CN103667614A - 提高钢材韧性的热处理方法 - Google Patents

提高钢材韧性的热处理方法 Download PDF

Info

Publication number
CN103667614A
CN103667614A CN201310653998.0A CN201310653998A CN103667614A CN 103667614 A CN103667614 A CN 103667614A CN 201310653998 A CN201310653998 A CN 201310653998A CN 103667614 A CN103667614 A CN 103667614A
Authority
CN
China
Prior art keywords
steel
quenching
temperature
furnace
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310653998.0A
Other languages
English (en)
Inventor
单佳
单永其
张文斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Original Assignee
CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY filed Critical CHANGSHU YONGDA CHEMICAL EQUIPMENT FACTORY
Priority to CN201310653998.0A priority Critical patent/CN103667614A/zh
Publication of CN103667614A publication Critical patent/CN103667614A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种提高钢材韧性的热处理方法，包括如下步骤：1）将经过粗加工后钢材，置于加热炉内预热，在850～900℃预热6小时；2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。本发明采用高温淬火油进行淬火，并且将淬火油和钢材同时放在空气中冷却，加强了钢材的韧性。

Description

提高钢材韧性的热处理方法
技术领域
本发明涉及提高钢材韧性的热处理方法。
背景技术
现有的钢材在使用的过程中，往往因为韧性的不够在压力或拉力过大的情况下会导致钢材的断裂。 
发明内容
本发明的目的在于提供一种提高钢材韧性的热处理方法，其采用高温淬火油进行淬火，并且将淬火油和钢材同时放在空气中冷却，加强了钢材的韧性。
为实现上述目的，本发明的技术方案是设计一种提高钢材韧性的热处理方法，包括如下步骤：
1）将经过粗加工后钢材，置于加热炉内预热，在850～900℃预热6小时；
2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；
3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；
4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。 
本发明的优点和有益效果在于：提供一种提高钢材韧性的热处理方法，其采用高温淬火油进行淬火，并且将淬火油和钢材同时放在空气中冷却，加强了钢材的韧性。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种提高钢材韧性的热处理方法，包括如下步骤：
1）将经过粗加工后钢材，置于加热炉内预热，在900℃预热6小时；
2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；
3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；
4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。
实施例2
一种提高钢材韧性的热处理方法，包括如下步骤：
1）将经过粗加工后钢材，置于加热炉内预热，在850℃预热6小时；
2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；
3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；
4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。
实施例3
一种提高钢材韧性的热处理方法，包括如下步骤：
1）将经过粗加工后钢材，置于加热炉内预热，在870℃预热6小时；
2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；
3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；
4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.提高钢材韧性的热处理方法，其特征在于，包括如下步骤：
1）将经过粗加工后钢材，置于加热炉内预热，在850～900℃预热6小时；
2）进行高温淬火，淬火温度在980℃，保温2小时，将钢材置入650℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到75℃时，从淬火油中取出钢材，水冷至室温；
3）将钢材置入保温炉中，将炉温以15℃/min升至200℃，保温1小时，再以10℃/min升至500℃，保温3小时；
4）将炉温降至60℃后，将钢材从炉内取出，空冷至室温。
CN201310653998.0A 2013-12-09 2013-12-09 提高钢材韧性的热处理方法 Pending CN103667614A (zh)