CN103757878A - 抗紫外线衬衫的制造方法 - Google Patents

抗紫外线衬衫的制造方法 Download PDF

Info

Publication number
CN103757878A
CN103757878A CN201310604692.6A CN201310604692A CN103757878A CN 103757878 A CN103757878 A CN 103757878A CN 201310604692 A CN201310604692 A CN 201310604692A CN 103757878 A CN103757878 A CN 103757878A
Authority
CN
China
Prior art keywords
fabric
shirt
finishing agent
composite antibacterial
antibacterial finishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310604692.6A
Other languages
English (en)
Inventor
张高备
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU GUIZU LAOYANDOU GARMENT Co Ltd
Original Assignee
JIANGSU GUIZU LAOYANDOU GARMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU GUIZU LAOYANDOU GARMENT Co Ltd filed Critical JIANGSU GUIZU LAOYANDOU GARMENT Co Ltd
Priority to CN201310604692.6A priority Critical patent/CN103757878A/zh
Publication of CN103757878A publication Critical patent/CN103757878A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗紫外线衬衫的制造方法，包括如下步骤：1）对衬衫面料进行液氨处理；2）对面料进行预缩处理；3）制得复合抗菌整理剂；4）将面料在60-65℃下在含有50-55％复合抗菌整理剂的浸渍液中浸轧处理35-40分钟，压力1-2MPa，带液率73-75％，烘干后将面料在120-125℃恒温2-3小时；5）对处理后的面料进行烘干、裁剪、制衣；6）在120-125℃下整烫定型40-45分钟。本发明制备的衬衫有优良的防紫外作用，耐久性强，无毒安全。

Description

抗紫外线衬衫的制造方法
技术领域
本发明涉及抗紫外线衬衫的制造方法。
背景技术
目前常用的衬衫都具有防紫外作用，而现有的抗紫外线衬衫的耐久性都不理想。 
发明内容
本发明的目的在于提供一种抗紫外线衬衫的制造方法，其制备的衬衫有优良的防紫外作用，耐久性强，无毒安全。
为实现上述目的，本发明的技术方案是设计一种抗紫外线衬衫的制造方法，包括如下步骤：
1）对衬衫面料进行液氨处理；
2）对面料进行预缩处理，蒸汽压力为2.5-3.5MPa，蒸汽用量为40-45kg/h；
3）将1-2份羟乙基纤维素、10-12份2-羟基-4-甲氧基二苯甲酮、20-25份水杨酸-4-叔丁基苯基酯和7-8份沸石混合，然后同时缓慢加入2-3份甘油单硬脂酸酯、1-2份乙酸乙酯、50-55份二氧化钛、10-15份三氧化二铝和3-4份聚丙烯酸钠分散剂，30-35分钟内投料完毕，继续混合1-2小时，制得复合抗菌整理剂；
4）将面料在60-65℃下在含有50-55％复合抗菌整理剂的浸渍液中浸轧处理35-40分钟，压力1-2MPa，带液率73-75％，烘干后将面料在120-125℃恒温2-3小时；
5）对处理后的面料进行烘干、裁剪、制衣；
6）在120-125℃下整烫定型40-45分钟。 
本发明的优点和有益效果在于：提供一种抗紫外线衬衫的制造方法，其制备的衬衫有优良的防紫外作用，耐久性强，无毒安全。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种抗紫外线衬衫的制造方法，包括如下步骤：
1）对衬衫面料进行液氨处理；
2）对面料进行预缩处理，蒸汽压力为3.5MPa，蒸汽用量为45kg/h；
3）将2份羟乙基纤维素、12份2-羟基-4-甲氧基二苯甲酮、25份水杨酸-4-叔丁基苯基酯和8份沸石混合，然后同时缓慢加入3份甘油单硬脂酸酯、2份乙酸乙酯、55份二氧化钛、15份三氧化二铝和4份聚丙烯酸钠分散剂，35分钟内投料完毕，继续混合2小时，制得复合抗菌整理剂；
4）将面料在65℃下在含有55％复合抗菌整理剂的浸渍液中浸轧处理40分钟，压力2MPa，带液率75％，烘干后将面料在125℃恒温3小时；
5）对处理后的面料进行烘干、裁剪、制衣；
6）在125℃下整烫定型45分钟。
实施例2
一种抗紫外线衬衫的制造方法，包括如下步骤：
1）对衬衫面料进行液氨处理；
2）对面料进行预缩处理，蒸汽压力为2.5MPa，蒸汽用量为40kg/h；
3）将1份羟乙基纤维素、10份2-羟基-4-甲氧基二苯甲酮、20份水杨酸-4-叔丁基苯基酯和7份沸石混合，然后同时缓慢加入2份甘油单硬脂酸酯、1份乙酸乙酯、50份二氧化钛、10份三氧化二铝和3份聚丙烯酸钠分散剂，30分钟内投料完毕，继续混合1小时，制得复合抗菌整理剂；
4）将面料在60℃下在含有50％复合抗菌整理剂的浸渍液中浸轧处理35分钟，压力1MPa，带液率73％，烘干后将面料在120℃恒温2小时；
5）对处理后的面料进行烘干、裁剪、制衣；
6）在120℃下整烫定型40分钟。
实施例3
一种抗紫外线衬衫的制造方法，包括如下步骤：
1）对衬衫面料进行液氨处理；
2）对面料进行预缩处理，蒸汽压力为3MPa，蒸汽用量为41kg/h；
3）将1.2份羟乙基纤维素、11份2-羟基-4-甲氧基二苯甲酮、23份水杨酸-4-叔丁基苯基酯和7.8份沸石混合，然后同时缓慢加入2.3份甘油单硬脂酸酯、1.2份乙酸乙酯、54份二氧化钛、13份三氧化二铝和3.4份聚丙烯酸钠分散剂，32分钟内投料完毕，继续混合1.5小时，制得复合抗菌整理剂；
4）将面料在63℃下在含有54％复合抗菌整理剂的浸渍液中浸轧处理33分钟，压力1.2MPa，带液率74％，烘干后将面料在123℃恒温2.5小时；
5）对处理后的面料进行烘干、裁剪、制衣；
6）在123℃下整烫定型44分钟。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.抗紫外线衬衫的制造方法，其特征在于，包括如下步骤：
1）对衬衫面料进行液氨处理；
2）对面料进行预缩处理，蒸汽压力为2.5-3.5MPa，蒸汽用量为40-45kg/h；
3）将1-2份羟乙基纤维素、10-12份2-羟基-4-甲氧基二苯甲酮、20-25份水杨酸-4-叔丁基苯基酯和7-8份沸石混合，然后同时缓慢加入2-3份甘油单硬脂酸酯、1-2份乙酸乙酯、50-55份二氧化钛、10-15份三氧化二铝和3-4份聚丙烯酸钠分散剂，30-35分钟内投料完毕，继续混合1-2小时，制得复合抗菌整理剂；
4）将面料在60-65℃下在含有50-55％复合抗菌整理剂的浸渍液中浸轧处理35-40分钟，压力1-2MPa，带液率73-75％，烘干后将面料在120-125℃恒温2-3小时；
5）对处理后的面料进行烘干、裁剪、制衣；
6）在120-125℃下整烫定型40-45分钟。
CN201310604692.6A 2013-11-26 2013-11-26 抗紫外线衬衫的制造方法 Pending CN103757878A (zh)