CN103695992A - 不锈钢表面处理方法 - Google Patents

不锈钢表面处理方法 Download PDF

Info

Publication number
CN103695992A
CN103695992A CN201310654237.7A CN201310654237A CN103695992A CN 103695992 A CN103695992 A CN 103695992A CN 201310654237 A CN201310654237 A CN 201310654237A CN 103695992 A CN103695992 A CN 103695992A
Authority
CN
China
Prior art keywords
stainless steel
steel surface
shot blasting
shot
treatment method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310654237.7A
Other languages
English (en)
Inventor
李惠军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU DAKANG CAR CUSHION Co Ltd
Original Assignee
CHANGSHU DAKANG CAR CUSHION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU DAKANG CAR CUSHION Co Ltd filed Critical CHANGSHU DAKANG CAR CUSHION Co Ltd
Priority to CN201310654237.7A priority Critical patent/CN103695992A/zh
Publication of CN103695992A publication Critical patent/CN103695992A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种不锈钢表面处理方法，包括如下步骤：1）取83～96g/L磷酸、20～25g/L明胶、35～40g/L六次甲基四胺、25～30g/L聚氧乙烯脱水山梨醇单油酸酯、73～82g/L硫酸和200～300L水制备电解液；2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。本发明的优点和有益效果在于：提供一种不锈钢表面处理方法，其可以处理基材的斑点、裂缝。

Description

不锈钢表面处理方法
技术领域
本发明涉及不锈钢表面处理方法。
背景技术
目前不锈钢件的表面处理方式存在着一定的弊端，特别是型钢类的不锈钢件产品，由于国内的型钢加工手段不是很完善，表面效果不是太好，在实际运用中，一般的表面处理方式都很难处理基材的斑点，裂缝等缺陷，而且做不到不能耐指纹，虽表面处理过但起不到应有的表面效果。 
发明内容
本发明的目的在于提供一种不锈钢表面处理方法，其可以处理基材的斑点、裂缝。
为实现上述目的，本发明的技术方案是设计一种不锈钢表面处理方法，包括如下步骤：
1）取83～96g/L磷酸、20～25g/L明胶、35～40g/L六次甲基四胺、25～30g/L聚氧乙烯脱水山梨醇单油酸酯、73～82g/L硫酸和200～300L水制备电解液；
2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；
3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；
4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。 
本发明的优点和有益效果在于：提供一种不锈钢表面处理方法，其可以处理基材的斑点、裂缝。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种不锈钢表面处理方法，包括如下步骤：
1）取83g/L磷酸、20g/L明胶、35g/L六次甲基四胺、25g/L聚氧乙烯脱水山梨醇单油酸酯、73g/L硫酸和200L水制备电解液；
2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；
3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；
4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。 
实施例2
一种不锈钢表面处理方法，包括如下步骤：
1）取96g/L磷酸、25g/L明胶、40g/L六次甲基四胺、30g/L聚氧乙烯脱水山梨醇单油酸酯、82g/L硫酸和300L水制备电解液；
2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；
3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；
4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。 
实施例3
一种不锈钢表面处理方法，包括如下步骤：
1）取88g/L磷酸、24g/L明胶、37g/L六次甲基四胺、28g/L聚氧乙烯脱水山梨醇单油酸酯、78g/L硫酸和250L水制备电解液；
2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；
3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；
4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。 
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.不锈钢表面处理方法，其特征在于，包括如下步骤：
1）取83～96g/L磷酸、20～25g/L明胶、35～40g/L六次甲基四胺、25～30g/L聚氧乙烯脱水山梨醇单油酸酯、73～82g/L硫酸和200～300L水制备电解液；
2）对待处理不锈钢表面进行抛丸处理，抛丸处理使用直径为0.25mm的钢丸，抛丸处理后，不锈钢表面粗糙度Ra为5.8；
3）对抛丸处理后的不锈钢表面进行喷砂处理，砂处理后的不锈钢表面粗糙度Ra为3.1；
4）对喷砂处理后的不锈钢表面进行电解抛光，电流密度为3安/平方分米，电压为8V，电解液温度为75℃，电解抛光时间为35分钟。
CN201310654237.7A 2013-12-09 2013-12-09 不锈钢表面处理方法 Pending CN103695992A (zh)