CN103627340A - 耐腐蚀胶带 - Google Patents
耐腐蚀胶带 Download PDFInfo
- Publication number
- CN103627340A CN103627340A CN201310582633.3A CN201310582633A CN103627340A CN 103627340 A CN103627340 A CN 103627340A CN 201310582633 A CN201310582633 A CN 201310582633A CN 103627340 A CN103627340 A CN 103627340A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- corrosion
- resistant adhesive
- accounts
- body weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种耐腐蚀胶带,所述耐腐蚀胶带包括最上层、中间层和最下层,所述最上层是氟橡胶,所述中间层是导电胶,所述最下层是无溶剂环氧涂料,所述氟橡胶占耐腐蚀胶带主体重量的71%-79%,所述导电胶占耐腐蚀胶带主体重量的10%-19%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%-11%,本发明提供一种耐腐蚀胶带,具有优异的耐化学性、耐侯性和耐腐蚀性等优点。
Description
技术领域
本发明涉及一种胶带,尤其涉及一种耐腐蚀胶带。
背景技术
常生活中普通的封箱包装胶带(BOPP双向拉伸聚丙烯)是 任何企业、公司、个人生活中不可缺少的日常用品,但是相对于目前国内的一个状况,厂家虽多,技术却参差不齐。而且国内胶带行业在技术上的含量还处于很低阶段,国家还对此没有一个明确的选择。人们常对胶带的认识处于很懵懂的阶段,认为价格低廉,手感粘度好,其实这些都是错误的认识和判断。
那么要怎么选择胶带的好坏呢?其实,胶带的胶水好坏在使用中有两个标准,一个是初粘力,一个是保持力,两者是成反比的。一般情况下粘力低于10号的胶带是胶水覆涂教少,一般只有20微米左右,如文具胶带,普通促销捆绑用的胶带。正常的封箱胶带的初粘力在15-20号之间,这种胶带胶水的厚度一般有22-28微米。是符合标准的厚度。但市场上的胶带大部分都掺加了杂质,所以厚度增加,为遮蔽杂质,胶水中还掺有色粉,所以透明胶带就出现了蛋黄色,淡绿色,这种胶带一般都是劣质的。
胶带表面上涂有一层粘着剂,才能令胶带能粘住物品,最早的粘着剂来自动物和植物,在十九世纪,橡胶是粘着剂的主要成份;而现代则广泛应用各种聚合物。粘着剂可以粘住东西,是由于本身的分子和欲连接物品的分子间形成键结,这种键结可以把分子牢牢地黏合在一起。 粘着剂的成份,依不同厂牌、不同种类,有各种不同的聚合物。从而导致胶带阻燃性不强、不耐热和有刺激性气味等缺点。
发明内容
本发明的目的在于提供一种耐腐蚀胶带,具有优异的耐化学性、耐侯性和耐腐蚀性等优点。
本发明的技术方案是:一种耐腐蚀胶带,所述耐腐蚀胶带包括最上层、中间层和最下层,所述最上层是氟橡胶,所述中间层是导电胶,所述最下层是无溶剂环氧涂料,所述氟橡胶占耐腐蚀胶带主体重量的71%-79%,所述导电胶占耐腐蚀胶带主体重量的10%-19%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%-11%。
在本发明一个较佳实施例中,所述无溶剂环氧涂料是氯磺化聚乙烯橡胶。
在本发明一个较佳实施例中,所述氟橡胶占耐腐蚀胶带主体重量的77%,所述导电胶占耐腐蚀胶带主体重量的14%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%。
本发明的一种耐腐蚀胶带,具有优异的耐化学性、耐侯性和耐腐蚀性等优点。
附图说明
附图1为本发明耐腐蚀胶带一较佳实施例的的主视结构示意图。
附图中各部件的标记如下:1、最上层,2、中间层,3、最下层。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
请参阅图1,图1是本发明一种耐腐蚀胶带,所述耐腐蚀胶带包括最上层1、中间层2和最下层3,所述最上层1是氟橡胶,所述中间层2是导电胶,所述最下层3是无溶剂环氧涂料。
进一步说明,所述无溶剂环氧涂料是氯磺化聚乙烯橡胶,所述氟橡胶占耐腐蚀胶带主体重量的77%,所述导电胶占耐腐蚀胶带主体重量的14%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%。所述氟橡胶具有高度的化学稳定性,是目前所有弹性体中耐介质性能最好的一种。26型氟橡胶耐石油基油类、双酯类油、硅醚类油、硅酸类油,耐无机酸,耐多数的有机、无机溶剂、药品等,仅不耐低分子的酮、醚、酯,不耐胺、氨、氢氟酸、氯磺酸、磷酸类液压油。23型氟胶的介质性能与26型相似,且更有独特之处,它耐强氧化性的无机酸如发烟硝酸、浓硫酸性能比26型好,在室温下98%的HNO3中浸渍27天它的体积膨胀仅为13%-15%。
进一步说明,所述导电胶是一种固化或干燥后具有一定导电性能的胶黏剂,它通常以基体树脂和导电填料即导电粒子为主要组成成分, 通过基体树脂的粘接作用把导电粒子结合在一起, 形成导电通路, 实现被粘材料的导电连接。由于导电胶的基体树脂是一种胶黏剂, 可以选择适宜的固化温度进行粘接, 同时, 由于电子元件的小型化、微型化及印刷电路板的高密度化和高度集成化的迅速发展, 而导电胶可以制成浆料, 实现很高的线分辨率。而且导电胶工艺简单, 易于操作, 可提高生产效率,所以导电胶是替代铅锡焊接, 实现导电连接的理想选择。
在进一步说明,所述无溶剂环氧涂料通过加入特种添加剂、助剂等,经先进工艺制备而成的双组分重防腐涂料,具有防腐性能好。涂层还具有极强的附着力、耐候性、耐水性、耐久性等性能。本发明的一种耐腐蚀胶带,具有优异的耐化学性、耐侯性和耐腐蚀性等优点。
本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种耐腐蚀胶带,其特征在于:所述耐腐蚀胶带包括最上层、中间层和最下层,所述最上层是氟橡胶,所述中间层是导电胶,所述最下层是无溶剂环氧涂料,所述氟橡胶占耐腐蚀胶带主体重量的71%-79%,所述导电胶占耐腐蚀胶带主体重量的10%-19%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%-11%。
2.根据权利要求1所述的耐腐蚀胶带,其特征在于:所述无溶剂环氧涂料是氯磺化聚乙烯橡胶。
3.根据权利要求1所述的耐腐蚀胶带,其特征在于:所述氟橡胶占耐腐蚀胶带主体重量的77%,所述导电胶占耐腐蚀胶带主体重量的14%,所述无溶剂环氧涂料占耐腐蚀胶带主体重量的9%。