CN1118358C - 聚苯轻质保温板及其制作工艺 - Google Patents
聚苯轻质保温板及其制作工艺 Download PDFInfo
- Publication number
- CN1118358C CN1118358C CN 00106331 CN00106331A CN1118358C CN 1118358 C CN1118358 C CN 1118358C CN 00106331 CN00106331 CN 00106331 CN 00106331 A CN00106331 A CN 00106331A CN 1118358 C CN1118358 C CN 1118358C
- Authority
- CN
- China
- Prior art keywords
- polystyrene foamed
- present
- magnesium oxide
- foamed plastic
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种聚苯轻质保温板及其制作工艺，属建筑保温材料，本发明由颗粒状废旧聚苯乙烯泡沫塑料，加入氧化镁、氯化镁溶液，加入膨胀珍珠岩粉后，经搅拌装置，搅拌均匀后，装入成组活模，脱模风干后即成本产品。本发明产品质轻，成本低，有利于环保，减少了白色污染，不需特殊养护，生产周期短，在-10～0℃不需加任何添加剂仍能生产，具有良好的保温、隔音性能，并且韧性好，工艺简单。适用于工业、民用建筑、屋面、内、外墙体的保温及楼层之间的隔音。
Description
本发明涉及一种聚苯轻质保温板及其制作工艺，属建筑用保温材料。
目前，建筑用保温板种类繁多。如冶金部建筑研究总院材料所和北京市建筑设计研究院科研所共同研制的水泥聚苯板，它是以聚苯乙烯泡沫塑料颗粒、水泥、EC起泡剂、稳泡剂，经搅拌成型养护而制成，其物理性能见表：
| 项目 | 指标 |
| 容重(Kg/m) | 280-330 |
| 导热系数(w/m.k) | ≤0.09 |
| 吸水率(％) | ≤30 |
此水泥聚苯板，容重较高，导热系数及吸水率较大，且是以水泥为粘合剂，需养生，养护期长，成品生产周期长。
本发明的目的在于提供一种重量轻，成本低，生产周期短，不需特殊养护，保温、隔音性能好，既降低了产品的导热系数及吸水率，同时也减少了白色污染的聚苯轻质保温板及其制作工艺。
本发明的目的是这样实现的：
本发明各物料按重量配比为：
颗粒状聚苯乙烯泡沫塑料5～10％；
氧化镁30～40％；
氯化镁溶液50～60％；
膨胀珍珠岩1～5％；
本发明是以直径5-10mm颗粒状的废旧聚苯乙烯泡沫塑料5-10％，加入含量大于60％的氧化镁30～40％、浓度大于20％的氯化镁溶液50～60％，再加膨胀珍珠岩1～5％，经搅拌装置，搅拌均匀，入模成型，脱模后自然风干而制成。
本发明由于采用了废旧的聚苯乙烯泡沫塑料为主要原料，所以本产品质轻，成本低，不但减少了白色污染，且有利于环保。本发明所使用的氧化镁和氯化镁溶液组成的粘合剂使产品不需特殊养护，生产周期缩短，且在-10～0℃不需任何添加剂仍能生产。由于膨胀珍珠岩也是一种保温材料，吸水性强，颗粒细小，本发明用于聚苯乙烯泡沫塑料颗粒间的填充料，它能饱吸粘合剂，包在聚苯乙烯泡沫塑料颗粒周围，防止粘合剂下沉，使成品拥有一定的强度。且有良好的保温、隔音性能、韧性好、工艺简单。适用于工业、民用建筑屋面、内、外墙体的保温及楼层间的隔音。
本发明的物理性能为：
| 项目 | 指标 |
| 容重(kg/m) | 230～280 |
| 导热系数(w/m.k) | ≤0.06 |
| 吸水率(％) | ≤15 |
实施例1：
生产聚苯轻质保温板干容重为240kg/m3时按重量比需用聚苯乙烯泡沫塑料颗粒9份、氧化镁36份、氯化镁溶液53份、膨胀珍珠岩2份装入搅拌机，搅拌均匀后，装入成组活模，脱模后自然风干而制成。
实施例2：
生产聚苯轻质保温板干容重为280kg/m3时按重量比需用聚苯乙烯泡沫塑料颗粒7份、氧化镁35份、氯化镁溶液55份、膨胀珍珠岩3份装入搅拌机，搅拌均匀后，装入成组活模，脱模后自然风干而制成。
实施例3：
如在1000m2的房屋上加盖聚苯轻质保温板，厚度为80mm，干容重为240kg/m3时，用(5～10mm)的废旧聚苯乙烯泡沫塑料颗粒2016kg，加入氧化镁8064kg，氯化镁溶液11872kg及膨胀珍珠岩448kg分次装入搅拌机，搅拌均匀后，装入成组活模，脱模后自然风干而制成，即可使用。
Claims (2)
1、聚苯轻质保温板，其特征在于：各成份重量配比：
颗粒状聚苯乙烯泡沫塑料 5～10％
氧化镁 30～40％
氯化镁溶液 50～60％
膨胀珍珠岩 1～5％
2、根据权利要求1所述的聚苯轻质保温板的制作工艺，其特征在于：取直径为5-10mm颗粒状的废旧聚苯乙烯泡沫塑料5-10％，加入含量大于60％的氧化镁30～40％、浓度大于20％的氯化镁溶液50～60％，然后再加入膨胀珍珠岩1～5％，经搅拌装置，搅拌均匀后，装入成组活模，脱模后自然风干而制成。