CN103980543B - 一种抗菌非金属粉体 - Google Patents

一种抗菌非金属粉体 Download PDF

Info

Publication number
CN103980543B
CN103980543B CN201410149144.3A CN201410149144A CN103980543B CN 103980543 B CN103980543 B CN 103980543B CN 201410149144 A CN201410149144 A CN 201410149144A CN 103980543 B CN103980543 B CN 103980543B
Authority
CN
China
Prior art keywords
powder
stir
calcium carbonate
stirring
suitable quantity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410149144.3A
Other languages
English (en)
Other versions
CN103980543A (zh
Inventor
陈永辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU TONGDA NEW MATERIALS TECHNOLOGY Co Ltd
Original Assignee
WUHU TONGDA NEW MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU TONGDA NEW MATERIALS TECHNOLOGY Co Ltd filed Critical WUHU TONGDA NEW MATERIALS TECHNOLOGY Co Ltd
Priority to CN201410149144.3A priority Critical patent/CN103980543B/zh
Publication of CN103980543A publication Critical patent/CN103980543A/zh
Application granted granted Critical
Publication of CN103980543B publication Critical patent/CN103980543B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗菌非金属粉体，其是由下述重量份的原料制得：重质碳酸钙粉60-75，硅铝粉5-12，复配抗菌剂10-20，柠檬酸三丁酯1-2、甘油三醋酸酯2-4、硅烷偶联剂DL602？1-2，硬脂酸1-2、马来酸二辛酯2.5-3、单硬脂酸甘油酯1-2、二甲基硅油1-2、石蜡油1-2；本发明添加有复配抗菌剂，具有很好的抗菌效果的同时可以在各种工业上应用。

Description

一种抗菌非金属粉体
技术领域
本发明涉及多重改性超细非金属粉体领域，确切地说是一种抗菌非金属粉体。
背景技术
非金属材料由非金属元素或化合物构成的材料。自19世纪以来，随着生产和科学技术的进步，尤其是无机化学和有机化学工业的发展，人类以天然的矿物、植物、石油等为原料，制造和合成了许多新型非金属材料，如水泥、人造石墨、特种陶瓷、合成橡胶、合成树脂（塑料）、合成纤维等。这些非金属材料因具有各种优异的性能，为天然的非金属材料和某些金属材料所不及，从而在近代工业中的用途不断扩大，并迅速发展。
非金属粉体广泛应用于涂料、塑料、造纸、印刷油墨、化纤、橡胶、化妆品等工业。
发明内容
本发明的目的在于提供一种抗菌非金属粉体。
上述目的通过以下方案实现：
一种抗菌非金属粉体，其特征在于：其是由下述重量份的原料制得：重质碳酸钙粉60-75，硅铝粉5-12，复配抗菌剂10-20，柠檬酸三丁酯1-2、甘油三醋酸酯2-4、硅烷偶联剂DL6021-2，硬脂酸1-2、马来酸二辛酯2.5-3、单硬脂酸甘油酯1-2、二甲基硅油1-2、石蜡油1-2；
所述的复配抗菌剂由下述重量份的原料制得：
轻质碳酸钙10-20，氧化锌3-5、羟基磷灰石粉3-5、聚碳酸酯1-2、贝壳粉4-6、硅烷偶联剂KH5501-2、碳酸银0.2-0.5、硫酸铜0.5-1，己二酸酯1-2、甘油三醋酸酯0.5-1、甲基壬基甲酮0.3-0.5；
所述的复配抗菌剂的制备方法为：将轻质碳酸钙加入适量水，搅拌均匀后，加入其余原料，于45-55℃下搅拌10-20分钟，烘干后，研磨，即得。
所述的一种抗菌非金属粉体，其特征在于：制备方法包括以下步骤：
（1）将复配抗菌剂与重质碳酸钙粉混匀，加入适量水，搅拌均匀，在50-60℃下搅拌30-40分钟后，过滤，滤饼干燥后，研磨成混合粉末后，备用；
（2）硅铝粉、柠檬酸三丁酯、硬脂酸混匀后，于45-55℃下搅拌5-10min，与步骤（1）所得混合粉末混匀，放入适量水，搅拌均匀后，调PH为5-6，再放入其余原料，搅拌均匀后，过滤，烘干，研磨，即得。
本发明的有益效果为：本发明添加有复配抗菌剂，具有很好的抗菌效果的同时可以在各种工业上应用。
具体实施方式
一种抗菌非金属粉体，其是由下述重量kg的原料制得：重质碳酸钙粉75，硅铝粉6，复配抗菌剂20，柠檬酸三丁酯2、甘油三醋酸酯4、硅烷偶联剂DL6022，硬脂酸2、马来酸二辛酯3、单硬脂酸甘油酯2、二甲基硅油2、石蜡油2；
所述的复配抗菌剂由下述重量kg的原料制得：
轻质碳酸钙20，氧化锌5、羟基磷灰石粉5、聚碳酸酯2、贝壳粉6、硅烷偶联剂KH5502、碳酸银0.5、硫酸铜0.8，己二酸酯2、甘油三醋酸酯1、甲基壬基甲酮0.5；
所述的复配抗菌剂的制备方法为：将轻质碳酸钙加入适量水，搅拌均匀后，加入其余原料，于55℃下搅拌20分钟，烘干后，研磨，即得。
所述的一种抗菌非金属粉体，制备方法包括以下步骤：
（1）将复配抗菌剂与重质碳酸钙粉混匀，加入适量水，搅拌均匀，在60℃下搅拌40分钟后，过滤，滤饼干燥后，研磨成混合粉末后，备用；
（2）硅铝粉、柠檬酸三丁酯、硬脂酸混匀后，于55℃下搅拌10min，与步骤（1）所得混合粉末混匀，放入适量水，搅拌均匀后，调PH为5.5，再放入其余原料，搅拌均匀后，过滤，烘干，研磨，即得。
对本实施例进行抗菌效果检测，作用24小时，对金黄色葡萄球菌的抗菌率为88%，对大肠杆菌的抗菌率为达到85%。

Claims (2)

1.一种抗菌非金属粉体，其特征在于：其是由下述重量份的原料制得：重质碳酸钙粉60-75，硅铝粉5-12，复配抗菌剂10-20，柠檬酸三丁酯1-2、甘油三醋酸酯2-4、硅烷偶联剂DL6021-2，硬脂酸1-2、马来酸二辛酯2.5-3、单硬脂酸甘油酯1-2、二甲基硅油1-2、石蜡油1-2；所述的复配抗菌剂由下述重量份的原料制得：轻质碳酸钙10-20，氧化锌3-5、羟基磷灰石粉3-5、聚碳酸酯1-2、贝壳粉4-6、硅烷偶联剂KH5501-2、碳酸银0.2-0.5、硫酸铜0.5-1，己二酸酯1-2、甘油三醋酸酯0.5-1、甲基壬基甲酮0.3-0.5；所述的复配抗菌剂的制备方法为：将轻质碳酸钙加入适量水，搅拌均匀后，加入其余原料，于45-55℃下搅拌10-20分钟，烘干后，研磨，即得。
2.根据权利要求1所述的一种抗菌非金属粉体，其特征在于：制备方法包括以下步骤：（1）将复配抗菌剂与重质碳酸钙粉混匀，加入适量水，搅拌均匀，在50-60℃下搅拌30-40分钟后，过滤，滤饼干燥后，研磨成混合粉末后，备用；（2）硅铝粉、柠檬酸三丁酯、硬脂酸混匀后，于45-55℃下搅拌5-10min，与步骤（1）所得混合粉末混匀，放入适量水，搅拌均匀后，调pH为5-6，再放入其余原料，搅拌均匀后，过滤，烘干，研磨，即得。
CN201410149144.3A 2014-04-15 2014-04-15 一种抗菌非金属粉体 Active CN103980543B (zh)