CN103910517B - 一种利用弗雷德盐制备烧结砖技术 - Google Patents

一种利用弗雷德盐制备烧结砖技术 Download PDF

Info

Publication number
CN103910517B
CN103910517B CN201410084900.9A CN201410084900A CN103910517B CN 103910517 B CN103910517 B CN 103910517B CN 201410084900 A CN201410084900 A CN 201410084900A CN 103910517 B CN103910517 B CN 103910517B
Authority
CN
China
Prior art keywords
fred salts
technology
fred
vitrified brick
salts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410084900.9A
Other languages
English (en)
Other versions
CN103910517A (zh
Inventor
王施娜
赵雪松
王敏芝
杨佰平
吴春江
佘卫民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RUGAO BAIPING BUILDING MATERIAL Co Ltd
Jiangsu Longchang Chemical Co Ltd
Original Assignee
RUGAO BAIPING BUILDING MATERIAL Co Ltd
Jiangsu Longchang Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by RUGAO BAIPING BUILDING MATERIAL Co Ltd, Jiangsu Longchang Chemical Co Ltd filed Critical RUGAO BAIPING BUILDING MATERIAL Co Ltd
Priority to CN201410084900.9A priority Critical patent/CN103910517B/zh
Publication of CN103910517A publication Critical patent/CN103910517A/zh
Application granted granted Critical
Publication of CN103910517B publication Critical patent/CN103910517B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种制备烧结砖技术，具体为利用弗雷德盐制备烧结砖技术为将弗雷德盐与折百粘土按比例充分混匀后，使用传统的粘土烧焙砖技术生产烧结砖。本发明采用的利用弗雷德盐制备烧结砖技术，利用了焙烧处理技术回收弗雷德盐，使弗雷德盐充分合理的资源化，变废为宝，减少了粘土使用量，保护土地资源；使用本发明技术生成的生坯在太阳下直接暴晒不会产生裂纹，不易变形，节约了辅料和凉棚，降低了生产成本；生坯在氢氧化钙的作用下弗雷德盐烧结砖自然干燥时间为7～8天，而普通粘土砖自然干燥时间为25天左右，明显比普通粘土砖缩短了生坯的自然干燥周期，有效提高了生产率。

Description

一种利用弗雷德盐制备烧结砖技术
技术领域
本发明涉及固废回收再利用技术领域，特别是涉及一种弗雷德盐的回收利用技术，属土木建筑材料领域。
背景技术
在弗雷德盐吸附处理废水后，含有少量的有机杂质，其主要成分为铝和钙，这些固废不能再次处理废水，且再生过程复杂，目前工厂只能将此类固废长期露天堆放或深度填埋于改良土壤，浪费了大量的资源。将处理废水后的弗雷德盐运用于烧结砖技术未见报道。由于普通粘土烧结砖技术生产的生坯在太阳下直接暴晒会产生裂纹，易变形，浪费了大量的辅料，提高了生产成本，且现有技术生产的普通粘土砖自然干燥时间为25天左右，生产效率不高。
发明内容
本发明的目的是为解决上述现有技术的缺陷，提供一种利用弗雷德盐制备烧结砖技术。
本发明采用的利用弗雷德盐制备烧结砖技术的技术方案为将弗雷德盐与折百粘土按比例充分混匀后，使用传统的粘土烧焙砖技术生产烧结砖。
所述的弗雷德盐与折百粘土的比例为弗雷德盐：折百粘土=2～5:8～5。
所述的弗雷德盐与折百粘土的比例为弗雷德盐：折百粘土=3:7。
所述的弗雷德盐中含钙和铝，所述钙和铝的比例为Ca：Al=2～4:1。
所述的弗雷德盐中钙和铝的比例为Ca：Al=3:1。
有益效果：本发明采用的利用弗雷德盐制备烧结砖技术，利用了焙烧处理技术回收弗雷德盐，使弗雷德盐充分合理的资源化，变废为宝，减少了粘土使用量，保护土地资源；使用本发明技术生成的生坯在太阳下直接暴晒不会产生裂纹，不易变形，节约了辅料和凉棚，降低了生产成本；生坯在氢氧化钙的作用下弗雷德盐烧结砖自然干燥时间为7～8天，而普通粘土砖自然干燥时间为25天左右，明显比普通粘土砖缩短了生坯的自然干燥周期，有效提高了生产率。
具体实施方式
下面的实施列可以使本专业技术人员更全面的理解本发明，但并不因此将本发明限制在所述的实施例范围之中。
实施例1
将弗雷德盐和粘土（折百）按弗雷德盐：粘土（折百）=2:8的比例充分搅拌混匀，传统方法制成砖坯，自然晾晒7天，整齐堆码置入多孔砖焙烧窑中，控制焙烧温度在850℃，连续焙烧两天，降温出窑。出窑后对弗雷德盐砖进行检测，外观光滑平整，颜色暗红，放射性达到A级，符合GB/T5101-98要求。
实施例2
将弗雷德盐和粘土（折百）按弗雷德盐：粘土（折百）=5:5的比例充分搅拌混匀，传统方法制成砖坯，自然晾晒7天，整齐堆码置入多孔砖焙烧窑中，控制焙烧温度在850℃，连续焙烧两天，降温出窑。出窑后对弗雷德盐砖进行检测，外观光滑平整，颜色暗红，放射性达到A级，符合GB/T5101-98要求。
实施例3
将弗雷德盐和粘土（折百）按弗雷德盐：粘土（折百）=3:7的比例充分搅拌混匀，传统方法制成砖坯，自然晾晒7天，整齐堆码置入多孔砖焙烧窑中，控制焙烧温度在850℃，连续焙烧两天，降温出窑。出窑后对弗雷德盐砖进行检测，外观光滑平整，颜色暗红，放射性达到A级，符合GB/T5101-98要求。

Claims (5)

1.一种制备烧结砖方法，其特征在于：所述的制备烧结砖技术为将弗雷德盐与折百粘土按比例充分混匀后，使用传统的粘土烧焙砖技术生产烧结砖。
2.根据权利要求1所述的制备烧结砖方法，其特征在于：所述的弗雷德盐与折百粘土的比例为弗雷德盐：折百粘土=2～5:8～5。
3.根据权利要求1所述的制备烧结砖方法，其特征在于：所述的弗雷德盐与折百粘土的比例为弗雷德盐：折百粘土=3:7。
4.根据权利要求1所述的制备烧结砖方法，其特征在于：所述的弗雷德盐中含钙和铝，所述钙和铝的比例为Ca：Al=2～4:1。
5.根据权利要求4所述的制备烧结砖方法，其特侦在于：所述的弗雷德盐中钙和铝的比例为Ca：Al=3:1。
CN201410084900.9A 2014-03-10 2014-03-10 一种利用弗雷德盐制备烧结砖技术 Active CN103910517B (zh)