CN104312353A - Building coating - Google Patents
Building coating Download PDFInfo
- Publication number
- CN104312353A CN104312353A CN201410474158.2A CN201410474158A CN104312353A CN 104312353 A CN104312353 A CN 104312353A CN 201410474158 A CN201410474158 A CN 201410474158A CN 104312353 A CN104312353 A CN 104312353A
- Authority
- CN
- China
- Prior art keywords
- building coating
- coating
- weight percentage
- comprises following
- following component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a building coating. The problem of poor performances of present aqueous building coatings is solved, the low dispersion of the present aqueous building coatings simply using water as a carrier is overcome, and a consolute alcoholic substance is added to improve the dispersion; a surfactant is added in the coating to promote the emulsifying dispersion of resin in the carrier water; and organic silicon resin is added to an acrylic emulsion in order to improve the weather ability and the contamination resistance of the coating. The coating comprises organic silicon resin, acrylic resin, a carrier, a pigment, a surfactant and an additive. The accurate ratio of all components makes the coating have excellent comprehensive performances, and the building coating is an aqueous coating, greatly reduces the application amount of an organic solvent, and is adapted to the international development trend of aqueous building coatings.
Description
Technical field
The present invention relates to a kind of building coating, particularly relate to a kind of building coating improving building coating weather resistance.
Background technology
Traditional Architectural Emulsion Paints needs the organic solvents such as the film coalescence aid adding more amount because of it in coating, cause the content of volatile organic compound of coating higher, in addition in order to when preventing coating to store become morally degenerate and film mouldy, in coating, also need the harmful organic mould inhibitor adding more amount, this directly has influence on the physical and mental health of user.The principal item of water-borne coatings is emulsion paint, is mainly made up of water, emulsion, color stuffing and various auxiliary agent four major part.The dispersion medium of water-borne coatings is water, and after coating application, what volatilize from film is water and a small amount of auxiliary agent, has the performance such as environmental protection, safety; Mainly account for the share more than 70% of Building-coating market based on the water-based paints of acrylic emulsions, it has been generally acknowledged that the paint of acrylic acid or the like latex emulsion base is for paint the most durable external application.The ventilation property of water-borne coatings is relatively good, and the water vapour of basic unit inside can to external diffusion; From the physical and chemical performance of film, some physical and chemical performance of water-borne coatings not as good as solvent based coating, as chemical-resistant, weathering resistance, contamination resistance etc.So the feature performance benefit such as environmental protection, safety of water-borne coatings should be retained, overcome the deficiency of its weathering resistance, contamination resistance performance again.The dispersing property used water as merely as carrier is not good, and the alcohols thing increasing cosolvency can improve its dispersing property.In coating, increase tensio-active agent be also beneficial to resin at the emulsion dispersion of water as carrier.Silicone resin is added in ACRYLIC EMULSION, is conducive to improving coating weathering resistance, contaminated resistance.But each component in coating influences each other with interactional, and each component of accurate proportioning just can obtain the coating of high comprehensive performance.
Summary of the invention
The object of the invention is to solve existing aqueous architectural coating dispersiveness, weathering resistance, contaminated resistance is not enough, provides a kind of building coating adopting silicone resin modification.
One, to achieve these goals, the present invention is by the following technical solutions:
1, a building coating, is characterized in that, coating comprises following component by weight percentage:
Silicone resin 0.6-0.9wt%, acrylic resin 11-49wt%, carrier 21-78wt%, pigment 5-35wt%, tensio-active agent 1-8wt%, additive 1-4wt%.
2, a kind of building coating according to claim 1, it is characterized in that, described carrier is a kind of solvent: it comprises following component by weight percentage: water 80wt%, Virahol 5 wt%, diethylene glycol butyl ether 5 wt%, ethylene glycol 5 wt%, methyl proxitol 5 wt%.
3, a kind of building coating according to claim 1, is characterized in that, described tensio-active agent is:
It comprises following component by weight percentage: sorbityl monododecanoate 30 wt%, Sorbitol Powder seven oleic acid ester 25 wt%, sorbitan laurate esters 25wt%, single oleylamide disodium sulfosuccinate 20wt%.
4, a kind of building coating according to claim 1, is characterized in that, described additive is made up of thickening material, disinfectant, siccative, solubility promoter, pigment dispersing agent, defoamer.
5, a kind of building coating according to claim 1, is characterized in that, described pigment is: it comprises following component by weight percentage: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt%, silicon-dioxide 30wt%.
6, a kind of building coating according to claim 1, is characterized in that, described acrylic resin is:
It comprises following component by weight percentage: vinylformic acid ester in ninth of the ten Heavenly Stems 40wt%, lauryl acrylate 38wt%, cyclohexyl acrylate 22wt%.
7, a kind of building coating according to claim 1, is characterized in that, described silicone resin is: it comprises following component by weight percentage: propyl group silsesquioxane resin 60 wt%, decamethylcyclopentaandoxane resin 40 wt%.
Two, preparation of the present invention: add silicone resin, acrylic resin and tensio-active agent at carrier and stir, adds other compositions and stirs after fully emulsified, filter and package i.e. obtained finished product.
Three, beneficial effect of the present invention:
The alcohols thing that the invention provides increases cosolvency improves the dispersing property of water; In coating, increase tensio-active agent be beneficial to resin at the emulsion dispersion of water as carrier; Silicone resin is added in ACRYLIC EMULSION, is conducive to improving coating weathering resistance, contaminated resistance, determines that the accurate proportioning of each component makes the high comprehensive performance of coating.As a kind of water-borne coatings, greatly reduce the usage quantity of organic solvent, adapt to the Overseas Development trend of building coating Water-borne modification.
embodiment
Below in conjunction with specific embodiment, the present invention is further explained:
The raw material adopted in the present invention all can be buied from market or the material that this area is conventional, all adopts the ordinary method of this area in following embodiment.
Embodiment 1:
1, a building coating, is characterized in that, coating comprises following component by weight percentage:
Silicone resin 0.6-0.9wt%, acrylic resin 11-49wt%, carrier 21-78wt%, pigment 5-35wt%, tensio-active agent 1-8wt%, additive 1-4wt%.
2, a kind of building coating according to claim 1, it is characterized in that, described carrier is a kind of solvent: it comprises following component by weight percentage: water 80wt%, Virahol 5 wt%, diethylene glycol butyl ether 5 wt%, ethylene glycol 5 wt%, methyl proxitol 5 wt%.
3, a kind of building coating according to claim 1, is characterized in that, described tensio-active agent is:
It comprises following component by weight percentage: sorbityl monododecanoate 30 wt%, Sorbitol Powder seven oleic acid ester 25 wt%, sorbitan laurate esters 25wt%, single oleylamide disodium sulfosuccinate 20wt%.
4, a kind of building coating according to claim 1, is characterized in that, described additive is made up of thickening material, disinfectant, siccative, solubility promoter, pigment dispersing agent, defoamer.
5, a kind of building coating according to claim 1, is characterized in that, described pigment is: it comprises following component by weight percentage: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt%, silicon-dioxide 30wt%.
6, a kind of building coating according to claim 1, is characterized in that, described acrylic resin is:
It comprises following component by weight percentage: vinylformic acid ester in ninth of the ten Heavenly Stems 40wt%, lauryl acrylate 38wt%, cyclohexyl acrylate 22wt%.
7, a kind of building coating according to claim 1, is characterized in that, described silicone resin is: it comprises following component by weight percentage: propyl group silsesquioxane resin 60 wt%, decamethylcyclopentaandoxane resin 40 wt%.
Embodiment 2:
1, a building coating, is characterized in that, coating comprises following component by weight percentage:
Silicone resin 0.8wt%, acrylic resin 40wt%, carrier 45wt%, pigment 8wt%, tensio-active agent 4wt%, additive 2.2wt%.
2, a kind of building coating according to claim 1, it is characterized in that, described carrier is a kind of solvent: it comprises following component by weight percentage: water 80wt%, Virahol 5 wt%, diethylene glycol butyl ether 5 wt%, ethylene glycol 5 wt%, methyl proxitol 5 wt%.
3, a kind of building coating according to claim 1, is characterized in that, described tensio-active agent is:
It comprises following component by weight percentage: sorbityl monododecanoate 30 wt%, Sorbitol Powder seven oleic acid ester 25 wt%, sorbitan laurate esters 25wt%, single oleylamide disodium sulfosuccinate 20wt%.
4, a kind of building coating according to claim 1, is characterized in that, described additive is made up of thickening material, disinfectant, siccative, solubility promoter, pigment dispersing agent, defoamer.
5, a kind of building coating according to claim 1, is characterized in that, described pigment is: it comprises following component by weight percentage: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt%, silicon-dioxide 30wt%.
6, a kind of building coating according to claim 1, is characterized in that, described acrylic resin is:
It comprises following component by weight percentage: vinylformic acid ester in ninth of the ten Heavenly Stems 40wt%, lauryl acrylate 38wt%, cyclohexyl acrylate 22wt%.
7, a kind of building coating according to claim 1, is characterized in that, described silicone resin is: it comprises following component by weight percentage: propyl group silsesquioxane resin 60 wt%, decamethylcyclopentaandoxane resin 40 wt%.
Claims (7)
1. a building coating, is characterized in that, coating comprises following component by weight percentage:
Silicone resin 0.6-0.9wt%, acrylic resin 11-49wt%, carrier 21-78wt%, pigment 5-35wt%, tensio-active agent 1-8wt%, additive 1-4wt%.
2. a kind of building coating according to claim 1, it is characterized in that, described carrier is a kind of solvent: it comprises following component by weight percentage: water 80wt%, Virahol 5 wt%, diethylene glycol butyl ether 5 wt%, ethylene glycol 5 wt%, methyl proxitol 5 wt%.
3. a kind of building coating according to claim 1, is characterized in that, described tensio-active agent is:
It comprises following component by weight percentage: sorbityl monododecanoate 30 wt%, Sorbitol Powder seven oleic acid ester 25 wt%, sorbitan laurate esters 25wt%, single oleylamide disodium sulfosuccinate 20wt%.
4. a kind of building coating according to claim 1, is characterized in that, described additive is made up of thickening material, disinfectant, siccative, solubility promoter, pigment dispersing agent, defoamer.
5. a kind of building coating according to claim 1, is characterized in that, described pigment is: it comprises following component by weight percentage: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt%, silicon-dioxide 30wt%.
6. a kind of building coating according to claim 1, is characterized in that, described acrylic resin is:
It comprises following component by weight percentage: vinylformic acid ester in ninth of the ten Heavenly Stems 40wt%, lauryl acrylate 38wt%, cyclohexyl acrylate 22wt%.
7. a kind of building coating according to claim 1, is characterized in that, described silicone resin is: it comprises following component by weight percentage: propyl group silsesquioxane resin 60 wt%, decamethylcyclopentaandoxane resin 40 wt%.