CN103667613A - 防止钢材变形的热处理方法 - Google Patents

防止钢材变形的热处理方法 Download PDF

Info

Publication number
CN103667613A
CN103667613A CN201310653997.6A CN201310653997A CN103667613A CN 103667613 A CN103667613 A CN 103667613A CN 201310653997 A CN201310653997 A CN 201310653997A CN 103667613 A CN103667613 A CN 103667613A
Authority
CN
China
Prior art keywords
temperature
steel
rolled steel
quenching
furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310653997.6A
Other languages
English (en)
Inventor
单佳
单永其
张文斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Original Assignee
CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY filed Critical CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Priority to CN201310653997.6A priority Critical patent/CN103667613A/zh
Publication of CN103667613A publication Critical patent/CN103667613A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防止钢材变形的热处理方法，包括如下步骤：1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至650～700℃预热5小时；2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。本发明热处理方法，其减少了内应力的产生，减少了钢材的变形量。

Description

防止钢材变形的热处理方法
技术领域
本发明涉及防止钢材变形的热处理方法。
背景技术
钢材不仅使用在工业生产中，在日常生活中，使用钢材铸造的材料也是随处可见的，因此钢材的适用与我们是息息相关的，但钢材在处理后，往往达不到人们想要的标准形状要求，往往容易走形，很难热处理得到人们想要的标准尺寸，所示怎样防止热处理后钢材的变形，成为了我们急待解决的问题。 
发明内容
本发明的目的在于提供一种防止钢材变形的热处理方法，其减少了内应力的产生，减少了钢材的变形量。
为实现上述目的，本发明的技术方案是设计一种防止钢材变形的热处理方法，包括如下步骤：
1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至650～700℃预热5小时；
2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；
3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；
4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。 
本发明的优点和有益效果在于：提供一种防止钢材变形的热处理方法，其减少了内应力的产生，减少了钢材的变形量。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种防止钢材变形的热处理方法，包括如下步骤：
1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至700℃预热5小时；
2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；
3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；
4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。
实施例2
一种防止钢材变形的热处理方法，包括如下步骤：
1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至650℃预热5小时；
2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；
3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；
4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。
实施例3
一种防止钢材变形的热处理方法，包括如下步骤：
1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至680℃预热5小时；
2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；
3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；
4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.防止钢材变形的热处理方法，其特征在于，包括如下步骤：
1）将粗加工后的钢材置入加热炉内预热，炉温以20℃/min升至650～700℃预热5小时；
2）高温淬火，淬火温度在1100℃，保温8小时，将钢材置入650℃淬火油中淬火，当钢材温度与淬火油温度接近时，取出钢材放入450℃的中温淬火油中二次淬火处理，当钢材的温度与中温淬火油的温度接近时，取出钢材空冷至室温；
3）将钢材置入保温炉中，炉温以15℃/min升至550℃，进行保温处理，持续3小时；
4）保温炉炉温以10℃/min降至55℃，将钢材从炉内取出，空冷至室温。
CN201310653997.6A 2013-12-09 2013-12-09 防止钢材变形的热处理方法 Pending CN103667613A (zh)