CN103755974A - 一种木质素改性聚酯多元醇的制备方法 - Google Patents

一种木质素改性聚酯多元醇的制备方法 Download PDF

Info

Publication number
CN103755974A
CN103755974A CN201410032945.1A CN201410032945A CN103755974A CN 103755974 A CN103755974 A CN 103755974A CN 201410032945 A CN201410032945 A CN 201410032945A CN 103755974 A CN103755974 A CN 103755974A
Authority
CN
China
Prior art keywords
polyester polyol
reactor
parts
preparation
calcium lignin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410032945.1A
Other languages
English (en)
Inventor
单成敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410032945.1A priority Critical patent/CN103755974A/zh
Publication of CN103755974A publication Critical patent/CN103755974A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种木质素改性聚酯多元醇的制备方法，包括以下步骤：1)将以下重量份数的原料投入反应器：木质素磺酸钙30-120，水20-150，纤维素酶0.5-10，氢氧化钠0.5-3，糠醇0.1-50；之后将反应器升温至30-65℃，制得酶解改性木质素磺酸钙；2)将经过步骤1)制得的酶解改性木质素磺酸钙及笨酚、甲醛、尿素、糠醛、氢氧化钠、三聚氢胺按以下重量份数投入反应器；制得酚化木质素磺酸钙；3)将经过步骤2)制得的酚化木质素磺酸钙及废塑料、季戊四醇、二甘醇、丙三醇、醋酸锑、乙二胺按以下重量份数投入反应器；加热至190-220℃，常压搅拌反应3-6小时，制得木质素改性聚酯多元醇。本发明的木质素改性聚酯多元醇的制备方法步骤简单，所制备的木质素改性聚酯多元醇性能稳定。

Description

一种木质素改性聚酯多元醇的制备方法
技术领域
本发明涉及一种木质素改性聚酯多元醇的制备方法。
背景技术
目前市场上泡沫板材使用比较广泛，而现有市场上的泡沫板大都采用聚氨脂材料制成，生产出的泡沫板放置一段时间后都会产生收缩现象，极易变形，使用寿命短，保温性能差，强度低；因此急需一种替代原料；聚酯多元醇作为一种有机物具有很好的物理性能，稳定性好，具有很好的机械强度，能够用来制作泡沫板材，因此急需一种木质素改性聚酯多元醇的制备方法。
发明内容
为解决上述技术问题，本发明提供一种木质素改性聚酯多元醇的制备方法，工艺简单，采用废塑料、季戊四醇、二甘醇、丙三醇制成，性能稳定。
本发明的木质素改性聚酯多元醇的制备方法，包括以下步骤：
1)将以下重量份数的原料投入反应器：木质素磺酸钙30-120，水20-150，纤维素酶0.5-10，氢氧化钠0.5-3，糠醇0.1-50；之后将反应器升温至30-65℃，搅拌反应2-6小时，制得酶解改性木质素磺酸钙；
2)将经过步骤1)制得的酶解改性木质素磺酸钙及笨酚、甲醛、尿素、糠醛、氢氧化钠、三聚氢胺按以下重量份数投入反应器：酶解改性木质素磺酸钙30-120，笨酚3-45，甲醛1-30，尿素3-19，糠醛4-23，氢氧化钠0-3，三聚氢胺1-16；搅拌加热至65-90℃，使其达到酚化、甲阶化、接枝共聚的效果，制得酚化木质素磺酸钙；
3)将经过步骤2)制得的酚化木质素磺酸钙及废塑料、季戊四醇、二甘醇、丙三醇、醋酸锑、乙二胺按以下重量份数投入反应器：酚化木质素磺酸钙20-100，废塑料37-150，季戊四醇11-29，二甘醇13-38，丙三醇9-31，醋酸锑0-3，乙二胺0-7；加热至190-220℃，常压搅拌反应3-6小时，使物料进行螯合、接枝、共聚，制得木质素改性聚酯多元醇。
本发明的木质素改性聚酯多元醇的制备方法，在步骤3)中：所述废塑料由废涤沦、废尼龙、废塑料瓶破碎加工而成。
与现有技术相比本发明的有益效果为：本发明的木质素改性聚酯多元醇的制备方法步骤简单，首先由木质素磺酸钙制备酶解改性木质素磺酸钙，然后制备酚化木质素磺酸钙，最后制成木质素改性聚酯多元醇，能够充分利用废塑料，环保节能，所制备的木质素改性聚酯多元醇性能稳定，适宜作为制作泡沫板材的原材料。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明，但不用来限制本发明的范围。
一种木质素改性聚酯多元醇的制备方法，包括以下步骤：
1)将以下重量份数的原料投入反应器：木质素磺酸钙30-120，水20-150，纤维素酶0.5-10，氢氧化钠0.5-3，糠醇0.1-50；之后将反应器升温至30-65℃，搅拌反应2-6小时，制得酶解改性木质素磺酸钙；
2)将经过步骤1)制得的酶解改性木质素磺酸钙及笨酚、甲醛、尿素、糠醛、氢氧化钠、三聚氢胺按以下重量份数投入反应器：酶解改性木质素磺酸钙30-120，笨酚3-45，甲醛1-30，尿素3-19，糠醛4-23，氢氧化钠0-3，三聚氢胺1-16；搅拌加热至65-90℃，使其达到酚化、甲阶化、接枝共聚的效果，制得酚化木质素磺酸钙；
3)将经过步骤2)制得的酚化木质素磺酸钙及废塑料、季戊四醇、二甘醇、丙三醇、醋酸锑、乙二胺按以下重量份数投入反应器：酚化木质素磺酸钙20-100，废塑料37-150，季戊四醇11-29，二甘醇13-38，丙三醇9-31，醋酸锑0-3，乙二胺0-7；加热至190-220℃，常压搅拌反应3-6小时，使物料进行螯合、接枝、共聚，制得木质素改性聚酯多元醇。
本发明的木质素改性聚酯多元醇的制备方法，在步骤3)中：所述废塑料由废涤沦、废尼龙、废塑料瓶破碎加工而成。
本发明的木质素改性聚酯多元醇的制备方法步骤简单，首先由木质素磺酸钙制备酶解改性木质素磺酸钙，然后制备酚化木质素磺酸钙，最后制成木质素改性聚酯多元醇，能够充分利用废塑料，环保节能，所制备的木质素改性聚酯多元醇性能稳定，适宜作为制作泡沫板材的原材料。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本发明的保护范围。

Claims (2)

1.一种木质素改性聚酯多元醇的制备方法，其特征在于，包括以下步骤：
1)将以下重量份数的原料投入反应器：木质素磺酸钙30-120，水20-150，纤维素酶0.5-10，氢氧化钠0.5-3，糠醇0.1-50；之后将反应器升温至30-65℃，搅拌反应2-6小时，制得酶解改性木质素磺酸钙；
2)将经过步骤1)制得的酶解改性木质素磺酸钙及笨酚、甲醛、尿素、糠醛、氢氧化钠、三聚氢胺按以下重量份数投入反应器：酶解改性木质素磺酸钙30-120，笨酚3-45，甲醛1-30，尿素3-19，糠醛4-23，氢氧化钠0-3，三聚氢胺1-16；搅拌加热至65-90℃，使其达到酚化、甲阶化、接枝共聚的效果，制得酚化木质素磺酸钙；
3)将经过步骤2)制得的酚化木质素磺酸钙及废塑料、季戊四醇、二甘醇、丙三醇、醋酸锑、乙二胺按以下重量份数投入反应器：酚化木质素磺酸钙20-100，废塑料37-150，季戊四醇11-29，二甘醇13-38，丙三醇9-31，醋酸锑0-3，乙二胺0-7；加热至190-220℃，常压搅拌反应3-6小时，使物料进行螯合、接枝、共聚，制得木质素改性聚酯多元醇。
2.根据权利要求1所述的木质素改性聚酯多元醇的制备方法，其特征在于，在步骤3)中：所述废塑料由废涤沦、废尼龙、废塑料瓶破碎加工而成。
CN201410032945.1A 2014-01-23 2014-01-23 一种木质素改性聚酯多元醇的制备方法 Pending CN103755974A (zh)