CN104278529A - 抗皱面料的整理方法 - Google Patents

抗皱面料的整理方法 Download PDF

Info

Publication number
CN104278529A
CN104278529A CN201410552585.8A CN201410552585A CN104278529A CN 104278529 A CN104278529 A CN 104278529A CN 201410552585 A CN201410552585 A CN 201410552585A CN 104278529 A CN104278529 A CN 104278529A
Authority
CN
China
Prior art keywords
parts
fabric
maceration extract
hours
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410552585.8A
Other languages
English (en)
Inventor
钱永忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU ZONEJOY CLOTHING Co Ltd
Original Assignee
SUZHOU ZONEJOY CLOTHING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU ZONEJOY CLOTHING Co Ltd filed Critical SUZHOU ZONEJOY CLOTHING Co Ltd
Priority to CN201410552585.8A priority Critical patent/CN104278529A/zh
Publication of CN104278529A publication Critical patent/CN104278529A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗皱面料的整理方法，包括如下步骤：1）将1～2份脂肪醇聚氧乙烯醚、4～5份壳聚糖、1～2份三乙醇胺、1～2份氯化镁、8～9份水性聚氨酯混合，然后同时缓慢加入1～2份乙烯基三甲氧基硅烷、1～2份羟丙基甲基纤维素、2～3份1,2,3-丙烷三羧酸，35～40分钟内投料完毕，继续混合1～2小时，制得浸渍液；2）将面料在浸渍液中浸轧处理，压力1～2MPa，带液率60％～65％，烘干后将面料在135～140℃恒温1～2小时。本发明整理的面料具有优良的抗皱作用，耐久性强。

Description

抗皱面料的整理方法
技术领域
本发明涉及抗皱面料的整理方法。
背景技术
现有的面料抗皱性能不是很理想。 
发明内容
本发明的目的在于提供一种抗皱面料的整理方法，其整理的面料具有优良的抗皱作用，耐久性强。
为实现上述目的，本发明的技术方案是设计一种抗皱面料的整理方法，包括如下步骤：
1）将1～2份脂肪醇聚氧乙烯醚、4～5份壳聚糖、1～2份三乙醇胺、1～2份氯化镁、8～9份水性聚氨酯混合，然后同时缓慢加入1～2份乙烯基三甲氧基硅烷、1～2份羟丙基甲基纤维素、2～3份1,2,3-丙烷三羧酸，35～40分钟内投料完毕，继续混合1～2小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1～2MPa，带液率60％～65％，烘干后将面料在135～140℃恒温1～2小时。
优选的，抗皱面料的整理方法，包括如下步骤：
1）将1.2份脂肪醇聚氧乙烯醚、4.5份壳聚糖、1.2份三乙醇胺、1.2份氯化镁、8.9份水性聚氨酯混合，然后同时缓慢加入1.2份乙烯基三甲氧基硅烷、1.2份羟丙基甲基纤维素、2.3份1,2,3-丙烷三羧酸，37分钟内投料完毕，继续混合1.5小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1.2MPa，带液率64％，烘干后将面料在137℃恒温1.5小时。
优选的，抗皱面料的整理方法，包括如下步骤：
1）将2份脂肪醇聚氧乙烯醚、5份壳聚糖、2份三乙醇胺、2份氯化镁、9份水性聚氨酯混合，然后同时缓慢加入2份乙烯基三甲氧基硅烷、2份羟丙基甲基纤维素、3份1,2,3-丙烷三羧酸，40分钟内投料完毕，继续混合2小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力2MPa，带液率65％，烘干后将面料在140℃恒温2小时。
优选的，抗皱面料的整理方法，包括如下步骤：
1）将1份脂肪醇聚氧乙烯醚、4份壳聚糖、1份三乙醇胺、1份氯化镁、8份水性聚氨酯混合，然后同时缓慢加入1份乙烯基三甲氧基硅烷、1份羟丙基甲基纤维素、2份1,2,3-丙烷三羧酸，35分钟内投料完毕，继续混合1小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1MPa，带液率60％，烘干后将面料在135℃恒温1小时。
本发明的优点和有益效果在于：提供一种抗皱面料的整理方法，其整理的面料具有优良的抗皱作用，耐久性强。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
抗皱面料的整理方法，包括如下步骤：
1）将1.2份脂肪醇聚氧乙烯醚、4.5份壳聚糖、1.2份三乙醇胺、1.2份氯化镁、8.9份水性聚氨酯混合，然后同时缓慢加入1.2份乙烯基三甲氧基硅烷、1.2份羟丙基甲基纤维素、2.3份1,2,3-丙烷三羧酸，37分钟内投料完毕，继续混合1.5小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1.2MPa，带液率64％，烘干后将面料在137℃恒温1.5小时。
实施例2
抗皱面料的整理方法，包括如下步骤：
1）将2份脂肪醇聚氧乙烯醚、5份壳聚糖、2份三乙醇胺、2份氯化镁、9份水性聚氨酯混合，然后同时缓慢加入2份乙烯基三甲氧基硅烷、2份羟丙基甲基纤维素、3份1,2,3-丙烷三羧酸，40分钟内投料完毕，继续混合2小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力2MPa，带液率65％，烘干后将面料在140℃恒温2小时。
实施例3
抗皱面料的整理方法，包括如下步骤：
1）将1份脂肪醇聚氧乙烯醚、4份壳聚糖、1份三乙醇胺、1份氯化镁、8份水性聚氨酯混合，然后同时缓慢加入1份乙烯基三甲氧基硅烷、1份羟丙基甲基纤维素、2份1,2,3-丙烷三羧酸，35分钟内投料完毕，继续混合1小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1MPa，带液率60％，烘干后将面料在135℃恒温1小时。
 
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (4)

1.抗皱面料的整理方法，其特征在于，包括如下步骤：
1）将1～2份脂肪醇聚氧乙烯醚、4～5份壳聚糖、1～2份三乙醇胺、1～2份氯化镁、8～9份水性聚氨酯混合，然后同时缓慢加入1～2份乙烯基三甲氧基硅烷、1～2份羟丙基甲基纤维素、2～3份1,2,3-丙烷三羧酸，35～40分钟内投料完毕，继续混合1～2小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1～2MPa，带液率60％～65％，烘干后将面料在135～140℃恒温1～2小时。
2.根据权利要求1所述的抗皱面料的整理方法，其特征在于，包括如下步骤：
1）将1.2份脂肪醇聚氧乙烯醚、4.5份壳聚糖、1.2份三乙醇胺、1.2份氯化镁、8.9份水性聚氨酯混合，然后同时缓慢加入1.2份乙烯基三甲氧基硅烷、1.2份羟丙基甲基纤维素、2.3份1,2,3-丙烷三羧酸，37分钟内投料完毕，继续混合1.5小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1.2MPa，带液率64％，烘干后将面料在137℃恒温1.5小时。
3.根据权利要求1所述的抗皱面料的整理方法，其特征在于，包括如下步骤：
1）将2份脂肪醇聚氧乙烯醚、5份壳聚糖、2份三乙醇胺、2份氯化镁、9份水性聚氨酯混合，然后同时缓慢加入2份乙烯基三甲氧基硅烷、2份羟丙基甲基纤维素、3份1,2,3-丙烷三羧酸，40分钟内投料完毕，继续混合2小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力2MPa，带液率65％，烘干后将面料在140℃恒温2小时。
4.根据权利要求1所述的抗皱面料的整理方法，其特征在于，包括如下步骤：
1）将1份脂肪醇聚氧乙烯醚、4份壳聚糖、1份三乙醇胺、1份氯化镁、8份水性聚氨酯混合，然后同时缓慢加入1份乙烯基三甲氧基硅烷、1份羟丙基甲基纤维素、2份1,2,3-丙烷三羧酸，35分钟内投料完毕，继续混合1小时，制得浸渍液；
2）将面料在浸渍液中浸轧处理，压力1MPa，带液率60％，烘干后将面料在135℃恒温1小时。
CN201410552585.8A 2014-10-20 2014-10-20 抗皱面料的整理方法 Pending CN104278529A (zh)