CN108047869A - A kind of no-solvent type polyurethane gravity flow self-leveling floor paint and preparation method thereof - Google Patents
A kind of no-solvent type polyurethane gravity flow self-leveling floor paint and preparation method thereof Download PDFInfo
- Publication number
- CN108047869A CN108047869A CN201711419808.3A CN201711419808A CN108047869A CN 108047869 A CN108047869 A CN 108047869A CN 201711419808 A CN201711419808 A CN 201711419808A CN 108047869 A CN108047869 A CN 108047869A
- Authority
- CN
- China
- Prior art keywords
- parts
- gravity flow
- solvent type
- type polyurethane
- floor paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of no-solvent type polyurethane gravity flow self-leveling floor paint the invention discloses paint technology field and preparation method thereof, which is made of the component of following parts by weight:100~120 parts of water-base resin, 4~6 parts of anti-settling agent, 5~7 parts of antifoaming agent, 8~10 parts of dispersant, 3~5 parts of glycidol ether, 4~6 parts of titanium dioxide, 3~5 parts of reactive diluent, 10~15 parts of porous-starch, 1~3 part of curing agent, 1~3 part of drier, the present invention can improve the water resistance and moisture resistance of floor paint, product obtained has wearability height, toughness is strong, hardening time is short, and is wherein free of hazardous solvent.
Description
Technical field
The invention discloses a kind of no-solvent type polyurethane gravity flow self-leveling floor paints and preparation method thereof, are specially paint technology
Field.
Background technology
At present, floor paint product is mainly based on epoxide terrace paint, and the hardness of paint film of epoxy floor paint is high, but toughness
Deficiency, and weatherability is bad, constrains the use scope of floor paint.At present, gravity flow self-leveling floor paint uses epoxy material,
Hard and crisp, weatherability is poor, in addition, contain phenyl ring on the chemical chain of epoxy resin, class structure of bisphenol A, since ultraviolet light irradiates, benzene
Ring is easily converted to quinoid structure so that paint film turns yellow, and has dusting tendency.Polyurethane terrace material mainly uses solvent-borne type,
Solvent borne polyurethane terrace leans on a large amount of solvents, does thin coating film, and to evade bubble, terrace solid content is low, big containing harmful quantity of solvent, dirty
Dye is big, and paint film is thin, is not durable.For this purpose, we have proposed a kind of no-solvent type polyurethane gravity flow self-leveling floor paints and preparation method thereof
It comes into operation, to solve the above problems.
The content of the invention
It is an object of the invention to provide a kind of no-solvent type polyurethane gravity flow self-leveling floor paint and preparation method thereof, to solve
The problems mentioned above in the background art.
To achieve the above object, the present invention provides following technical solution:A kind of no-solvent type polyurethane gravity flow self-leveling floor paint,
The floor paint is made of the component of following parts by weight:100~120 parts of water-base resin, 4~6 parts of anti-settling agent, 5~7 parts of antifoaming agent,
8~10 parts of dispersant, 3~5 parts of glycidol ether, 4~6 parts of titanium dioxide, 3~5 parts of reactive diluent, porous-starch 10~15
Part, 1~3 part of curing agent, 1~3 part of drier.
Preferably, the water-base resin polyester resin, phenolic resin, acrylic resin, organic siliconresin and polyurethane
One kind in resin.
Preferably, the anti-settling agent is bentonite or polyamide wax.
Preferably, the antifoaming agent is nano polysilicon oxygen alkane-poly- close copolymer emulsion class, polypropylene glycols, polyacrylic acid
One kind in class.
Preferably, the dispersant is modified polycarboxylic acid ammonium salt, modified polyacrylate, calgon, polyphosphoric acids
One or more mixtures in sodium and sodium pyrophosphate.
Preferably, the porous-starch is the mixed of the one or more in cornstarch, tapioca and wheaten starch
Close object.
Preferably, the curing agent is that the curing agent is cyclohexanediamine, polyamide, methyl ring pentanediamine and polyoxygenated
One kind in propylene triamine.
Preferably, the drier is the mixture of vanadic anhydride, isooctyl acid, manganese carbonate and light rare earth carbonate,
Wherein vanadic anhydride:Isooctyl acid:Manganese carbonate:Light rare earth carbonate=0.3:1.1:0.4:0.8.
Preferably, a kind of preparation method of no-solvent type polyurethane gravity flow self-leveling floor paint, this method are as follows:
S1:Water-base resin, titanium dioxide, porous-starch are inserted in mixer, by material mixing under stirring at low speed state;
S2:It then adds in anti-settling agent, antifoaming agent, dispersant, glycidol ether and reactive diluent and carries out high speed shear
Mixing stands 10~20min;
S3:Drier is added, and is uniformly mixed, 3~5min of mixing time;
S4:It is mixed with curing agent, no-solvent type polyurethane gravity flow self-leveling floor is made and paints product.
Compared with prior art, the beneficial effects of the invention are as follows:The present invention can improve floor paint water resistance and
Moisture resistance, product obtained has wearability height, toughness is strong, hardening time is short, and is wherein free of hazardous solvent.
Description of the drawings
Fig. 1 is preparation technology flow chart of the present invention.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment belongs to the scope of protection of the invention.
Embodiment one
The present invention provides a kind of no-solvent type polyurethane gravity flow self-leveling floor paint, the floor paint by following parts by weight component
It forms:100 parts of phenolic resin, 4 parts of bentonite, nano polysilicon oxygen alkane-gather close 5 parts of copolymer emulsion class antifoaming agent, be modified poly- carboxylic
8 parts of acid ammonium salt, 3 parts of glycidol ether, 4 parts of titanium dioxide, 3 parts of reactive diluent, 10 parts of cornstarch, 1 part of polyamide, drier
1 part.
The present invention also provides a kind of preparation method of no-solvent type polyurethane gravity flow self-leveling floor paint, the specific steps of this method
It is rapid as follows:
S1:Phenolic resin, titanium dioxide, cornstarch are inserted in mixer, by material mixing under stirring at low speed state;
S2:Then add in bentonite, nano polysilicon oxygen alkane-gather close copolymer emulsion class antifoaming agent, modified polycarboxylic acid ammonium salt,
Glycidol ether and reactive diluent carry out high speed shear mixing, stand 10min;
S3:Drier is added, and is uniformly mixed, mixing time 3min;
S4:It is mixed with polyamide, no-solvent type polyurethane gravity flow self-leveling floor is made and paints product.
Embodiment two
The present invention provides a kind of no-solvent type polyurethane gravity flow self-leveling floor paint, the floor paint by following parts by weight component
It forms:120 parts of acrylic resin, 6 parts of polyamide wax, 7 parts of polypropylene glycols antifoaming agent, 10 parts of calgon, glycidol
5 parts of ether, 6 parts of titanium dioxide, 5 parts of reactive diluent, 15 parts of tapioca, 3 parts of methyl ring pentanediamine, 3 parts of drier.
The present invention also provides a kind of preparation method of no-solvent type polyurethane gravity flow self-leveling floor paint, the specific steps of this method
It is rapid as follows:
S1:Acrylic resin, titanium dioxide, tapioca are inserted in mixer, mixed material under stirring at low speed state
It is even;
S2:It is dilute then to add in polyamide wax, polypropylene glycols antifoaming agent, calgon, glycidol ether and activity
It releases agent and carries out high speed shear mixing, stand 20min;
S3:Drier is added, and is uniformly mixed, mixing time 5min;
S4:It is mixed with methyl ring pentanediamine, no-solvent type polyurethane gravity flow self-leveling floor is made and paints product.
Embodiment three
The present invention provides a kind of no-solvent type polyurethane gravity flow self-leveling floor paint, the floor paint by following parts by weight component
It forms:110 parts of organic siliconresin, 5 parts of polyamide wax, 6 parts of polyacrylic antifoaming agent, 9 parts of sodium polyphosphate, glycidol ether
4 parts, 5 parts of titanium dioxide, 4 parts of reactive diluent, 13 parts of wheaten starch, 2 parts of polypropylene oxide triamine, 2 parts of drier.
The present invention also provides a kind of preparation method of no-solvent type polyurethane gravity flow self-leveling floor paint, the specific steps of this method
It is rapid as follows:
S1:Organic siliconresin, titanium dioxide, wheaten starch are inserted in mixer, mixed material under stirring at low speed state
It is even;
S2:It is dilute then to add in polyamide wax, polyacrylic antifoaming agent, sodium polyphosphate, glycidol ether and activity
It releases agent and carries out high speed shear mixing, stand 20min;
S3:Drier is added, and is uniformly mixed, mixing time 4min;
S4:It is mixed with polypropylene oxide triamine, no-solvent type polyurethane gravity flow self-leveling floor is made and paints product.
In summary described in embodiment, highly preferred embodiment of the present invention is embodiment three, can improve the waterproof of floor paint
Performance and moisture resistance, product obtained has wearability height, toughness is strong, hardening time is short, and is wherein free of hazardous solvent.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint, it is characterised in that:The floor paint by following parts by weight component structure
Into:100~120 parts of water-base resin, 4~6 parts of anti-settling agent, 5~7 parts of antifoaming agent, 8~10 parts of dispersant, glycidol ether 3~5
Part, 4~6 parts of titanium dioxide, 3~5 parts of reactive diluent, 10~15 parts of porous-starch, 1~3 part of curing agent, 1~3 part of drier.
2. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The aqueous tree
One kind in fat polyester resin, phenolic resin, acrylic resin, organic siliconresin and polyurethane resin.
3. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The anti-settling agent
For bentonite or polyamide wax.
4. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The antifoaming agent
For one kind in nano polysilicon oxygen alkane-poly- close copolymer emulsion class, polypropylene glycols, polyacrylic.
5. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The dispersant
For one kind in modified polycarboxylic acid ammonium salt, modified polyacrylate, calgon, sodium polyphosphate and sodium pyrophosphate or more
The mixture of kind.
6. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The porous shallow lake
Powder is one or more mixtures in cornstarch, tapioca and wheaten starch.
7. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The curing agent
It is one kind in cyclohexanediamine, polyamide, methyl ring pentanediamine and polypropylene oxide triamine for the curing agent.
8. a kind of no-solvent type polyurethane gravity flow self-leveling floor paint according to claim 1, it is characterised in that:The drier
For the mixture of vanadic anhydride, isooctyl acid, manganese carbonate and light rare earth carbonate, wherein vanadic anhydride:Isooctyl acid:Carbonic acid
Manganese:Light rare earth carbonate=0.3:1.1:0.4:0.8.
9. a kind of preparation method of no-solvent type polyurethane gravity flow self-leveling floor paint, it is characterised in that:The specific steps of this method are such as
Under:
S1:Water-base resin, titanium dioxide, porous-starch are inserted in mixer, by material mixing under stirring at low speed state;
S2:It then adds in anti-settling agent, antifoaming agent, dispersant, glycidol ether and reactive diluent and carries out high speed shear mixing,
Stand 10~20min;
S3:Drier is added, and is uniformly mixed, 3~5min of mixing time;
S4:It is mixed with curing agent, no-solvent type polyurethane gravity flow self-leveling floor is made and paints product.