CN103897449A - Method for preparing water-based paint - Google Patents
Method for preparing water-based paint Download PDFInfo
- Publication number
- CN103897449A CN103897449A CN201410065171.2A CN201410065171A CN103897449A CN 103897449 A CN103897449 A CN 103897449A CN 201410065171 A CN201410065171 A CN 201410065171A CN 103897449 A CN103897449 A CN 103897449A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- mass
- parts
- water
- based paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a water-based paint. The method comprises the following steps: putting 50-70 parts by mass of silicon dioxide, 30-40 parts by mass of calcium carbonate, 20-40 parts by mass of bentonite clay rock, 18-28 parts by mass of anhydrous sodium carbonate and 15-30 parts by mass of dibutyltin dilaurate into a sand mixer to carry out dry mixing for 10-30 minutes; adding 80-100 parts by mass of water and 20-40 parts by mass of vinyl acetate to carry out wet mixing for 20-40 minutes; pouring the mixture into an agitation barrel; adding 13-23 parts by mass of p-phenylenediamine, 15-20 parts by mass of sodium benzoate and 20-30 parts by mass of ethylene oxide; setting the rotation speed of the agitation barrel to 1500-2,000r/min and agitating for 1.5-2.5 hours. The method has the beneficial effects that the water-based paint prepared by the method disclosed by the invention is simple to fabricate, wide in application range, strong in environmental protection property and high in stability.
Description
Technical field
The present invention relates to a kind of preparation method of coating, relate in particular to a kind of preparation method of water-based paint.
Background technology
Coating is that one can firmly cover body surface, plays the chemical mixture of protection, decoration, mark and other special purposes.Along with improving constantly of scientific and technical development and living standards of the people, people are also growing for demand and the quality of coating, so water-based paint becomes the new fashion that current people pursue.Water-based paint is that one has " environmental protection " functional paint.The invention provides a kind of method of making water-based paint.
Summary of the invention
The invention discloses a kind of simple, to use the water-based paint having a wide reach preparation method that makes.
The technical solution used in the present invention:
A kind of preparation method of water-based paint is: by the silicon-dioxide of 50-70 mass parts, the calcium carbonate of 30-40 mass parts, the Montmorillonite clay stone of 20-40 mass parts, the dibutyl tin laurate of the anhydrous sodium carbonate of 18-28 mass parts and 15-30 mass parts is inserted sand mill, be dry mixed 10-30min, add again the water of 80-100 mass parts and the vinyl acetate between to for plastic of 20-40 mass parts, wet mixing 20-40min, pour batch mixing into agitation vat, add again the Ursol D of 13-23 mass parts, the oxyethane of the Sodium Benzoate of 15-20 mass parts and 20-30 mass parts, the rotating speed that agitation vat is set is 1500-2000r/min, stir 1.5-2.5h.
Beneficial effect of the present invention: water-based paint provided by the invention is made simple, broad range of applicability, the feature of environmental protection is strong, and stability is high; Adopt Ursol D tinting material, make water-based paint colouring of the present invention easily; Adopt vinyl acetate between to for plastic binding agent, bond effect is good; Adopt Sodium Benzoate sanitas, stablize anticorrosion; Adopt oxyethane defoamer, coating is evenly still.
Embodiment
Embodiment 1
A kind of preparation method of water-based paint is: by the calcium carbonate of the silicon-dioxide of 50 mass parts, 30 mass parts, the dibutyl tin laurate of the Montmorillonite clay stone of 20 mass parts, the anhydrous sodium carbonate of 18 mass parts and 15 mass parts is inserted sand mill, be dry mixed 10min, add again the water of 80 mass parts and the vinyl acetate between to for plastic of 20 mass parts, wet mixing 20min, pour batch mixing into agitation vat, add again Ursol D, the Sodium Benzoate of 15 mass parts and the oxyethane of 20 mass parts of 13 mass parts, the rotating speed that agitation vat is set is 1500r/min, stirs 1.5h.
Beneficial effect: water-based paint provided by the invention is made simple, broad range of applicability, the feature of environmental protection is strong, and stability is high; Adopt Ursol D tinting material, make water-based paint colouring of the present invention easily; Adopt vinyl acetate between to for plastic binding agent, bond effect is good; Adopt Sodium Benzoate sanitas, stablize anticorrosion; Adopt oxyethane defoamer, coating is evenly still.
Embodiment 2
A kind of preparation method of water-based paint is: by the calcium carbonate of the silicon-dioxide of 60 mass parts, 35 mass parts, the dibutyl tin laurate of the Montmorillonite clay stone of 30 mass parts, the anhydrous sodium carbonate of 20 mass parts and 23 mass parts is inserted sand mill, be dry mixed 20min, add again the water of 90 mass parts and the vinyl acetate between to for plastic of 30 mass parts, wet mixing 30min, pour batch mixing into agitation vat, add again Ursol D, the Sodium Benzoate of 17 mass parts and the oxyethane of 25 mass parts of 17 mass parts, the rotating speed that agitation vat is set is 1700r/min, stirs 2h.
Beneficial effect: water-based paint provided by the invention is made simple, broad range of applicability, the feature of environmental protection is strong, and stability is high; Adopt Ursol D tinting material, make water-based paint colouring of the present invention easily; Adopt vinyl acetate between to for plastic binding agent, bond effect is good; Adopt Sodium Benzoate sanitas, stablize anticorrosion; Adopt oxyethane defoamer, coating is evenly still.
Embodiment 3
A kind of preparation method of water-based paint is: by the calcium carbonate of the silicon-dioxide of 70 mass parts, 40 mass parts, the dibutyl tin laurate of the Montmorillonite clay stone of 40 mass parts, the anhydrous sodium carbonate of 28 mass parts and 30 mass parts is inserted sand mill, be dry mixed 30min, add again the water of 100 mass parts and the vinyl acetate between to for plastic of 40 mass parts, wet mixing 40min, pour batch mixing into agitation vat, add again Ursol D, the Sodium Benzoate of 20 mass parts and the oxyethane of 30 mass parts of 23 mass parts, the rotating speed that agitation vat is set is 2000r/min, stirs 2.5h.
Beneficial effect: water-based paint provided by the invention is made simple, broad range of applicability, the feature of environmental protection is strong, and stability is high; Adopt Ursol D tinting material, make water-based paint colouring of the present invention easily; Adopt vinyl acetate between to for plastic binding agent, bond effect is good; Adopt Sodium Benzoate sanitas, stablize anticorrosion; Adopt oxyethane defoamer, coating is evenly still.
Claims (1)
1. the preparation method of a water-based paint, it is characterized in that: by the silicon-dioxide of 50-70 mass parts, the calcium carbonate of 30-40 mass parts, the Montmorillonite clay stone of 20-40 mass parts, the dibutyl tin laurate of the anhydrous sodium carbonate of 18-28 mass parts and 15-30 mass parts is inserted sand mill, be dry mixed 10-30min, add again the water of 80-100 mass parts and the vinyl acetate between to for plastic of 20-40 mass parts, wet mixing 20-40min, pour batch mixing into agitation vat, add again the Ursol D of 13-23 mass parts, the oxyethane of the Sodium Benzoate of 15-20 mass parts and 20-30 mass parts, the rotating speed that agitation vat is set is 1500-2000r/min, stir 1.5-2.5h.