CN102828398A - 保暖衬衫的生产方法 - Google Patents

保暖衬衫的生产方法 Download PDF

Info

Publication number
CN102828398A
CN102828398A CN2012103489275A CN201210348927A CN102828398A CN 102828398 A CN102828398 A CN 102828398A CN 2012103489275 A CN2012103489275 A CN 2012103489275A CN 201210348927 A CN201210348927 A CN 201210348927A CN 102828398 A CN102828398 A CN 102828398A
Authority
CN
China
Prior art keywords
warming
parts
production method
finishing agent
shirt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103489275A
Other languages
English (en)
Inventor
解吉平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Original Assignee
KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY filed Critical KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Priority to CN2012103489275A priority Critical patent/CN102828398A/zh
Publication of CN102828398A publication Critical patent/CN102828398A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种保暖衬衫的生产方法，包括如下步骤：对全棉精纺面料进行液氨处理；用预缩机对面料进行预缩处理；将面料在含有保暖整理剂的浸渍液中浸轧处理；对处理后的面料进行烘干、裁剪、制衣；采用烘培定型机整烫定型；所述保暖整理剂由如下重量份的组分组成：海藻碳纤维60-75份、二氧化钛10-15份、氧化镁10-20份、麦饭石10-15份、氧化锌2-5份、硅烷偶联剂2-5份、聚丙烯酸钠分散剂0.5-1.0份，并加水配成质量浓度为15-40％的浸轧液。本发明保暖衬衫不仅具有优异的保暖功能，还可增强细胞能量，增强细胞的功能和活力等作用。耐久性强，经多次洗涤后仍可基本保持原有性能。

Description

保暖衬衫的生产方法
技术领域
本发明涉及一种保暖衬衫的生产方法。
背景技术
随着生活水平的不断提高，人们对衣物的功能性要求越来越高，尤其对内衣的选择不仅注重柔软舒适，更注重健康、保健功能。传统的保暖衬衫通常采用加厚设计，虽然保暖性好，但存在衣物过于厚重、舒适性和透气性差等问题。现有的保暖衬衫面料耐久性差，多次水洗后保暖效果大大减弱。因此，开发一种即无毒安全、又具有优异耐久性的保暖衬衫成为重要的研究课题。
发明内容
本发明要解决的技术问题是提供一种保暖衬衫的生产方法，以克服现有技术存在的上述缺陷。
为解决上述技术问题，本发明保暖衬衫的生产方法，包括如下步骤：
1)对全棉精纺面料进行液氨处理；
2)用预缩机对面料进行预缩处理，蒸汽压力为2-3kg/m2，蒸汽用量为50-70kg/h；
3)将面料在含有保暖整理剂的浸渍液中浸轧处理，压力1.5-2kg/cm2，带液率60-70％；
4)对处理后的面料进行烘干、裁剪、制衣；
5)采用烘培定型机在140-150℃下整烫定型10-20分钟；
所述保暖整理剂由如下重量份的组分组成：
海藻碳纤维        60-75份、
二氧化钛            10-15份、
氧化镁              10-20份、
麦饭石              10-15份、
氧化锌              2-5份、
硅烷偶联剂          2-5份、
聚丙烯酸钠分散剂    0.5-1.0份，
并加水配成质量浓度为15-40％的浸轧液。
所述全棉精纺面料为120支的高精密全棉纱织面料。
所述聚丙烯酸钠分散剂优选粘度200-300mPa·s。
保暖整理剂可采用一般的混合方法。
保暖整理剂优选配成质量含量30-40％的浸渍液。
本发明保暖衬衫中的海藻碳纤维具有吸收远红外的功能，远红外不仅具有优异的保暖功能，还可以使细胞活化，使老死细胞排泄或赋予再生能力，可增强细胞能量，增强细胞的功能和活力等作用。本发明保暖衬衫保暖、保健效果优异，且耐久性强，经多次洗涤后仍可基本保持原有性能。
具体实施方式
实施例1
保暖整理剂的制备：
海藻碳纤维        75份、
二氧化钛          10份、
氧化镁            10份、
麦饭石            10份、
氧化锌            2份、
硅烷偶联剂        2份、
聚丙烯酸钠分散剂  0.5份，
将上述组分混合后加水配成质量浓度为15％的浸轧液。
保暖衬衫的生产：
1)对全棉精纺面料进行液氨处理；
2)用预缩机对面料进行预缩处理，蒸汽压力为2kg/m2，蒸汽用量为50kg/h；
3)将面料在含有保暖整理剂的浸渍液中浸轧处理，压力1.5kg/cm2，带液率60％；
4)对处理后的面料进行烘干、裁剪、制衣；
5)采用烘培定型机在140℃下整烫定型20分钟。
实施例2
保暖整理剂的制备：
海藻碳纤维        60份、
二氧化钛          15份、
氧化镁            20份、
麦饭石            15份、
氧化锌            5份、
硅烷偶联剂        5份、
聚丙烯酸钠分散剂  1.0份，
将上述组分混合后加水配成质量浓度为40％的浸轧液。
保暖衬衫的生产：
1)对全棉精纺面料进行液氨处理；
2)用预缩机对面料进行预缩处理，蒸汽压力为3kg/m2，蒸汽用量为70kg/h；
3)将面料在含有保暖整理剂的浸渍液中浸轧处理，压力2kg/cm2，带液率70％；
4)对处理后的面料进行烘干、裁剪、制衣；
5)采用烘培定型机在150℃下整烫定型10分钟。

Claims (4)

1.保暖衬衫的生产方法，其特征在于，包括如下步骤：
1)对全棉精纺面料进行液氨处理；
2)用预缩机对面料进行预缩处理，蒸汽压力为2-3kg/m2，蒸汽用量为50-70kg/h；
3)将面料在含有保暖整理剂的浸渍液中浸轧处理，压力1.5-2kg/cm2，带液率60-70％；
4)对处理后的面料进行烘干、裁剪、制衣；
5)采用烘培定型机在140-150℃下整烫定型10-20分钟；
所述保暖整理剂由如下重量份的组分组成：
海藻碳纤维          60-75份、
二氧化钛            10-15份、
氧化镁              10-20份、
麦饭石              10-15份、
氧化锌              2-5份、
硅烷偶联剂          2-5份、
聚丙烯酸钠分散剂    0.5-1.0份，
并加水配成质量浓度为15-40％的浸轧液。
2.根据权利要求1所述的保暖衬衫的生产方法，其特征在于，所述全棉精纺面料为120支的高精密全棉纱织面料。
3.根据权利要求1所述的保暖衬衫的生产方法，其特征在于，所述保暖整理剂配成质量含量30-40％的浸渍液。
4.根据权利要求1所述的保暖衬衫的生产方法，其特征在于，所述聚丙烯酸钠分散剂粘度为200-300mPa·s。
CN2012103489275A 2012-09-19 2012-09-19 保暖衬衫的生产方法 Pending CN102828398A (zh)