CN103666036B - 一种抗刮防污紫外光固化油墨及其制备方法 - Google Patents
一种抗刮防污紫外光固化油墨及其制备方法 Download PDFInfo
- Publication number
- CN103666036B CN103666036B CN201310600454.8A CN201310600454A CN103666036B CN 103666036 B CN103666036 B CN 103666036B CN 201310600454 A CN201310600454 A CN 201310600454A CN 103666036 B CN103666036 B CN 103666036B
- Authority
- CN
- China
- Prior art keywords
- ink
- auxiliary agent
- scratch
- curable ink
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种抗刮防污紫外光固化油墨,其特征在于,由下列重量份的原料制备制成:有机颜料1-3、184光引发剂4-6、二茂铁2-3、碳酸钾4-5、芳香族聚氨酯丙烯酸酯24-28、异丙醇2-3、双季戊四醇六丙烯酸酯14-18、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三丙二醇二丙烯酸酯4-7、抗氧剂1010?1-2、促进剂MBTS?1-3、助剂4-5;本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明油墨工艺简单,易于实施,适合工业化生产,具有良好的抗刮防污特性,可广泛应用于各类电子产品屏幕保护膜。
Description
技术领域
本发明涉及一种油墨及其制备方法,特别是一种抗刮防污紫外光固化油墨及其制备方法。
背景技术
随着液晶屏幕保护膜行业的蓬勃发展,例如在手机、MP4、MP5、相机、数码摄影机、笔记本电脑等电子产品的液晶屏上都已使用起了各式各样的保护膜,而一般屏幕保护膜的外表面都需要涂布一层防刮层油墨,但现有的防刮层油墨没有防污功能,为了避免屏幕保护膜表面受到油渍、污渍的污染,同时可以有效防止对屏幕保护膜表面的刮伤或磨损,影响使用效果。因此,需要一种新的抗刮防污油墨以解决上述问题。
发明内容
本发明的目的是提供一种抗刮防污紫外光固化油墨及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种抗刮防污紫外光固化油墨,由下列重量份的原料制备制成:有机颜料1-3、184光引发剂4-6、二茂铁2-3、碳酸钾4-5、芳香族聚氨酯丙烯酸酯24-28、异丙醇2-3、双季戊四醇六丙烯酸酯14-18、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三丙二醇二丙烯酸酯4-7、抗氧剂10101-2、促进剂MBTS1-3、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-5502-3、茶多酚2-3、新戊二醇5-7、对叔丁基苯甲酸1-2、抗氧剂10351-2、2-丁氧基-乙醇3-4、交联剂TAC2-3、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述抗刮防污紫外光固化油墨,由以下具体步骤制成:首先加入有机颜料、二茂铁、碳酸钾、芳香族聚氨酯丙烯酸酯、异丙醇、双季戊四醇六丙烯酸酯、邻苯二甲酸二辛酯、苯并三氮唑、三丙二醇二丙烯酸酯搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除184光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入184光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
本发明的有益效果是:本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明油墨工艺简单,易于实施,适合工业化生产,具有良好的抗刮防污特性,可广泛应用于各类电子产品屏幕保护膜。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种抗刮防污紫外光固化油墨,由下列重量份(公斤)的原料制备制成:有机颜料1、184光引发剂4、二茂铁2、碳酸钾4、芳香族聚氨酯丙烯酸酯24、异丙醇2、双季戊四醇六丙烯酸酯14、邻苯二甲酸二辛酯2、苯并三氮唑2、三丙二醇二丙烯酸酯4、抗氧剂10101、促进剂MBTS1、助剂4;
所述助剂由下列重量份(公斤)的原料制备而成:纳米硅藻土粉0.2、纳米云母粉0.2、硅烷偶联剂KH-5502、茶多酚2、新戊二醇5、对叔丁基苯甲酸1、抗氧剂10351、2-丁氧基-乙醇3、交联剂TAC2、乙氧基化三羟甲基丙烷三丙烯酸酯10、没食子酸丙酯2、薏仁油1;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述抗刮防污紫外光固化油墨,由以下具体步骤制成:首先加入有机颜料、二茂铁、碳酸钾、芳香族聚氨酯丙烯酸酯、异丙醇、双季戊四醇六丙烯酸酯、邻苯二甲酸二辛酯、苯并三氮唑、三丙二醇二丙烯酸酯搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除184光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入184光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
所得的油墨,使用划格法牛皮胶带剥离,划格间距1mm,100%附着;使用浸有酒精的棉球,300克压力擦拭50次,无异状;浸泡于色拉油中(常温)8小时,无异状;使用浸有盐水的棉球,300克压力擦拭50次,无异状。
Claims (2)
1.一种抗刮防污紫外光固化油墨,其特征在于,由下列重量份的原料制备而成:有机颜料1-3、184光引发剂4-6、二茂铁2-3、碳酸钾4-5、芳香族聚氨酯丙烯酸酯24-28、异丙醇2-3、双季戊四醇六丙烯酸酯14-18、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三丙二醇二丙烯酸酯4-7、抗氧剂10101-2、促进剂MBTS1-3、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-5502-3、茶多酚2-3、新戊二醇5-7、对叔丁基苯甲酸1-2、抗氧剂10351-2、2-丁氧基乙醇3-4、交联剂TAC2-3、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
2.根据权利要求1所述抗刮防污紫外光固化油墨,其特征在于,由以下具体步骤制成:首先加入有机颜料、二茂铁、碳酸钾、芳香族聚氨酯丙烯酸酯、异丙醇、双季戊四醇六丙烯酸酯、邻苯二甲酸二辛酯、苯并三氮唑、三丙二醇二丙烯酸酯搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除184光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入184光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。