CN103979554B - 酸化后的高岭土 - Google Patents

酸化后的高岭土 Download PDF

Info

Publication number
CN103979554B
CN103979554B CN201410237837.8A CN201410237837A CN103979554B CN 103979554 B CN103979554 B CN 103979554B CN 201410237837 A CN201410237837 A CN 201410237837A CN 103979554 B CN103979554 B CN 103979554B
Authority
CN
China
Prior art keywords
kaolin
acidifying
batching
weathering
flap
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410237837.8A
Other languages
English (en)
Other versions
CN103979554A (zh
Inventor
许庆华
许盛英
黄允金
黄飞翔
陈丽萍
蒋文兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Inbonny Technology Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410237837.8A priority Critical patent/CN103979554B/zh
Publication of CN103979554A publication Critical patent/CN103979554A/zh
Application granted granted Critical
Publication of CN103979554B publication Critical patent/CN103979554B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种酸化后的高岭土，其技术方案的要点是，酸化后的高岭土配料由高岭土、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成。酸化后的高岭土的生产方法：将酸化后的高岭土配料输入磨机中磨粉，磨粉后的粉状物为酸化后的高岭土。采取先酸化再进行复合配料，可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应，充分发挥配料中原材料的各自特性，确保酸化后的高岭土内在质量。酸化后的高岭土具有白度高、质软、易分散悬浮于水中、良好的可塑性、优良的电绝缘性能；还能增加酸化后的高岭土的胶体粘度和调整酸化后的高岭土pH值，适用于生产造纸、涂料、陶瓷、化工、橡胶、医药和耐火材料。

Description

酸化后的高岭土
技术领域
本发明涉及酸化处理，具体涉及一种酸化后的高岭土。
背景技术
高岭土是一种以高岭石族粘土矿物为主的粘土和粘土岩，多无光泽，质纯时颜白细腻，如含杂质时可带有灰、黄、褐等色，外观依成因不同可呈松散的土块状及致密状态岩块状。
以高岭土矿床成因为基础，根据不同成矿作用所体现的成矿地质、地理条件、矿床规模、矿体形态和赋存特征、矿石物质组分等方面的差异，将高岭土矿床划分为三种类型：硬质高岭土：质硬，无可塑性，粉碎细磨后具可塑性；软质高岭土：质软，可塑性较强，砂质质量分数≤50%；砂质高岭土：质松软，可塑性较弱，砂质质量分数≥50%。
在高岭土矿区，使用挖掘机进行机械化开采高岭土原矿，挖掘出来的是一种致密块状高岭土原矿，高岭土原矿的体积较大，不能直接用于酸化处理，常采用粉碎机破碎为细小的颗粒进行酸化处理，很容易破坏高岭土的晶体结构。
酸化处理后没有进行后续的辅助性改性处理，不能全面提高高岭土产品的质量。
发明内容
本发明的目的是克服现有技术中不足之处，提供一种酸化后的高岭土。
酸化后的高岭土配料由高岭土、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成。
酸化后的高岭土的生产方法：将酸化后的高岭土配料输入磨机中磨粉，磨粉后的粉状物为酸化后的高岭土。
高岭土具有白度高、质软、易分散悬浮于水中、良好的可塑性、较高的粘结性、优良的电绝缘性能和较好的耐火性等理化性质。
硫酸选用浓度为98%的浓硫酸。
速溶硅酸钠为白色粉状物料，能快速溶解于水，具有粘结力强、强度较高，耐酸性、耐热性好，耐碱性和耐水性差的特点。
聚乙烯醇系白色固体，外型分絮状、颗粒状、粉末状三种；无毒无味、颗粒状可在80--90℃水中溶解，粉末状的在其他粉料的预分散后可在常温下溶解。具有较好的粘稠度、聚合性、粘结性及保水性。
羟丙基甲基纤维素具有增稠能力、排盐性、pH稳定性、保水性、尺寸稳定性、优良的成膜性以及广泛的耐酶性、分散性和粘结性等特点。
碳酸钠具有盐的通性和热稳定性，易溶于水，其水溶液呈碱性，在本发明中用于调整酸化后的高岭土pH值。
本发明通过下述技术方案予以实现：
1、酸化后的高岭土配料按重量百分比由下列组分组成：酸化后的高岭土半成品90～98％、速溶硅酸钠0.1～5％、聚乙烯醇0.1～5％、羟丙基甲基纤维素0.01～3％和碳酸钠0～3％。
2、酸化后的高岭土的生产方法：将酸化后的高岭土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的高岭土成品。
3、酸化后的高岭土半成品的生产方法：⑴先将自然风化后的高岭土输入已经运转的搅拌机中，再将稀硫酸缓慢加入自然风化后的高岭土中进行酸化处理；⑵将酸化处理后的高岭土，通过对辊机挤压为高岭土片状物，高岭土片状物的厚度≤3毫米；⑶将高岭土片状物输送到回转式烘干炉内焙烧，焙烧时间为1～3小时，焙烧温度控制在250～350℃，焙烧后的高岭土片状物含水量≤5％，焙烧后的高岭土片状物为酸化后的高岭土半成品，含水量百分比为重量百分比。
4、高岭土片状物的配料按重量百分比由下列组分组成：自然风化后的高岭土55～75％和稀硫酸25～45％。
5、稀硫酸的配料按重量百分比由下列组分组成：浓度为98%的浓硫酸1～5％，水95～99％，浓度为98%的浓硫酸百分比为重量百分比。
6、高岭土原矿需要经过两个冬天以上的时间自然风化，从大块致密的原矿崩解为细小颗粒的自然风化后的高岭土，捡出明显可见的废石块、植物纤维和其它泥土杂质，自然风化后的高岭土颗粒细度≤5毫米。
酸化后的高岭土的生产方法采取先酸化再进行复合配料，可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应，充分发挥配料中原材料的各自特性，并得到互补，确保酸化后的高岭土内在质量。
根据产品质量的需要，采用碳酸钠调整酸化后的高岭土pH值，方法简单易行。
本发明充分利用太阳能、风雨交替和寒来暑往，促进对高岭土原矿的自然风化作用，提高高岭土原矿的崩解效果，加快高岭土原矿的分散。
酸化后的高岭土具有白度高、质软、易分散悬浮于水中、良好的可塑性、优良的电绝缘性能；还能增加酸化后的高岭土的胶体粘度和调整酸化后的高岭土pH值。
酸化后的高岭土适用于生产造纸、涂料、陶瓷、化工、橡胶、医药和耐火材料。
具体实施方式
下面结合实施例对本发明作进一步的描述：
1、酸化后的高岭土配料按重量百分比由下列组分组成：酸化后的高岭土半成品94.5％、速溶硅酸钠2.3％、聚乙烯醇2％、羟丙基甲基纤维素1％和碳酸钠0.2％。
2、酸化后的高岭土的生产方法：将酸化后的高岭土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的高岭土成品。
3、酸化后的高岭土半成品的生产方法：⑴先将自然风化后的高岭土输入已经运转的搅拌机中，再将稀硫酸缓慢加入自然风化后的高岭土中进行酸化处理；⑵将酸化处理后的高岭土，通过对辊机挤压为高岭土片状物，高岭土片状物的厚度≤3毫米；⑶将高岭土片状物输送到回转式烘干炉内焙烧，焙烧时间为2小时，焙烧温度控制在280～320℃，焙烧后的高岭土片状物含水量≤5％，焙烧后的高岭土片状物为酸化后的高岭土半成品。
4、高岭土片状物的配料按重量百分比由下列组分组成：自然风化后的高岭土68％和稀硫酸32％。
5、稀硫酸的配料按重量百分比由下列组分组成：浓度98﹪的硫酸2％，水98％。
6、高岭土原矿需要经过两个冬天以上的时间自然风化，从大块致密的原矿崩解为细小颗粒的自然风化后的高岭土，捡出明显可见的废石块、植物纤维和其它泥土杂质，自然风化后的高岭土颗粒细度≤5毫米。

Claims (2)

1.一种酸化后的高岭土，其特征在于，酸化后的高岭土配料按重量百分比由下列组分组成：酸化后的高岭土半成品90～98％、速溶硅酸钠0.1～5％、聚乙烯醇0.1～5％、羟丙基甲基纤维素0.01～3％和碳酸钠0～3％；
所述酸化后的高岭土半成品的生产方法：⑴先将自然风化后的高岭土输入已经运转的搅拌机中，再将稀硫酸缓慢加入自然风化后的高岭土中进行酸化处理；⑵将酸化处理后的高岭土，通过对辊机挤压为高岭土片状物，高岭土片状物的厚度≤3毫米；⑶将高岭土片状物输送到回转式烘干炉内焙烧，焙烧时间为1～3小时，焙烧温度控制在250～350℃，焙烧后的高岭土片状物含水量≤5％，焙烧后的高岭土片状物为酸化后的高岭土半成品；
高岭土片状物的配料按重量百分比由下列组分组成：自然风化后的高岭土55～75％和稀硫酸25～45％；稀硫酸的配料按重量百分比由下列组分组成：浓度98﹪的硫酸1～5％，水95～99％；高岭土原矿需要经过两个冬天以上的时间自然风化，从大块致密的原矿崩解为细小颗粒的自然风化后的高岭土，捡出明显可见的废石块、植物纤维和其它泥土杂质，自然风化后的高岭土颗粒细度≤5毫米。
2.根据权利要求1所述一种酸化后的高岭土，其特征在于，酸化后的高岭土的生产方法：将酸化后的高岭土配料输入磨机中磨粉，颗粒细度≤0.074毫米，磨粉后的粉状物为酸化后的高岭土成品。
CN201410237837.8A 2014-06-01 2014-06-01 酸化后的高岭土 Active CN103979554B (zh)