CN103725012A - 一种硅橡胶混炼胶及其制备方法 - Google Patents

一种硅橡胶混炼胶及其制备方法 Download PDF

Info

Publication number
CN103725012A
CN103725012A CN201310661672.2A CN201310661672A CN103725012A CN 103725012 A CN103725012 A CN 103725012A CN 201310661672 A CN201310661672 A CN 201310661672A CN 103725012 A CN103725012 A CN 103725012A
Authority
CN
China
Prior art keywords
vinyl
silicone rubber
mass parts
rubber compound
silicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310661672.2A
Other languages
English (en)
Inventor
阚新宇
徐文俊
耿政
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU TIANCHENG SILICON CO Ltd
Original Assignee
JIANGSU TIANCHENG SILICON CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU TIANCHENG SILICON CO Ltd filed Critical JIANGSU TIANCHENG SILICON CO Ltd
Priority to CN201310661672.2A priority Critical patent/CN103725012A/zh
Publication of CN103725012A publication Critical patent/CN103725012A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅橡胶混炼胶，按质量份数计组成为：100份甲基乙烯基硅橡胶生胶、40～50份沉淀白炭黑、3～6份乙烯基羟基硅油、0.5～1份聚四氟乙烯、0.5～1份脱模剂，所述乙烯基羟基硅油乙烯基质量百分比为1.0-2.0%，羟基质量百分比为6～8%，粘度为35～50mPa.s。本发明硅橡胶混炼胶中加入聚四氟乙烯避免了在加工过程中粘连到开炼机辊筒、操作台或与其接触的物体上，使得硅橡胶混炼胶在加工过程中更加方便和洁净；同时加入了乙烯基羟基硅油，有限降低了硅橡胶生胶在后续制备过程中的挥发性成份。本发明制备方法简单易行，成本低廉，适合规模化生产，具有工业应用价值。

Description

一种硅橡胶混炼胶及其制备方法
技术领域
本发明涉及硅橡胶技术领域，具体的是一种硅橡胶混炼胶及其制备方法。
背景技术
硅橡胶具备良好的耐高低温、耐臭氧、耐候性、绝缘性及生产惰性等很多优异的性能，通常用来制造绝缘零件、密封圈、密封器材等。由于硅橡胶生胶本身的特性，硅橡胶混炼胶在加工过程中容易粘连到开炼机辊筒、操作台或与其接触的物体上，从而造成对其它物体的污染。在用于接触食品的绝缘零件、密封圈、密封器材等硅橡胶制品中还要求硅橡胶挥发性成份不能太高，这就进一步限制了硅橡胶的应用范围。
发明内容
本发明的目的是提供一种硅橡胶混炼胶及其制备方法，以解决现有技术中存在的不足。
为解决上述问题，本发明采用以下技术方案：
一种硅橡胶混炼胶，按质量份数计组成为：
Figure BDA0000433284900000011
所述乙烯基羟基硅油乙烯基质量百分比为1.0～2.0%，羟基质量百分比为6～8%，粘度为35～50mPa.s。
进一步地，所述甲基乙烯基硅橡胶生胶粘均分子量为60万至70万，乙烯基摩尔含量为0.05%～0.15%。
进一步地，所述沉淀白炭黑比表面积为100～120m2/g。
进一步地，所述脱模剂为硬质酸锌。
上述硅橡胶混炼胶的制备方法，包括如下步骤，：
步骤一、将100质量份甲基乙烯基硅橡胶生胶和0.5～1质量份聚四氟乙烯薄通6～8次，分散均匀；
步骤二、将步骤一得到的混合物、3～6质量份乙烯基羟基硅油、0.5～1质量份脱模剂加入到捏合机中捏合10～15分钟，再分3～6次将40～50质量份沉淀白炭黑加入到捏合机中捏合均匀，得到硅橡胶混炼胶。
本发明的有益效果：
1、本发明硅橡胶混炼胶中加入聚四氟乙烯避免了在加工过程中粘连到开炼机辊筒、操作台或与其接触的物体上，使得硅橡胶混炼胶在加工过程中更加方便和洁净。
2、本发明硅橡胶混炼胶中加入了乙烯基羟基硅油，有限降低了硅橡胶生胶在后续制备过程中的挥发性成份。
3、本发明制备方法简单易行，成本低廉，适合规模化生产，具有工业应用价值。
具体实施方式：
下面结合实施例对本发明做更进一步地解释。下列实施例仅用于说明本发明，但并不用来限定本发明的实施范围。
实施例1
将100质量份甲基乙烯基硅橡胶生胶和0.7质量份聚四氟乙烯薄通7次，使聚四氟有乙烯均匀分散于甲基乙烯基硅橡胶生胶中；将上述得到的混合物、5质量份乙烯基羟基硅油、0.7质量份硬质酸锌加入到捏合机中捏合12分钟，再分5次将45质量份沉淀白炭黑加入到捏合机中捏合均匀，得到硅橡胶混炼胶。
实施例2
将100质量份甲基乙烯基硅橡胶生胶和0.5质量份聚四氟乙烯薄通6次，使聚四氟有乙烯均匀分散于甲基乙烯基硅橡胶生胶中；将上述得到的混合物、3质量份乙烯基羟基硅油、0.5质量份硬质酸锌加入到捏合机中捏合10分钟，再分3次将40质量份沉淀白炭黑加入到捏合机中捏合均匀，得到硅橡胶混炼胶。
实施例3
将100质量份甲基乙烯基硅橡胶生胶和1质量份聚四氟乙烯薄通8次，，使聚四氟有乙烯均匀分散于甲基乙烯基硅橡胶生胶中；将上述得到的混合物、6质量份乙烯基羟基硅油、1质量份硬质酸锌加入到捏合机中捏合15分钟，再分6次将50质量份沉淀白炭黑加入到捏合机中捏合均匀，得到硅橡胶混炼胶。

Claims (5)

1.一种硅橡胶混炼胶，其特征在于，按质量份数计组成为：
Figure FDA0000433284890000011
所述乙烯基羟基硅油乙烯基质量百分比为1.0～2.0%，羟基质量百分比为6～8%，粘度为35～50mPa.s。
2.根据权利要求1所述的硅橡胶混炼胶，其特征在于，所述甲基乙烯基硅橡胶生胶粘均分子量为60万至70万，乙烯基摩尔含量为0.05%～0.15%。
3.根据权利要求1所述的硅橡胶混炼胶，其特征在于，所述沉淀白炭黑比表面积为100～120m2/g。
4.根据权利要求1所述的硅橡胶混炼胶，其特征在于，所述脱模剂为硬质酸锌。
5.权利要求1～4任一权利要求所述的硅橡胶混炼胶的制备方法，其特征在于，包括如下步骤，：
步骤一、将100质量份甲基乙烯基硅橡胶生胶和0.5～1质量份聚四氟乙烯薄通6～8次，分散均匀；
步骤二、将步骤一得到的混合物、3～6质量份乙烯基羟基硅油、0.5～1质量份脱模剂加入到捏合机中捏合10～15分钟，再分3～6次将40～50质量份沉淀白炭黑加入到捏合机中捏合均匀，得到硅橡胶混炼胶。
CN201310661672.2A 2013-12-09 2013-12-09 一种硅橡胶混炼胶及其制备方法 Pending CN103725012A (zh)