CN103740246A - 一种有机导电涂料及其制备方法 - Google Patents
一种有机导电涂料及其制备方法 Download PDFInfo
- Publication number
- CN103740246A CN103740246A CN201310746709.1A CN201310746709A CN103740246A CN 103740246 A CN103740246 A CN 103740246A CN 201310746709 A CN201310746709 A CN 201310746709A CN 103740246 A CN103740246 A CN 103740246A
- Authority
- CN
- China
- Prior art keywords
- parts
- organic conductive
- oxide
- conductive coating
- titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供了一种有机导电涂料及其制备方法,其中有机导电涂料以重量份计包括:石墨8~15份,二氧化钛1~6份,三氧化二锑0.05~0.15份,氧化镁0.3~1.2份,氧化铅0.5~1.8份,三氧化二钛1~5份,醇酸树脂10~30份,硅油0.2~0.8份,二甲苯0.05~0.12份,环氧树脂0.1~0.8份,碳酸钡0.3~0.7份。其制备方法为先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。本发明提供的有机导电涂料,附着力可达98%以上,优于同类产品,而且具有良好的导电性能,电阻小于60Ω。
Description
技术领域
本发明属于涂料技术领域,具体涉及一种有机导电涂料及其制备方法。
背景技术
导电涂料作为一种液体涂料,可以方便地喷涂或刷涂于各种形状的材料表面,形成电磁屏蔽导电层,从而使材料达到屏蔽电磁波的目的。导电涂料具有成本低廉、工艺简单、施工方便、应用范围广以及屏蔽电磁波效果好等特点,获得广泛应用。导电涂料是防静电涂料的一种特例,通常含有大量铜粉或炭黑、镍粉、铝粉、钼粉、银粉等金属粉。目前,大多数采用的塑料表面的导电涂料集中在溶剂型导电涂料,而溶剂型导电涂料在使用过程中会挥发吃大量的有害物质,对环境和人们的健康造成有害影响。而水性涂料又存在着附着力不强的问题,会导致涂膜碎片落入机壳内线路板造成短路。
发明内容
本发明的目的是提供一种有机导电涂料,其附着力可达98%以上,而且具有良好的导电性能,电阻小于60Ω。
一种有机导电涂料,以重量份计包括:石墨8~15份,二氧化钛1~6份,三氧化二锑0.05~0.15份,氧化镁0.3~1.2份,氧化铅0.5~1.8份,三氧化二钛1~5份,醇酸树脂10~30份,硅油0.2~0.8份,二甲苯0.05~0.12份,环氧树脂0.1~0.8份,碳酸钡0.3~0.7份。
进一步优选,上述有机导电涂料,以重量份计包括:石墨10~12份,二氧化钛2~5份,三氧化二锑0.08~0.12份,氧化镁0.6~1.1份,氧化铅0.8~1.4份,三氧化二钛2~4份,醇酸树脂15~22份,硅油0.3~0.7份,二甲苯0.07~0.1份,环氧树脂0.3~0.6份,碳酸钡0.4~0.6份。
上述有机导电涂料的制备方法,包括以下步骤:先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
本发明提供的有机导电涂料,附着力可达98%以上,优于同类产品,而且具有良好的导电性能,电阻小于60Ω。
具体实施方式
实施例1
一种有机导电涂料,以重量份计包括:石墨8份,二氧化钛1份,三氧化二锑0.05份,氧化镁0.3份,氧化铅0.5份,三氧化二钛1份,醇酸树脂10份,硅油0.2份,二甲苯0.05份,环氧树脂0.1份,碳酸钡0.3份。
先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
经检测,所得有机导电涂料涂层干燥后,测量涂层电阻为58Ω,厚度为0.08mm,柔韧性为5级,耐冲击强度为50Nm,硬度(与玻璃试片之比)0.854,附着力为98%。
实施例2
一种有机导电涂料,以重量份计包括:石墨15份,二氧化钛6份,三氧化二锑0.15份,氧化镁1.2份,氧化铅1.8份,三氧化二钛5份,醇酸树脂30份,硅油0.8份,二甲苯0.12份,环氧树脂0.8份,碳酸钡0.7份。
先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
经检测,所得有机导电涂料涂层干燥后,测量涂层电阻为55Ω,厚度为0.06mm,柔韧性为6级,耐冲击强度为55Nm,硬度(与玻璃试片之比)0.831,附着力为99%。
实施例3
一种有机导电涂料,以重量份计包括:石墨10份,二氧化钛2份,三氧化二锑0.08份,氧化镁0.6份,氧化铅0.8份,三氧化二钛2份,醇酸树脂15份,硅油0.3份,二甲苯0.07份,环氧树脂0.3份,碳酸钡0.4份。
先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
经检测,所得有机导电涂料涂层干燥后,测量涂层电阻为53Ω,厚度为0.07mm,柔韧性为6级,耐冲击强度为60Nm,硬度(与玻璃试片之比)0.812,附着力为99%。
实施例4
一种有机导电涂料,以重量份计包括:石墨12份,二氧化钛5份,三氧化二锑0.12份,氧化镁1.1份,氧化铅1.4份,三氧化二钛4份,醇酸树脂22份,硅油0.7份,二甲苯0.1份,环氧树脂0.6份,碳酸钡0.6份。
先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
经检测,所得有机导电涂料涂层干燥后,测量涂层电阻为52Ω,厚度为0.06mm,柔韧性为6级,耐冲击强度为57Nm,硬度(与玻璃试片之比)0.789,附着力为98%。
实施例5
一种有机导电涂料,以重量份计包括:石墨11份,二氧化钛4份,三氧化二锑0.1份,氧化镁0.9份,氧化铅1.1份,三氧化二钛3份,醇酸树脂18份,硅油0.5份,二甲苯0.08份,环氧树脂0.5份,碳酸钡0.5份。
先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。
经检测,所得有机导电涂料涂层干燥后,测量涂层电阻为55Ω,厚度为0.07mm,柔韧性为6级,耐冲击强度为60Nm,硬度(与玻璃试片之比)0.899,附着力为98%。
Claims (3)
1.一种有机导电涂料,其特征在于,以重量份计包括:石墨8~15份,二氧化钛1~6份,三氧化二锑0.05~0.15份,氧化镁0.3~1.2份,氧化铅0.5~1.8份,三氧化二钛1~5份,醇酸树脂10~30份,硅油0.2~0.8份,二甲苯0.05~0.12份,环氧树脂0.1~0.8份,碳酸钡0.3~0.7份。
2.根据权利要求1所述的有机导电涂料,其特征在于,以重量份计包括:石墨10~12份,二氧化钛2~5份,三氧化二锑0.08~0.12份,氧化镁0.6~1.1份,氧化铅0.8~1.4份,三氧化二钛2~4份,醇酸树脂15~22份,硅油0.3~0.7份,二甲苯0.07~0.1份,环氧树脂0.3~0.6份,碳酸钡0.4~0.6份。
3.一种权利要求1或2所述的有机导电涂料的制备方法,其特征在于:先将石墨、二氧化钛、三氧化二锑、氧化镁、氧化铅、三氧化二钛和碳酸钡混合均匀,然后加入醇酸树脂、环氧树脂和硅油,搅拌均匀后再加入二甲苯,混合均匀即得。