CN102587136A - 一种纯棉布料的免烫处理工艺 - Google Patents
一种纯棉布料的免烫处理工艺 Download PDFInfo
- Publication number
- CN102587136A CN102587136A CN2011104552746A CN201110455274A CN102587136A CN 102587136 A CN102587136 A CN 102587136A CN 2011104552746 A CN2011104552746 A CN 2011104552746A CN 201110455274 A CN201110455274 A CN 201110455274A CN 102587136 A CN102587136 A CN 102587136A
- Authority
- CN
- China
- Prior art keywords
- cloth
- cotton cloth
- treatment process
- pure cotton
- ironing treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种纯棉布料的免烫处理工艺,将纯棉布料浸轧到防皱整理液中,使其完全浸透,控制时间在20~50min,取出布料进行脱水,使布料带液率控制在50~70%,脱水得到的防皱整理液回收继续使用,将脱水后的布料采用转鼓烘干,重复操作3~5次,高温170~220℃压烫30~60s,然后在110~130℃下烘焙4~20min,得到成品。所述的防皱整理液为乙二醛5~15g/L,戊二醛5~15g/L,酒石酸0.1~1g/L,MgCl2催化剂15~25g/L,其余为20%的淀粉溶液。本工艺采用乙二醛与戊二醛混合整理剂取代传统的树脂整理剂,从而不会引入甲醛,使得产物更环保,安全;高温短时间压烫,使布料快速定型,同时在防皱整理液中添加酒石酸,可以有效改善高温压烫布料泛黄的问题。
Description
技术领域
本发明涉及一种布料处理方法,特别涉及一种纯棉布料的免烫处理方法。
背景技术
目前随着都市生活节奏的加快,越来越多的上班族选择购买免烫衬衫,不再为每天要熨烫衬衫而烦恼,目前市售的免烫衬衫主要是在其后整理过程中使用树脂整理剂进行处理,以提高其产品的防皱防缩效果,但是生产成本很高,通常所用树脂整理剂中含有一定量的甲醛,则在织物整理、服装制作、仓库贮存和穿着过程中都会释放出甲醛。甲醛是一种有毒的化学品,一种皮肤刺激剂和过敏剂,可剧烈刺激眼睛、皮肤和黏膜。另外,免烫衬衫大都不是纯棉面料,因为纯棉布料的湿膨胀性较高,且在湿态与干态下得弹性回复力较低,因为很容易起皱和变形,通常免烫衬衫都会添加涤棉,随着现在消费者对纯棉衣物的喜爱,急需开发一种纯棉布料的免烫工艺,现在的纯棉免烫其实就是纯棉涂了一层硅胶的东西,穿起来不舒服,没棉的亲切感,并且不易烫平。
发明内容
技术问题:本发明针对上述技术问题,提供一种纯棉布料的免烫处理方法,采用乙二醛与戊二醛混合整理剂,以酒石酸为添加剂,可以有效改善泛黄的问题,在催化剂作用下进行免烫处理。
技术方案:一种纯棉布料的免烫处理工艺,将纯棉布料浸轧到防皱整理液中,使其完全浸透,控制时间在20~50min,取出布料进行脱水,使布料带液率控制在50~70%,脱水得到的防皱整理液回收继续使用,将脱水后的布料采用转鼓烘干,重复操作3~5次,高温170~220℃压烫30~60s,然后在110~130℃下烘焙4~20min,得到成品。
所述的防皱整理液为乙二醛5~15g/L,戊二醛5~15g/L,酒石酸0.1~1g/L,MgCl2催化剂15~25g/L,其余为20%的淀粉溶液。
所述的防皱整理液中乙二醇与戊二醇的摩尔比为1:3~3:1。
有益效果:本发明一种纯棉布料的免烫处理方法,具有如下优点:
(1)、采用乙二醛与戊二醛混合整理剂取代传统的树脂整理剂,从而不会引入甲醛,使得产物更环保,安全。
(2)、采用高温短时间压烫,使布料快速定型,同时在防皱整理液中添加酒石酸,可以有效改善高温压烫布料泛黄的问题。
(3)、在防皱整理液中加入戊二醛,不仅能够增强防皱效果,还能一步对布料进行初步杀菌。
具体实施方式
实施例1:
一种纯棉布料的免烫处理工艺,将纯棉布料浸轧到防皱整理液中,使其完全浸透,控制时间在20min,取出布料进行脱水,使布料带液率控制在50%,脱水得到的防皱整理液回收继续使用,将脱水后的布料采用转鼓烘干,重复操作3次,高温170℃压烫60s,然后在110℃下烘焙4min,得到成品。防皱整理液为乙二醛5g/L,戊二醛15g/L,酒石酸0.1g/L,MgCl2催化剂15g/L,其余为20%的淀粉溶液。
实施例2:
一种纯棉布料的免烫处理工艺,将纯棉布料浸轧到防皱整理液中,使其完全浸透,控制时间在50min,取出布料进行脱水,使布料带液率控制在70%,脱水得到的防皱整理液回收继续使用,将脱水后的布料采用转鼓烘干,重复操作5次,高温220℃压烫30s,然后在130℃下烘焙20min,得到成品。防皱整理液为乙二醛15g/L,戊二醛5g/L,酒石酸1g/L,MgCl2催化剂25g/L,其余为20%的淀粉溶液。
Claims (3)
1.一种纯棉布料的免烫处理工艺,其特征在于:将纯棉布料浸轧到防皱整理液中,使其完全浸透,控制时间在20~50min,取出布料进行脱水,使布料带液率控制在50~70%,脱水得到的防皱整理液回收继续使用,将脱水后的布料采用转鼓烘干,重复操作3~5次,高温170~220℃压烫30~60s,然后在110~130℃下烘焙4~20min,得到成品。
2.根据权利要求1所述的一种纯棉布料的免烫处理工艺,其特征在于:所述的防皱整理液为乙二醛5~15g/L,戊二醛5~15g/L,酒石酸0.1~1g/L,MgCl2催化剂15~25g/L,其余为20%的淀粉溶液。
3.根据权利要求1所述的一种纯棉布料的免烫处理工艺,其特征在于:所述的防皱整理液中乙二醇与戊二醇的摩尔比为1:3~3:1。