水量≤5％，焙烧后的铝矾土片状物为酸化后的铝矾土半成品；
铝矾土片状物的配料按重量百分比由下列组分组成：铝矾土55～75％和稀硫酸25～45％；稀硫酸的配料按重量百分比由下列组分组成：浓度98﹪的硫酸1～5％，水95～99％。
2.根据权利要求1所述酸化后的铝矾土，其特征在于，酸化后的铝矾土的生产方法：将酸化后的铝矾土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的铝矾土成品。
3.根据权利要求1所述酸化后的铝矾土，其特征在于，选用铝矾土的颗粒细度≤5毫米。
CN201410237836.3A 2014-06-01 2014-06-01 酸化后的铝矾土 Active CN103991887B (zh)