CN103643489A - 抗紫外线全棉衬衫的制造方法 - Google Patents
抗紫外线全棉衬衫的制造方法 Download PDFInfo
- Publication number
- CN103643489A CN103643489A CN201310610136.XA CN201310610136A CN103643489A CN 103643489 A CN103643489 A CN 103643489A CN 201310610136 A CN201310610136 A CN 201310610136A CN 103643489 A CN103643489 A CN 103643489A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- cotton shirt
- ultraviolet
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗紫外线全棉衬衫的制造方法,包括如下步骤:1)对全棉衬衫面料进行液氨处理;2)将3-5份椰子油脂肪酸单乙醇酰胺、7-8份沸石、7-8份水杨酸-4-叔丁基苯基酯、8-9份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入2-3份乙烯基三甲氧基硅烷、3-4份聚丙烯酸钠、20-25份二氧化钛、30-35份三氧化二铝,30-35分钟内投料完毕,继续混合1-2小时,制得抗紫外线整理剂;3)将面料在含有45-50%抗紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率73-75%,烘干后将织物在130-135℃恒温30-35分钟;4)对处理后的面料进行烘干、裁剪、制衣;5)在160-165℃下整烫定型5-8分钟。本发明制造的全棉衬衫具有优良的防紫外功能,耐久性强,无毒安全。
Description
技术领域
本发明涉及抗紫外线全棉衬衫的制造方法。
背景技术
目前常用的抗紫外线全棉衬衫防紫外功能不理想,耐久性不强。
发明内容
本发明的目的在于提供一种抗紫外线全棉衬衫的制造方法,其制造的全棉衬衫具有优良的防紫外功能,耐久性强,无毒安全。
为实现上述目的,本发明的技术方案是设计一种抗紫外线全棉衬衫的制造方法,包括如下步骤:
1)对全棉衬衫面料进行液氨处理;
2)将3-5份椰子油脂肪酸单乙醇酰胺、7-8份沸石、7-8份水杨酸-4-叔丁基苯基酯、8-9份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入2-3份乙烯基三甲氧基硅烷、3-4份聚丙烯酸钠、20-25份二氧化钛、30-35份三氧化二铝,30-35分钟内投料完毕,继续混合1-2小时,制得抗紫外线整理剂;
3)将面料在含有45-50%抗紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率73-75%,烘干后将织物在130-135℃恒温30-35分钟;
4)对处理后的面料进行烘干、裁剪、制衣;
5)在160-165℃下整烫定型5-8分钟。
本发明的优点和有益效果在于:提供一种抗紫外线全棉衬衫的制造方法,其制造的全棉衬衫具有优良的防紫外功能,耐久性强,无毒安全。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种抗紫外线全棉衬衫的制造方法,包括如下步骤:
1)对全棉衬衫面料进行液氨处理;
2)将5份椰子油脂肪酸单乙醇酰胺、8份沸石、8份水杨酸-4-叔丁基苯基酯、9份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入3份乙烯基三甲氧基硅烷、4份聚丙烯酸钠、25份二氧化钛、35份三氧化二铝,35分钟内投料完毕,继续混合2小时,制得抗紫外线整理剂;
3)将面料在含有50%抗紫外线整理剂的浸渍液中浸轧处理,压力2MPa,带液率75%,烘干后将织物在135℃恒温35分钟;
4)对处理后的面料进行烘干、裁剪、制衣;
5)在165℃下整烫定型8分钟。
实施例2
一种抗紫外线全棉衬衫的制造方法,包括如下步骤:
1)对全棉衬衫面料进行液氨处理;
2)将3份椰子油脂肪酸单乙醇酰胺、7份沸石、7份水杨酸-4-叔丁基苯基酯、8份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入2份乙烯基三甲氧基硅烷、3份聚丙烯酸钠、20份二氧化钛、30份三氧化二铝,30分钟内投料完毕,继续混合1小时,制得抗紫外线整理剂;
3)将面料在含有45%抗紫外线整理剂的浸渍液中浸轧处理,压力1MPa,带液率73%,烘干后将织物在130℃恒温30分钟;
4)对处理后的面料进行烘干、裁剪、制衣;
5)在160℃下整烫定型5分钟。
实施例3
一种抗紫外线全棉衬衫的制造方法,包括如下步骤:
1)对全棉衬衫面料进行液氨处理;
2)将3.5份椰子油脂肪酸单乙醇酰胺、7.8份沸石、7.8份水杨酸-4-叔丁基苯基酯、8.9份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入2.3份乙烯基三甲氧基硅烷、3.4份聚丙烯酸钠、23份二氧化钛、34份三氧化二铝,32分钟内投料完毕,继续混合1.5小时,制得抗紫外线整理剂;
3)将面料在含有47%抗紫外线整理剂的浸渍液中浸轧处理,压力1.2MPa,带液率74%,烘干后将织物在132℃恒温33分钟;
4)对处理后的面料进行烘干、裁剪、制衣;
5)在164℃下整烫定型6分钟。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.抗紫外线全棉衬衫的制造方法,其特征在于,包括如下步骤:
1)对全棉衬衫面料进行液氨处理;
2)将3-5份椰子油脂肪酸单乙醇酰胺、7-8份沸石、7-8份水杨酸-4-叔丁基苯基酯、8-9份2-羟基-4-甲氧基二苯甲酮混合,然后同时缓慢加入2-3份乙烯基三甲氧基硅烷、3-4份聚丙烯酸钠、20-25份二氧化钛、30-35份三氧化二铝,30-35分钟内投料完毕,继续混合1-2小时,制得抗紫外线整理剂;
3)将面料在含有45-50%抗紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率73-75%,烘干后将织物在130-135℃恒温30-35分钟;
4)对处理后的面料进行烘干、裁剪、制衣;
5)在160-165℃下整烫定型5-8分钟。