CN102344298A - 一种泡沫混凝土保温承重砖及其生产方法 - Google Patents
一种泡沫混凝土保温承重砖及其生产方法 Download PDFInfo
- Publication number
- CN102344298A CN102344298A CN201010242031XA CN201010242031A CN102344298A CN 102344298 A CN102344298 A CN 102344298A CN 201010242031X A CN201010242031X A CN 201010242031XA CN 201010242031 A CN201010242031 A CN 201010242031A CN 102344298 A CN102344298 A CN 102344298A
- Authority
- CN
- China
- Prior art keywords
- foam
- water
- foamed concrete
- brick
- preservation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种泡沫混凝土保温承重砖及其生产方法。其步骤是将水泥、粉煤灰渣、生石灰、石膏、粉煤灰渣(及砂)、复合抗裂纤维HF-8和专用早强减水剂HFsm,称量后加入搅拌机,干混1min,按适宜水料比计量加水、搅拌均匀,然后将发泡稳泡剂HF-3通过空压制泡系统制成微小泡沫加入搅拌机,快速搅拌使微泡均匀分布在浆体中,控制泡沫引入量,达到规定的料浆容重后,浇注入免切割成组模中,入窑进行远红外辐射干热养护,24小时后脱模,推码养护28天,测试性能,出厂使用。本发明生产的泡沫混凝土承重保温砖,质量轻,强度高,且保温性能好,利废环保,造价低廉,是粘土砖的理想替代产品。
Description
技术领域
本发明涉及一种泡沫混凝土保温承重砖及其生产方法。
背景技术
为落实建设部“关于禁用粘土实心砖推广新型建筑墙体材料”的规定,开发一种既可承重,抗压强度指标与粘土砖相当,又符合建筑节能要求的新型墙体材料是当前建材行业迫切需要解决的问题。在新型墙体材料中,泡沫混凝土是一种质量轻、热工性能好的建筑材料,其突出特点是在混凝土基体内部形成封闭的泡沫微孔,使混凝土获得轻质、保温隔热、防水耐火、抗冻耐久性能。其抗压强度来源于水泥并可大量应用工业废渣,可通过调节水泥和工业废渣用量比使水泥和工业废渣共同作用形成复合胶凝作用产生强度,既符合“综合利用废渣的循环经济和生态建材政策”,又降低了生产成本,使全面取代粘土砖成为可能。
发明内容
鉴于上述,本发明的目的旨在提供一种泡沫混凝土保温承重砖。
本发明的另一目的旨在提供一种泡沫混凝土保温承重砖的生产方法。
本发明的目的可以通过以下技术方案来实现:
一种泡沫混凝土保温承重砖,其原料及重量配比为:
普通硅酸盐水泥 20-35%
生石灰(CaO≥60%) 5-10%
石膏 1-2%
粉煤灰渣(及砂) 40-65%
复合抗裂纤维HF-8 50-110g/m3
专用早强减水剂HFsm 水泥量0.5-1%
水料比 0.45~0.60
发泡稳泡剂HF-3 3-5kg/m3
一种泡沫混凝土保温承重砖的生产方法,其特征是:
将水泥、粉煤灰渣、生石灰、石膏、粉煤灰渣(及砂)、复合抗裂纤维HF-8和专用早强减水剂HFsm,称量后加入搅拌机,干混1min,按0.45水料比计量加水、搅拌均匀,然后将发泡稳泡剂HF-3通过空压制泡系统制成微小泡沫加入搅拌机,快速搅拌使微泡均匀分布在浆体中,控制泡沫引入量,达到规定的料浆容重后,浇注入免切割成组模中,入窑进行远红外辐射干热养护,24小时后脱模,推码养护28天,测试性能,出厂使用。
本发明生产的泡沫混凝土保温承重砖规格与性能:
基本规格:300*150*100;600*300*200;600*300*150等
主要性能指标:表观密度:800-1200kg/m3;抗压强度≥7.5Mpa;干燥收缩值(快速法)≤0.8mm/m;导热系数(干态)≤0.18w/mk;抗冻性能合格;软化系数≥0.8。本发明技术指标测试参照《泡沫混凝土砌块》JC/T1062-2007和《加气混凝土性能试验方法》GB/T11969-11975-1997要求进行。
本发明的优点表现在以下几个方面:
泡沫混凝土承重保温砖,质量轻,强度高,且保温性能好,利废环保,造价低廉,是粘土砖的理想替代产品。本发明采用免切割成组模浇注成型新工艺,避免了使用控制难度大、成品率较低的大坯体初凝切割成型工艺,使小块型砖体和超轻质砖的生产成为可能。不但可方便地成型出小块型节能承重砖,还可高质量取代粘土砖,而且该工艺还可推广到加气混凝土生产中,采用免切割成组模成型,以带模蒸压工艺生产出高强节能承重砖和超轻节能保温砌块块(密度100-300kg/m3加气产品),产品性能优良、造价适中,对于替代粘土砖和超轻保温加气砼建材产品传统生产技术都将产生积极的革新作用。
具体实施方式
本发明采用的主要原材料:水泥为祁连山牌42.5普通硅酸盐水泥;生石灰有效CaO含量为70.1%;粉煤灰渣为西固热电厂混排灰渣;兰州海锋建材科技有限公司生产复合抗裂纤维HF-8、专用早强减水剂HFsm及发泡稳泡剂HF-3。采用压缩空气制泡快速搅拌制浆、免切割成组模浇注成型,远红外辐射干热养护新工艺。具体工艺方法如下:
将30kg水泥、8kg生石灰、2kg石膏、60kg粉煤灰渣(及砂)、100g/m3复合抗裂纤维HF-8和1kg专用早强减水剂HFsm,加入搅拌机,干混1min,按0.45水料比计量加水、搅拌均匀,然后将5kg/m3发泡稳泡剂HF-3通过空压制泡系统制成微小泡沫加入搅拌机,快速搅拌使微泡均匀分布在浆体中,通过调节制泡时间,控制泡沫引入量,达到规定的料浆容重后(一般控制料浆容重为1200kg/m3),浇注入免切割成组模中。免切割成组模由底模、边框模和纵横拼插的内隔板组成,纵隔板上方1/2出开插板口,横隔板下方1/2出开插板品以实现纵横拼插。内隔板两端设有吊耳,即可吊出上压内隔板。待上压内隔板全部调出后,再以同样方式吊出下置内隔板。移取底模上除去内隔板的制品砖入窑进行远红外辐射干热养护,24小时后脱模,推码养护28天,测试性能,出厂使用。
Claims (2)
1.一种泡沫混凝土承重砖,其原材料及重量配比为:
普通硅酸盐水泥 10-35%
生石灰(CaO≥60%) 5-10%
石膏 1-2%
粉煤灰渣(及砂) 40-65%
复合抗裂纤维HF-8 70-110g/m3
专用早强减水剂HFsm 水泥量0.5-1%
水料比 0.4~0.6
发泡稳泡剂HF-3 3-5kg/m3 。
2.如权利要求1所述的一种泡沫混凝土承重砖的生产方法,其特征是:
将水泥、粉煤灰渣、生石灰、石膏、粉煤灰渣(及砂)、复合抗裂纤维HF-8和专用早强减水剂HFsm,称量后加入搅拌机,干混1min,按0.45水料比计量加水、搅拌均匀,然后将发泡稳泡剂HF-3通过空压制泡系统制成微小泡沫加入搅拌机,快速搅拌使微泡均匀分布在浆体中,控制泡沫引入量,达到规定的料浆容重后,浇注入免切割成组模中,入窑进行远红外辐射干热养护,24小时后脱模,推码养护28天,测试性能,出厂使用。