CN103643513A - 纯棉布料的免烫处理方法 - Google Patents

纯棉布料的免烫处理方法 Download PDF

Info

Publication number
CN103643513A
CN103643513A CN201310638517.9A CN201310638517A CN103643513A CN 103643513 A CN103643513 A CN 103643513A CN 201310638517 A CN201310638517 A CN 201310638517A CN 103643513 A CN103643513 A CN 103643513A
Authority
CN
China
Prior art keywords
cotton cloth
parts
mass
purified cotton
pure cotton
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310638517.9A
Other languages
English (en)
Inventor
苏国华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU BOSBANI FASHION Co Ltd
Original Assignee
JIANGSU BOSBANI FASHION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU BOSBANI FASHION Co Ltd filed Critical JIANGSU BOSBANI FASHION Co Ltd
Priority to CN201310638517.9A priority Critical patent/CN103643513A/zh
Publication of CN103643513A publication Critical patent/CN103643513A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种纯棉布料的免烫处理方法，包括如下步骤：1）取1-2质量份十二烷基三甲基氯化铵、2-3质量份酒石酸、1-2质量份羟乙基纤维素、25-30质量份淀粉溶液、15-18质量份戊二醛、14-17质量份乙二醛，25-30质量份氯化镁混合，制备防皱整理剂；2）将纯棉布料在含有65-70％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧45-50分钟；3）取出后脱水，控制纯棉布料带液率在35-40%，将脱水后的纯棉布料采用转鼓烘干；4）再将纯棉布料在含有55-60％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧35-40分钟；5）取出后脱水，控制纯棉布料带液率在25-30%，将脱水后的纯棉布料采用转鼓烘干；6）在225-230℃压烫15-20秒；7）在140-145℃恒温7-9分钟。本发明不会释放甲醛，更环保，安全。

Description

纯棉布料的免烫处理方法
技术领域
本发明涉及纯棉布料的免烫处理方法。
背景技术
目前市售的免烫衬衫主要是在其后整理过程中使用树脂整理剂进行处理，通常所用树脂整理剂中含有一定量的甲醛，会在织物整理、服装制作、穿着过程中都会释放出甲醛。 
发明内容
本发明的目的在于提供一种纯棉布料的免烫处理方法，其不会释放甲醛，更环保，安全。
为实现上述目的，本发明的技术方案是设计一种纯棉布料的免烫处理方法，包括如下步骤：
1）取1-2质量份十二烷基三甲基氯化铵、2-3质量份酒石酸、1-2质量份羟乙基纤维素、25-30质量份淀粉溶液、15-18质量份戊二醛、14-17质量份乙二醛，25-30质量份氯化镁混合，制备防皱整理剂；
2）将纯棉布料在含有65-70％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧45-50分钟；
3）取出后脱水，控制纯棉布料带液率在35-40%，将脱水后的纯棉布料采用转鼓烘干；
4）再将纯棉布料在含有55-60％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧35-40分钟；
5）取出后脱水，控制纯棉布料带液率在25-30%，将脱水后的纯棉布料采用转鼓烘干；
6）在225-230℃压烫15-20秒；
7）在140-145℃恒温7-9分钟。 
本发明的优点和有益效果在于：提供一种纯棉布料的免烫处理方法，其不会释放甲醛，更环保，安全。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种纯棉布料的免烫处理方法，包括如下步骤：
1）取2质量份十二烷基三甲基氯化铵、3质量份酒石酸、2质量份羟乙基纤维素、30质量份淀粉溶液、18质量份戊二醛、17质量份乙二醛，30质量份氯化镁混合，制备防皱整理剂；
2）将纯棉布料在含有70％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧50分钟；
3）取出后脱水，控制纯棉布料带液率在40%，将脱水后的纯棉布料采用转鼓烘干；
4）再将纯棉布料在含有60％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧40分钟；
5）取出后脱水，控制纯棉布料带液率在30%，将脱水后的纯棉布料采用转鼓烘干；
6）在230℃压烫20秒；
7）在145℃恒温9分钟。
实施例2
一种纯棉布料的免烫处理方法，包括如下步骤：
1）取1质量份十二烷基三甲基氯化铵、2质量份酒石酸、1质量份羟乙基纤维素、25质量份淀粉溶液、15质量份戊二醛、14质量份乙二醛，25质量份氯化镁混合，制备防皱整理剂；
2）将纯棉布料在含有65％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧45分钟；
3）取出后脱水，控制纯棉布料带液率在35%，将脱水后的纯棉布料采用转鼓烘干；
4）再将纯棉布料在含有55％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧35分钟；
5）取出后脱水，控制纯棉布料带液率在25%，将脱水后的纯棉布料采用转鼓烘干；
6）在225℃压烫15秒；
7）在140℃恒温7分钟。
实施例3
一种纯棉布料的免烫处理方法，包括如下步骤：
1）取1.2质量份十二烷基三甲基氯化铵、2.3质量份酒石酸、1.2质量份羟乙基纤维素、28质量份淀粉溶液、17质量份戊二醛、16质量份乙二醛，28质量份氯化镁混合，制备防皱整理剂；
2）将纯棉布料在含有68％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧48分钟；
3）取出后脱水，控制纯棉布料带液率在37%，将脱水后的纯棉布料采用转鼓烘干；
4）再将纯棉布料在含有58％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧36分钟；
5）取出后脱水，控制纯棉布料带液率在28%，将脱水后的纯棉布料采用转鼓烘干；
6）在228℃压烫18秒；
7）在143℃恒温8分钟。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.纯棉布料的免烫处理方法，其特征在于，包括如下步骤：
1）取1-2质量份十二烷基三甲基氯化铵、2-3质量份酒石酸、1-2质量份羟乙基纤维素、25-30质量份淀粉溶液、15-18质量份戊二醛、14-17质量份乙二醛，25-30质量份氯化镁混合，制备防皱整理剂；
2）将纯棉布料在含有65-70％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧45-50分钟；
3）取出后脱水，控制纯棉布料带液率在35-40%，将脱水后的纯棉布料采用转鼓烘干；
4）再将纯棉布料在含有55-60％防皱整理剂的浸渍液中浸轧处理，浴比为1:7，浸轧35-40分钟；
5）取出后脱水，控制纯棉布料带液率在25-30%，将脱水后的纯棉布料采用转鼓烘干；
6）在225-230℃压烫15-20秒；
7）在140-145℃恒温7-9分钟。
CN201310638517.9A 2013-12-04 2013-12-04 纯棉布料的免烫处理方法 Pending CN103643513A (zh)