CN104403429A - Interior and exterior wall priming paint and preparation method thereof - Google Patents
Interior and exterior wall priming paint and preparation method thereof Download PDFInfo
- Publication number
- CN104403429A CN104403429A CN201410649593.4A CN201410649593A CN104403429A CN 104403429 A CN104403429 A CN 104403429A CN 201410649593 A CN201410649593 A CN 201410649593A CN 104403429 A CN104403429 A CN 104403429A
- Authority
- CN
- China
- Prior art keywords
- priming paint
- water
- adopts
- rotating speed
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Belonging to the field of building and decoration materials, the invention particularly relates to an interior and exterior wall priming paint and a preparation method thereof. The priming paint is prepared from the following raw materials by weight: 10-35 parts of water, 0.5-0.6 part of hydroxyethyl cellulose, 0.1-0.2 part of a water-based multifunctional additive, 0.5-0.6 part of a water-based dispersing agent, 0.1-0.2 part of a water-based wetting agent, 0.35-0.4 part of a water-based defoaming agent, 0.2-0.3 part of a mildew inhibitor, 8-10 parts of titanium dioxide, 8-10 parts of mica powder, 5-8 parts of talcum powder, 20-25 parts of calcium carbonate, 13-15 parts of a styrene-acrylic emulsion, 0.8-1.0 part of a film forming additive, 0.8-1.0 part of an antifreezing agent, and 0.2-0.3 part of a bactericidal antiseptic. On the basis of meeting the JG/T210-2007 building interior and exterior wall priming paint type II standards, the interior and exterior wall priming paint prepared by the invention has an emulsion dosage reduced by 5% than ordinary exterior wall priming paint, thus reducing the production cost.
Description
Technical field
The present invention relates to a kind of primer base and preparation method thereof, particularly a kind of inner-outer wall priming paint and preparation method thereof, belongs to architectural decoration material field.
Background technology
The building of current employing coating for internal and external wall is increasing, and the problems such as decortication, foaming, explosion, variable color appear in some metopes, have impact on the result of use of coating.Trace it to its cause, except coating quality, major part is short in understanding to priming paint or does not have proper use of causing.External wall base material mostly is cement mortar or concrete surface, be characterized in many spaces, alkalescence by force, wherein vesicular structure makes its water-absorbent strong, causes coatingsurface smooth not, easily cause film wrinkling, and dried coating film may be caused too fast and cause finish paint cracking waste finish paint; Alkalescence can cause by force the chemical degradation of resin in coating, accelerates ginkgo seeds, reduces the time limit of service of coating.So, must priming paint be used in application.
The effect of priming paint closes body of wall, resists the alkaline matter that body of wall cement layer oozes out, and priming paint can also strengthen the hardness of wall plastering layer.The index minimum due to exterior wall base paint must pass through JG/T210-2007 building inside and outside wall priming paint II type standard, and this standard is directly high for common for priming paint contrast locating exterior wall paint, so the general price of priming paint is also high than common exterior wall paint; This just makes some human consumers be reluctant to buy the immediate cause of priming paint, the most finally causes the problems such as decortication, foaming, explosion, variable color.Because the index request of exterior wall base paint is higher than interior wall, naturally also just higher (general exterior wall base paint emulsion is with being no less than 20%), guarantee is by permeability rate and resistance to salting-out for emulsion consumption.
Summary of the invention
In order to solve the problems referred to above existing for prior art, the invention provides a kind of inner-outer wall priming paint and preparation method thereof, inner-outer wall priming paint prepared by the present invention is on the basis meeting JG/T210-2007 building inside and outside wall priming paint II type standard, the common exterior wall base paint of emulsion amount ratio is low by 5%, reduces production cost.
Technical solution of the present invention is as follows:
One) scheme one:
A kind of inner-outer wall priming paint, it is made up of the raw material of following weight proportioning:
Water in technique scheme can adopt common tap water or other clean water, and it is as the dispersion of dispersed color, regulates the viscosity of slurry during making beating.
Described Natvosol adopts the water dissolvable ether of cellulose of non-ionic type, can be the Natvosol of different molecular weight, and it is as thickening material when regulating dispersion to pull an oar, and makes pigment have a good dispersion viscosity.
Described water-soluble multifunctional auxiliary agent adopts AMP-95 multifunctional assistant, and it is mainly used for regulating potential of hydrogen, has the effect of wetting, dispersion and stabilising system.
Described aqueous dispersant adopts polyacrylic acid sodium salt waterborne pigment dispersant or polycarboxylate sodium's type discrete dosage forms dispersion agent.
Described wetting agent is environment-friendly type non-ionic emulsifier wetting agent, not containing APEO, soak for coating, reduce the making beating viscosity of color stuffing, improve the consistency of color stuffing and benzene emulsion, there is excellent seepage force and reduce the capillary wetting aid as color stuffing dispersion.
Described water-based defoamer is non-ionic type defoamer or silicone antifoam agent.
Described mould inhibitor adopts daconil M emulsion, is a kind of efficient, wide spectrum water mildow-proof agent, can effectively killing fungus and algae, does not contain organic solvent.
Described titanium dioxide is anatase thpe white powder or Rutile type Titanium Dioxide.
Described mica powder reduces the perviousness of coating in formulation for coating material system, thus reduces the permeability rate of paint film.
Described talcum powder adopts 1200-1300 object talcum powder, reduces the perviousness of coating in formulation for coating material system, thus reduces the permeability rate of paint film.
Described calcium carbonate adopts 800 order water-ground limestones; Play a part to fill and reduce costs in formula system.
Described benzene emulsion adopts vinylbenzene and acrylate copolymer, has excellent weathering resistance, sticking power, is film forming matter, can provides good cohesive force.
Described film coalescence aid adopts 2,2,4-trimethylammonium-1,3-pentanediol diisobutyrate, the film coalescence aid of non-VOC, low smell, is to help film forming matter more than 5 DEG C, become a continuous print film.
Described frostproofer is triphenyl vinyl phenol ethoxy compound, and film forming matter can be prevented freezing when storing for-5 DEG C to 0 DEG C.
Described biocide mildewcide adopts isothiazolinone disinfecting agent, has sterilization and anticorrosion effect.
Two) scheme two:
For the preparation of a preparation method for inner-outer wall priming paint described in scheme one, it comprises following step of sequentially carrying out:
(1) 10-35 part water is added in dispersion cylinder, under 350-550r/min rotating speed, add 0.5-0.6 part Natvosol and 0.1-0.2 part water-soluble multifunctional auxiliary agent successively, dispersion 1-3min;
(2) after improving rotating speed to 800-1000r/min, after adding 0.5-0.6 part aqueous dispersant, 0.1-0.2 part aqueous wetting agent, 0.35-0.4 part water-based defoamer, 0.2-0.3 part mould inhibitor, 8-10 part titanium dioxide, 8-10 part mica powder, 5-8 part talcum powder and 20-25 part calcium carbonate successively, again improve rotating speed and disperse 15-20min to 1800-2000r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1000-1200r/min rotating speed, add 13-15 part benzene emulsion, 0.8-1.0 part film coalescence aid, 0.8-1.0 part frostproofer and 0.2-0.3 part fungicidal preservative successively, 15-20min is even to mixing liquid in dispersion.
The selected various Material cladding collocation of the present invention, component and weight proportion thereof is determined by multinomial experiment, it is a kind of new coating developed for the permeability rate of priming paint, inner-outer wall priming paint of the present invention tool compared with the common priming paint of exterior wall has the following advantages: the common priming paint of the original exterior wall of benzene emulsion amount ratio can reduce 5%, but the indices such as permeability rate all meet the exterior wall standard of building trade standard JGT210-2007 " building inside and outside wall priming paint ", and reduce formulation cost.
Embodiment
Below in conjunction with embodiment, embodiment, content of the present invention is described in detail:
(1) embodiment
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 10-35 part water is added in dispersion cylinder, under 350-550r/min rotating speed, add 0.5-0.6 part Natvosol and 0.1-0.2 part water-soluble multifunctional auxiliary agent successively, dispersion 1-3min;
(2) after improving rotating speed to 800-1000r/min, after adding 0.5-0.6 part aqueous dispersant, 0.1-0.2 part aqueous wetting agent, 0.35-0.4 part water-based defoamer, 0.2-0.3 part mould inhibitor, 8-10 part titanium dioxide, 8-10 part mica powder, 5-8 part talcum powder and 20-25 part calcium carbonate successively, again improve rotating speed and disperse 15-20min to 1800-2000r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1000-1200r/min rotating speed, add 13-15 part benzene emulsion, 0.8-1.0 part film coalescence aid, 0.8-1.0 part frostproofer and 0.2-0.3 part fungicidal preservative successively, 15-20min is even to mixing liquid in dispersion.
(2) embodiment
Embodiment 1 (most preferred embodiment)
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 32.7 parts of water are added in dispersion cylinder, under 450r/min rotating speed, add 0.5 part of Natvosol and 0.1 part of water-soluble multifunctional auxiliary agent successively, dispersion 2min;
(2) after improving rotating speed to 900r/min, after adding 0.6 part of aqueous dispersant, 0.2 part of aqueous wetting agent, 0.4 part of water-based defoamer, 0.2 part of mould inhibitor, 10 parts of titanium dioxides, 10 parts of mica powders, 5 parts of talcum powder and 23 parts of calcium carbonate successively, again improve rotating speed and disperse 18min to 1900r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1100r/min rotating speed, add 15 parts of benzene emulsions, 1.0 parts of film coalescence aid, 1.0 parts of frostproofers and 0.3 part of fungicidal preservative successively, 18min is even to mixing liquid in dispersion.
Embodiment 2
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 34.85 parts of water are added in dispersion cylinder, under 350r/min rotating speed, add 0.6 part of Natvosol and 0.2 part of water-soluble multifunctional auxiliary agent successively, dispersion 2min;
(2) after improving rotating speed to 800r/min, after adding 0.6 part of aqueous dispersant, 0.1 part of aqueous wetting agent, 0.35 part of water-based defoamer, 0.3 part of mould inhibitor, 8 parts of titanium dioxides, 10 parts of part mica powders, 7 parts of talcum powder and 23 parts of calcium carbonate successively, again improve rotating speed and disperse 15min to 1800r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1000r/min rotating speed, add 13 parts of benzene emulsions, 0.8 part of film coalescence aid, 1.0 parts of frostproofers and 0.2 part of fungicidal preservative successively, 15min is even to mixing liquid in dispersion.
Embodiment 3
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 32.65 parts of water are added in dispersion cylinder, under 550r/min rotating speed, add 0.55 part of Natvosol and 0.15 part of water-soluble multifunctional auxiliary agent successively, dispersion 3min;
(2) after improving rotating speed to 1000r/min, after adding 0.55 part of aqueous dispersant, 0.2 part of aqueous wetting agent, 0.4 part of water-based defoamer, 0.2 part of mould inhibitor, 8 parts of titanium dioxides, 8 parts of mica powders, 7 parts of talcum powder and 25 parts of calcium carbonate successively, again improve rotating speed and disperse 20min to 2000r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1200r/min rotating speed, add 15 parts of benzene emulsions, 1.0 parts of film coalescence aid, 1.0 parts of frostproofers and 0.3 part of fungicidal preservative successively, 20min is even to mixing liquid in dispersion.
Embodiment 4
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 33.7 parts of water are added in dispersion cylinder, under 350r/min rotating speed, add 0.55 part of Natvosol and 0.15 part of water-soluble multifunctional auxiliary agent successively, dispersion 3min;
(2) after improving rotating speed to 800r/min, after adding 0.6 part of aqueous dispersant, 0.1 part of aqueous wetting agent, 0.4 part of water-based defoamer, 0.2 part of mould inhibitor, 10 parts of titanium dioxides, 10 parts of mica powders, 8 parts of talcum powder and 20 parts of calcium carbonate successively, again improve rotating speed and disperse 15min to 2000r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1200r/min rotating speed, add 14 parts of benzene emulsions, 1.0 parts of film coalescence aid, 1.0 parts of frostproofers and 0.3 part of fungicidal preservative successively, 20min is even to mixing liquid in dispersion.
Embodiment 5
A kind of inner-outer wall priming paint, it is prepared from by following steps by following quality proportioning by following raw material:
(1) 10 parts of water are added in dispersion cylinder, under 550r/min rotating speed, add 0.5 part of Natvosol and 0.2 part of water-soluble multifunctional auxiliary agent successively, dispersion 1min;
(2) after improving rotating speed to 1000r/min, after adding 0.5 part of aqueous dispersant, 0.2 part of aqueous wetting agent, 0.35 part of water-based defoamer, 0.3 part of mould inhibitor, 8 parts of titanium dioxides, 10 parts of mica powders, 5 parts of talcum powder and 25 parts of calcium carbonate successively, again improve rotating speed and disperse 20min to 1800r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1000r/min rotating speed, add 15 parts of benzene emulsions, 0.8 part of film coalescence aid, 1.0 parts of frostproofers and 0.2 part of fungicidal preservative successively, 20min is even to mixing liquid in dispersion.
In above each embodiment:
Described hydromining ordinary tap water;
Described Natvosol adopts the sub-250HBR produced across dragon;
The AMP-95 that described water-soluble multifunctional auxiliary agent adopts Tao Shi to produce;
The SN5040 that described aqueous dispersant adopts Nuo Puke to produce;
Described aqueous wetting agent adopts 2500 of Hai Run production;
The A10 that CF246 and Hai Chuan that described water-based defoamer adopts Blackburn to produce produces;
The EPW that described mould inhibitor adopts Troy to produce;
The BLR-699 that described titanium dioxide adopts one hundred profit connection to produce;
Described mica powder adopts U.S. high mica powder;
The MS-1250 order talcum powder that described talcum powder adopts wide good fortune to produce;
The 700 order coarse whitings that described calcium carbonate adopts agriculture-countryside-farmer to produce;
The RS-308 that described benzene emulsion adopts Ahmedabad richness to produce;
The OE-300 that described film coalescence aid Yi Shiman produces;
Described frostproofer adopts the sub-FT-100 freeze-thaw stabiliser produced in sieve ground;
The RS that described biocide mildewcide adopts Troy to produce.
In each embodiment of inner-outer wall priming paint prepared by the present invention according to the property indices measured by JG/T210-2007 building inside and outside wall priming paint II type standard and technical indicator as shown in following table:
The experimental data that each embodiment of the inner-outer wall priming paint prepared by table one-the present invention records according to JG/T210-2007 building inside and outside wall priming paint II type standard
| Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Common exterior wall base paint |
| Water tolerance | Pass through | Pass through | Pass through | Pass through | Pass through | Pass through |
| Alkali resistance | Pass through | Pass through | Pass through | Pass through | Pass through | Pass through |
| Alkali burnout resistance | Pass through | Pass through | Pass through | Pass through | Pass through | Pass through |
| Salting-out resistance | Pass through | Pass through | Pass through | Pass through | Pass through | Pass through |
| Permeability rate | 0.4 | 0.45 | 0.45 | 0.42 | 0.42 | 0.45 |
| Sticking power | 2 | 2 | 2 | 2 | 2 | 2 |
As apparent from table one can, various embodiments of the present invention all meet the requirement of the salable product of JG/T210-2007 building inside and outside wall priming paint II type standard, and cost is lower than existing common exterior wall base paint.
Above-mentioned embodiment is just explained in detail technical scheme of the present invention; the present invention has more than and is only confined to above-described embodiment; those skilled in the art should be understood that; every improvement on basis of the present invention according to above-mentioned principle and spirit, substitute, all should within protection scope of the present invention.
Claims (8)
1. an inner-outer wall priming paint, is characterized in that: it is made up of the raw material of following weight proportioning:
2. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described Natvosol is the water dissolvable ether of cellulose of non-ionic type;
Described water-soluble multifunctional auxiliary agent adopts 2-amino-2-methyl-1-propanol;
Described aqueous dispersant adopts polyacrylic acid sodium salt waterborne pigment dispersant or polycarboxylate sodium's type dispersion agent or acrylic copolymer ammonium salt type dispersion agent.
3. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described aqueous wetting agent adopts environment-friendly type non-ionic emulsifier wetting agent;
Described water-based defoamer is non-ionic type defoamer or silicone antifoam agent;
Described mould inhibitor adopts daconil M emulsion;
Described titanium dioxide adopts anatase thpe white powder or Rutile type Titanium Dioxide.
4. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described calcium carbonate adopts water-ground limestone.
5. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described film coalescence aid adopts 2,2,4-trimethylammonium-1,3-pentanediol diisobutyrate.
6. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described frostproofer adopts triphenyl vinyl phenol ethoxy compound.
7. inner-outer wall priming paint as claimed in claim 1, is characterized in that:
Described fungicidal preservative adopts isothiazolinone disinfecting agent.
8., for the preparation of a preparation method for inner-outer wall priming paint according to any one of claim 1-8, it is characterized in that: it comprises following step of sequentially carrying out:
(1) 10-35 part water is added in dispersion cylinder, under 350-550r/min rotating speed, add 0.5-0.6 part Natvosol and 0.1-0.2 part water-soluble multifunctional auxiliary agent successively, dispersion 1-3min;
(2) after improving rotating speed to 800-1000r/min, after adding 0.5-0.6 part aqueous dispersant, 0.1-0.2 part aqueous wetting agent, 0.35-0.4 part water-based defoamer, 0.2-0.3 part mould inhibitor, 8-10 part titanium dioxide, 8-10 part mica powder, 5-8 part talcum powder and 20-25 part calcium carbonate successively, again improve rotating speed and disperse 15-20min to 1800-2000r/min rotating speed, detect fineness whether≤60 μm afterwards, if fineness≤60 μm, continue to perform step (3);
(3) reduce rotating speed under 1000-1200r/min rotating speed, after adding 13-15 part benzene emulsion, 0.8-1.0 part film coalescence aid, 0.8-1.0 part frostproofer and 0.2-0.3 part fungicidal preservative successively, 15-20min is even to mixing liquid in dispersion.