CN1037698A - 无机泡沫保温材料 - Google Patents

无机泡沫保温材料 Download PDF

Info

Publication number
CN1037698A
CN1037698A CN88107041A CN88107041A CN1037698A CN 1037698 A CN1037698 A CN 1037698A CN 88107041 A CN88107041 A CN 88107041A CN 88107041 A CN88107041 A CN 88107041A CN 1037698 A CN1037698 A CN 1037698A
Authority
CN
China
Prior art keywords
cellular insulant
inorganic cellular
inorganic
insulant
normal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN88107041A
Other languages
English (en)
Inventor
许继昌
杨庆理
高福成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HARBIN MODERN PRACTICAL CHEMISTRY INST
Original Assignee
HARBIN MODERN PRACTICAL CHEMISTRY INST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HARBIN MODERN PRACTICAL CHEMISTRY INST filed Critical HARBIN MODERN PRACTICAL CHEMISTRY INST
Priority to CN88107041A priority Critical patent/CN1037698A/zh
Publication of CN1037698A publication Critical patent/CN1037698A/zh
Pending legal-status Critical Current

Abstract

本发明属于无机泡沫保温材料，目前已有的泡沫 保温材料是以塑料、橡胶等有机高分子材为基材制成 的泡沫保温材料，这种泡沫保温材料成本高，加工制 造工艺复杂，本发明是用无机物氧化镁和氯化镁为基 材生产无机泡沫保温材料，具有生产工艺简单，成本 低廉的优点。

Description

本发明属于无机泡沫保温材料。
目前已有的泡沫保温材料，是以塑料，橡胶等有机高分子材料为基材制成的泡沫保温材料，这种泡沫保温材料的基材来源是石油化工产品，因此存在成本高、原料来源不易得、加工制造工艺复杂，不耐高温、易燃烧等缺点。
本发明的目的在于提出一种廉价的无机泡沫保温材料，用无机物氧化镁和氯化镁为基材生产无机泡沫保温材料，这种保温材料克服了已有泡沫保温材料存在的缺点，具有生产工艺简单，成本低廉、保温性能好等优点。
本发明的主要技术内容是，该无机泡沫保温材料是以氯化镁和氧化镁为基材制成，首先用波美度为22-35度的氯化镁和含量为85%以上的氧化镁调成粘稠的糊状物，然后向糊状物中加入予发泡好的发泡体，搅拌均匀制成浆料，然后将浆料放入模具中固化成型，固化时间为12-24小时，固化温度为常温，即可得无机泡沫保温材料。
本发明的技术效果在于，该无机泡沫保温材料是以氧化镁和氯化镁为基材制成，氧化镁是由菱镁矿石煅烧制成，氯化镁是海水生产食盐的附产品，因此成本低，原料来源广泛，易得;另外由于该泡沫保温材料的生产是在常温下进行发泡和固化成型的，因此工艺简单、节省能源和设备，同时该保温材料具有良好的保温性能和耐高温不易燃烧的优点。
附图为本发明的工艺流程示意图;
1波美度为22-35度的氯化镁、2含量为85%以上的氧化镁、3常温发泡剂、4泡沫稳定剂、5糊状物、6予发泡好的发泡体、7浆料、8模具、9固化成型。
实现本发明的最佳技术方案为，首先将波美度为22-35度的氯化镁1和含量为85%以上的氧化镁2混合，调成粘稠的糊状物5，然后将常温发泡剂3和泡沫稳定剂4在常温下混合进行予发泡，制成予发泡好的发泡体6，再将予发泡好的发泡体6和糊状物5混合制成浆料7，然后将浆料7放在模具8中进行固化成型9，固化温度为常温，固化的时间为12-24小时，即可得无机泡沫保温材料。
本发明中予发泡好的发泡体是采用常温发泡剂和泡沫稳定剂在常温下混合制成，常温发泡剂为皂化松香、十二烷基苯磺酸钠、腐植酸钠等，泡沫稳定剂为骨胶、聚乙烯醇、羧甲基纤维素、海藻酸钠等。
该无机泡沫保温材料的容重可通过发泡倍数来调节，发泡倍数由发泡剂的加入量控制，通过控制发泡剂的用量，使该保温材料的容重在150公斤/米3至400公斤/米3的范围内任意控制。
不同容重的产品具有不同的导热系数和抗压强度，根据不同的用途和需要可制成导热系数为0.05Kcal/mh℃至0.1Kcal/mh℃抗压强度为2公斤/厘米2至20公斤/厘米2的各种不同规格、型号的系列无机泡沫保温材料。

Claims (2)

1、一种无机泡沫保温材料，本发明的特征在于，该无机泡沫保温材料是以氯化镁和氧化镁为基材制成，首先将波美度为22-35度的氯化镁和含量为85%以上的氧化镁调成粘稠的糊状物，然后向糊状物中加入预发泡好的发泡体，搅拌均匀制成浆料然后将浆料放入模具中固化成型，固化的时间为12-24小时，固化的温度为常温，即可得无机泡沫保温材料。
2、根据权利要求1所述的无机泡沫保温材料，其特征在于预发泡好的发泡体是采用常温发泡剂和泡沫稳定剂在常温下混合制成，常温发泡剂为皂化松香、十二烷基苯磺酸钠，腐植酸钠等，泡沫稳定剂为骨胶，聚乙烯醇、羧甲基纤维素、海藻酸钠等。
CN88107041A 1988-10-09 1988-10-09 无机泡沫保温材料 Pending CN1037698A (zh)