CN105238910A - 一种六角轴热处理工艺 - Google Patents

一种六角轴热处理工艺 Download PDF

Info

Publication number
CN105238910A
CN105238910A CN201510767741.7A CN201510767741A CN105238910A CN 105238910 A CN105238910 A CN 105238910A CN 201510767741 A CN201510767741 A CN 201510767741A CN 105238910 A CN105238910 A CN 105238910A
Authority
CN
China
Prior art keywords
hexagonal axis
carbon potential
controlling
heat
heating furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510767741.7A
Other languages
English (en)
Inventor
鲁一军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510767741.7A priority Critical patent/CN105238910A/zh
Publication of CN105238910A publication Critical patent/CN105238910A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种六角轴热处理工艺,其包括以下步骤:A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;F、回火处理,加热至160-180℃,保温时间200min;G、空冷至室温,完成热处理并入库。本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。

Description

一种六角轴热处理工艺
技术领域
本发明涉及一种热处理工艺,特别涉及一种六角轴热处理工艺。
背景技术
六角轴是汽车部件上一个重要部件,其由圆柱体和六角轴体焊接而成,由于其是关键部件,因此对其质量要求有极高要求。传统的热处理工艺工序复杂,成本高。
发明内容
【1】要解决的技术问题
本发明要解决的技术问题是提供一种工序简单、成本低的六角轴热处理工艺。
【2】解决问题的技术方案
本发明提供一种六角轴热处理工艺,其包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。
【3】有益效果
本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。
具体实施方式
下面详细介绍本发明实施例。
本发明提供一种六角轴热处理工艺,其包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。
本发明六角轴热处理工艺,工序简单、处理成本低,能提高六角轴的质量稳定性。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.一种六角轴热处理工艺,其特征在于,包括以下步骤:
A、将六角轴放入加热炉中,并将加热炉加热至900-920℃,恒温保持30-40min,控制此期间加热炉中的碳势为0.90-1.00%;
B、强渗处理,强渗时间200min,控制此期间加热炉内碳势在0.90-1.00%;
C、扩散阶段,扩散时间50min,控制此期间加热炉内碳势在0.70-0.80%;
D、降温处理,降温至800℃,并恒温保持60min,控制此期间加热炉内碳势在0.70-0.80%;
E、油淬处理,油淬温度为130℃,控制此期间碳势在0.70-0.80%;
F、回火处理,加热至160-180℃,保温时间200min;
G、空冷至室温,完成热处理并入库。
CN201510767741.7A 2015-11-11 2015-11-11 一种六角轴热处理工艺 Pending CN105238910A (zh)