CN103628311A - 一种羊毛织物的耐久定型整理工艺 - Google Patents
一种羊毛织物的耐久定型整理工艺 Download PDFInfo
- Publication number
- CN103628311A CN103628311A CN201310592721.1A CN201310592721A CN103628311A CN 103628311 A CN103628311 A CN 103628311A CN 201310592721 A CN201310592721 A CN 201310592721A CN 103628311 A CN103628311 A CN 103628311A
- Authority
- CN
- China
- Prior art keywords
- finishing
- wool fabric
- minutes
- padding
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种羊毛织物的耐久定型整理工艺,首先为浸轧工序,采用80~100g/L的2D树脂整理剂、1~3g/L渗透剂、20~50g/L柔软剂和10~15g/L催化剂组成的整理液在室温下进行浸轧,所述浸轧整理工序采用二浸二轧,轧液率为70~80%;其次进行对折、重锤加压;而后在80~90℃下预烘3~5分钟;然后在120~160℃下焙烘60~90秒;再后在90~100℃下汽蒸8~10分钟;最后烘干、落布。经本发明提供的整理工艺处理后的羊毛织物,具有优良的洗可穿效果,突出的回弹性和耐久压烫性能;被整理的织物手感丰满,挺括、厚实,无色变和褪色现象。
Description
技术领域
本发明涉及一种织物的整理工艺,特别是涉及一种羊毛织物的耐久定型整理工艺。
背景技术
由于羊毛织物具有手感柔软,保暖性、弹性好,穿着舒适等优点,其高档服饰备受消费者青睐。目前消费市场要求羊毛针织服饰具有更好的免烫和褶裥持久等功能。现有的对于羊毛织物的耐久压烫整理一般采用还原体系整理剂,但是这种整理方法存在使织物变色和褪色的现象,不适用于有色织物的整理。
发明内容
本发明的目的是提供一种羊毛织物的耐久定型整理工艺。
本发明要解决的是现有羊毛织物的耐久定型整理方法中存在的工序复杂、整理效果不佳的缺陷。
本发明的技术方案是:一种羊毛织物的耐久定型整理工艺,所述整理工艺至少包括如下步骤:首先为浸轧工序,采用80~100g/L的2D树脂整理剂、1~3g/L渗透剂、20~50g/L柔软剂和10~15g/L催化剂组成的整理液进行浸轧,所述浸轧整理工序采用二浸二轧,所述浸轧工序轧液率为70~80%,所述浸轧在室温下进行;其次进行对折、重锤加压;而后在80~90℃下预烘3~5分钟;然后在120~160℃下焙烘60~90秒;再后在90~100℃下汽蒸8~10分钟;最后烘干、落布。
所述柔软剂为咪唑啉类柔软剂;所述催化剂为氯化镁、氯化锌、硝酸锌、氯化铝中的一种。
本发明产生的有益效果是:经本发明提供的整理工艺处理后的羊毛织物,具有优良的洗可穿效果,突出的回弹性和耐久压烫性能;同时,被整理的织物手感丰满,挺括、厚实,无色变和褪色现象。
具体实施方式
下面结合实施例对本发明作进一步说明。
一种羊毛织物的耐久定型整理工艺,所述整理工艺至少包括如下步骤:首先为浸轧工序,采用100g/L的2D树脂整理剂、1g/L渗透剂、20g/L咪唑啉类柔软剂和10g/L氯化镁组成的整理液进行浸轧,所述浸轧整理工序采用二浸二轧,所述浸轧工序轧液率为80%,所述浸轧在室温下进行;其次进行对折、重锤加压;而后在90℃下预烘3分钟;然后在160℃下焙烘60秒;再后在90℃下汽蒸10分钟;最后烘干、落布。
Claims (2)
1.一种羊毛织物的耐久定型整理工艺,其特征在于所述整理工艺至少包括如下步骤:首先为浸轧工序,采用80~100g/L的2D树脂整理剂、1~3g/L渗透剂、20~50g/L柔软剂和10~15g/L催化剂组成的整理液进行浸轧,所述浸轧整理工序采用二浸二轧,所述浸轧工序轧液率为70~80%,所述浸轧在室温下进行;其次进行对折、重锤加压;而后在80~90℃下预烘3~5分钟;然后在120~160℃下焙烘60~90秒;再后在90~100℃下汽蒸8~10分钟;最后烘干、落布。
2.如权利要求1所述的一种羊毛织物的耐久定型整理工艺,其特征在于所述柔软剂为咪唑啉类柔软剂;所述催化剂为氯化镁、氯化锌、硝酸锌、氯化铝中的一种。