CN103526632A - 一种免打底纸张uv涂料及其制备方法 - Google Patents

一种免打底纸张uv涂料及其制备方法 Download PDF

Info

Publication number
CN103526632A
CN103526632A CN201310457094.0A CN201310457094A CN103526632A CN 103526632 A CN103526632 A CN 103526632A CN 201310457094 A CN201310457094 A CN 201310457094A CN 103526632 A CN103526632 A CN 103526632A
Authority
CN
China
Prior art keywords
parts
coating
paper
acetone
hydroxyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310457094.0A
Other languages
English (en)
Inventor
李琦
张小冬
刘小怡
张广宵
赵文飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Original Assignee
ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI LANKE COMPOSITE MATERIALS Co Ltd filed Critical ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Priority to CN201310457094.0A priority Critical patent/CN103526632A/zh
Publication of CN103526632A publication Critical patent/CN103526632A/zh
Pending legal-status Critical Current

Abstract

一种免打底纸张UV涂料,由下列重量份的原料制成：聚酯丙烯酸酯50-55、乙酸乙酯10-12、1，6己二醇二丙烯酸酯14-15、双季戊四醇六丙烯酸酯4-5、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三聚氰胺1-2、12-羟基硬脂酸1-2、二缩三丙二醇二丙烯酸酯6-9、2-羟基-2-甲基-1-苯基-1-丙酮(1173)4-5、分散助剂4-5。本发明涂料简化生产工艺过程,省略了传统工艺中的打底涂的工序；分散性好，流平性，形成的涂膜均匀，该涂料涂覆纸张基材后,具有干燥速度快、附着力强、抗黄变、低气味的优点。

Description

一种免打底纸张UV涂料及其制备方法
技术领域
本发明属于涂料领域，尤其涉及一种免打底纸张UV涂料及其制备方法。
背景技术
随着市场经济的发展，涂料领域发生了巨大变化，其中UV 涂料具有固化速度快、节能、常温固化、性能优越、绿色环保等优点，其上光速度快，膜层光亮度高，干燥后膜面坚固耐热，折光效果好，使底材产生强烈的主体感，已广泛应用于化工、机械、电子轻工、通讯等领域。由于其环保优势，UV 固化已获得了相关环境法规的强有力支持和工业界的密切关注，UV 辐射固化材料在市场需求高速增长的同时，UV 辐射固化体系正同多种技术结合，以克服某些缺陷，满足实际的应用。现在印刷行业中，UV 能使包装取得一些特殊的效果：高光泽度、良好的油墨保护特性、可加控制的滑爽性和耐摩擦性、低气味或没有气味、低萃取物或无法检出萃取物，以及对油墨的保护作用。
    目前的UV固化材料各种各样，但是还是不同程度的存在着一些问题，例如：有机物污染、黄变、易爆色、不耐低温、成本高、耐腐蚀性差等一系列问题，都需要针对不同的用途继续改良，降低生产成本，扩大用途。
发明内容
本发明的目的在于提供一种免打底纸张UV涂料及其制备方法。
本发明的技术方案如下：
一种免打底纸张UV涂料,其特征在于由下列重量份的原料制成：聚酯丙烯酸酯50-55、乙酸乙酯10-12、1，6己二醇二丙烯酸酯14-15、双季戊四醇六丙烯酸酯4-5、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三聚氰胺1-2、12-羟基硬脂酸1-2、二缩三丙二醇二丙烯酸酯6-9、2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173) 4-5、分散助剂4-5；
所述分散助剂由以下重量份的原料制成: 竹炭粉4-5、玉石粉2-3、玫瑰精油1-2、抗坏血酸1-2、季戊四醇三丙烯酸酯4-5、醇酯十二3-4、硅烷偶联剂KH550 1-2、乙酸乙酯14-18；制备方法是将竹炭粉、玉石粉放入10-15%盐酸溶液中泡3-4小时，取出，用去离子水洗涤多次，烘干，加入至乙酸乙酯中，研磨得20-40μm浆料，向浆料中加入其它剩余成分，加热至50-55℃，搅拌40-50分钟；继续升温至70-75℃，搅拌反应1-2小时，即得。
所述的免打底纸张UV涂料的制备方法，其特征在于包括以下步骤：将除2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)外的其它成分混合，升温至60-70℃，15-20分钟，降温到40℃以下再加入2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)，继续搅10-15分钟，即得。
本发明的有益效果
本发明涂料简化生产工艺过程,省略了传统工艺中的打底涂的工序；分散性好，流平性，形成的涂膜均匀，该涂料涂覆纸张基材后,具有干燥速度快、附着力强、抗黄变、低气味的优点。
具体实施方式
一种免打底纸张UV涂料,由下列重量份（公斤）的原料制成：聚酯丙烯酸酯53、乙酸乙酯11、1，6己二醇二丙烯酸酯14、双季戊四醇六丙烯酸酯4、邻苯二甲酸二辛酯3、苯并三氮唑3、三聚氰胺2、12-羟基硬脂酸1.6、二缩三丙二醇二丙烯酸酯8、2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173) 4、分散助剂4；
所述分散助剂由以下重量份(公斤)的原料制成: 竹炭粉4、玉石粉2、玫瑰精油2、抗坏血酸1.5、季戊四醇三丙烯酸酯4.6、醇酯十二3.5、硅烷偶联剂KH550 1.4、乙酸乙酯16；制备方法是将竹炭粉、玉石粉放入14%盐酸溶液中泡3小时，取出，用去离子水洗涤5次，烘干，加入至乙酸乙酯中，研磨得25μm浆料，向浆料中加入其它剩余成分，加热至53℃，搅拌44分钟；继续升温至72℃，搅拌反应2小时，即得。
所述的免打底纸张UV涂料的制备方法，其特征在于包括以下步骤：将除2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)外的其它成分混合，升温至63℃，16分钟，降温到40℃以下再加入2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)，继续搅13分钟，即得。
该免打底纸张UV涂料可以采用滚涂、淋涂、喷涂的施工方式进行施工。按以上方案制得的涂料涂装在木板上附着力都好于二级，耐75％乙醇24 小时以上，耐碱24小时以上、耐酸48小时以上，耐受零下40 度和40度的冷热循环10 次不发生开裂，耐15％食盐水60 小时以上，硬度可在2HB 到3H 间调节，耐磨指数在3000转以上。

Claims (2)

1.一种免打底纸张UV涂料,其特征在于由下列重量份的原料制成：聚酯丙烯酸酯50-55、乙酸乙酯10-12、1，6己二醇二丙烯酸酯14-15、双季戊四醇六丙烯酸酯4-5、邻苯二甲酸二辛酯2-3、苯并三氮唑2-3、三聚氰胺1-2、12-羟基硬脂酸1-2、二缩三丙二醇二丙烯酸酯6-9、2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173) 4-5、分散助剂4-5；
所述分散助剂由以下重量份的原料制成: 竹炭粉4-5、玉石粉2-3、玫瑰精油1-2、抗坏血酸1-2、季戊四醇三丙烯酸酯4-5、醇酯十二3-4、硅烷偶联剂KH550 1-2、乙酸乙酯14-18；制备方法是将竹炭粉、玉石粉放入10-15%盐酸溶液中泡3-4小时，取出，用去离子水洗涤多次，烘干，加入至乙酸乙酯中，研磨得20-40μm浆料，向浆料中加入其它剩余成分，加热至50-55℃，搅拌40-50分钟；继续升温至70-75℃，搅拌反应1-2小时，即得。
2.根据权利要求1所述的免打底纸张UV涂料的制备方法，其特征在于包括以下步骤：将除2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)外的其它成分混合，升温至60-70℃，15-20分钟，降温到40℃以下再加入2- 羟基-2- 甲基-1- 苯基-1- 丙酮(1173)，继续搅10-15分钟，即得。
CN201310457094.0A 2013-09-30 2013-09-30 一种免打底纸张uv涂料及其制备方法 Pending CN103526632A (zh)